Study of the Poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/Cellulose Nanowhisker Composites Prepared by Solution Casting and Melt Processing

Abstract

In this study cellulose nanowhiskers (CNW) were prepared by sulfuric acid hyrolysis from microcrystalline cellulose (MCC). The biopolymer composites of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV)/CNW, was fabricated by solution casting using N,N-dimethylformamide (DMF) as the solvent. Homogeneous dispersion of the whiskers was achieved and the composites exhibited improved tensile strength and modulus and increased glass transition temperature. The melt processing (extrusion and injection molding) of PHBV/CNW composites was also attempted. Despite using polyethylene glycol (PEG) as a compatibilizer, CNW agglomerates formed during freeze-drying could not be broken and well dispersed by the extrusion process due to the large surface area and the polar nature of CNW. As a result, the melt processed PHBV/CNW composites exhibited decreased strength and constant glass transition temperature, a typical trend of microparticle filled polymer systems. MCC was also treated by high-speed mechanical homogenizer to reduce its particle size down to nanoscale range. The homogenized MCC (HMCC) was blended with PHBV by melt processing with the same conditions. The obtained composites were found to have similar properties as the melt-processed PHBV/CNW composites due to poor HMCC dispersion. To the best of our knowledge, PHBV/ CNW system has not been studied so far. The treatment of MCC with high-speed homogenizer has also not been reported. This study augments the research on CNW nanocomposites.

Keywords

cellulose whisker nanocomposites natural fiber biodegradable polymer PHB.

Get full access to this article

View all access options for this article.

References

Herrmann, A. , Nickel, J. and Riedel, U. (1998). Construction Materials Based Upon Biologically Renewable Resources - From Components to Finished Parts, Polymer Degradation and Stability , 59(1-3): 251-261.

Riedel, U. and Nickel, J. (1999). Natural Fibre-Reinforced Biopolymers as Construction Materials - New Discoveries, Die Angewandte Makromolekulare Chemie, 272: 34-40.

Marchessault, R.H. and Coulombe, S. (1981). Solid State Properties of Poly-B-Hydroxybutyrate and of Its Oligomers, Canadian Journal of Chemistry, 59(1): 38-44.

Barham, P.J. , Keller, A. , Otun, E.L. and Holmes, P.A. (1984). Crystallization and Morphology of a Bacterial Thermoplastic: Poly-3-Hydroxybutyrate, Journal of Materials Science, 19(9): 2781-2794.

Holmes, P.A. (1988). In: Development in Crystalline Polymers, Elsevier Applied Science Publishers, London .

Reinsch, V. and Kelley, S. (1997). Crystallization of Poly (Hydroxybutrate-co-Hydroxyvalerate) in Wood Fiber-Reinforced Composites, Journal of Applied Polymer Science, 64(9): 1785-1796.

Fernandes, E.G. , Pietrini, M. and Chiellini, E. (2004). Bio-Based Polymeric Composites Comprising Wood Flour as Filler, Biomacromolecules, 5(4): 1200-1205.

Singh, S. and Mohanty, A.K. (2007). Wood Fiber Reinforced Bacterial Bioplastic Composites: Fabrication and Performance Evaluation, Composites Science and Technology, 67(9): 1753-1763.

Wong, S. , Shanks, R.A. and Hodzic, A. (2002). Properties of Poly(3-hydroxybutyric acid) Composites with Flax Fibres Modified by Plasticiser Absorption, Macromolecular Materials and Engineering, 287(10): 647-655.

10.

Van De VElde K. and Kiekens, P. (2002). Biopolymers: Overview of Several Properties and Consequences on Their Applications, Polymer Testing, 21(4): 433-442.

11.

Bhardwaj, R. , Mohanty, A. , Drzal , L. , Pourboghrat, T.F. and Misra, M. (2006). Renewable Resource based Green Composites from Recycled Cellulose Fiber and Poly (3-hydroxybutyarteco-3-hydroxyvalerate) Bioplastic, Biomacromolecules, 7(6): 2044-2051.

12.

Luo, S. and Netravali, A.N. (1999). Interfacial and Mechanical Properties of Environment-Friendly Green Composites Made from Pineapple Fibers and Poly(Hydroxybutyrate-Co-Valerate) Resin, Journal of Materials Science, 34(15): 3709-3719.

13.

Ouajai, S. , Hodzic, A. and Shanks, R.A. (2004). Morphological and Grafting Modification of Natural Cellulose Fibers, Journal of Applied Polymer Science, 94(6): 2456-2465.

14.

Sturcova, A. , Davies, G.R. and Eichhorn, S.J. (2005). Elastic Modulus and Stress-Transfer Properties of Tunicate Cellulose Whiskers , Biomacromolecules, 6(2): 1055-1061.

15.

Bondeson, D. , Mathew, A. and Oksman, K. (2006). Optimization of the Isolation of Nanocrystals from Microcrystalline Cellulose by Acid Hydrolysis, Cellulose, 13(2): 171-180.

16.

Kvien, I. , Tanem, B.S. and Oksman, K. (2005). Characterization of Cellulose Whiskers and Their Nanocomposites by Atomic Force and Electron Microscopy, Biomacromolecules , 6(6): 3160-3165.

17.

Oksman, K. , Mathew, A.P. , Bondeson, D. and Kvien, I. (2006). Manufacturing Process of Polylactic Acid (PLA) - Cellulose Whiskers Nanocomposites, Composite Science and Technology, 66(15): 2776-2784.

18.

Bondeson, D. , Syre, P. and Oksman, K. (2007). All Cellulose Nanocomposites Produced by Extrusion, Journal of Biomaterials and Bioenergy , 1(3): 367-371.

19.

Bondeson, D. and Oksman, K. (2007). Polylactic Acid/Cellulose Whisker Nanocomposites Modified by Polyvinyl Alcohol, Composites Part A, 38: 2486-2492.

20.

Bondeson, D. and Oksman, K. (2007). Dispersion and Characteristics of Surfactant Modified Cellulose Whiskers Nanocomposites , Composite Interfaces, 14: 617-630.

21.

Petersson, L. , Kvien, I. and Oksman, K. (2007). Structure and Thermal Properties of Poly(lactic acid)/Cellulose Whiskers Nanocomposites , Composite Science and Technology, 67: 2535-2544.

22.

Petersson, L. and Oksman, K. (2006). Preparation and Properties of Biopolymer based Nanocomposites Films using Microcrystalline Cellulose (MCC), In: Oksman, K. and Sain, M. (eds), Cellulose Nanocomposites: Processing, Characterization and Properties, ACS Symposium Series, Vol. 938, Oxford Press .

23.

de Rodriguez, N.L.G. , Thielemans , W. and Dufresne, A. (2006). Sisal Cellulose Whiskers Reinforced Polyvinyl Acetate Nanocomposites , Cellulose, 13(3): 261-270.

24.

Wang, Y.X. , Cao, X.D. and Zhang, L. (2006). Effects of Cellulose Whiskers on Properties of Soy Protein Thermoplastics, Macromolecular Bioscience, 6(7): 524-531.

25.

Sriupayoa, J. , Supaphola, P. , Blackwellb , J. and Rujiravanit , R. (2005). Preparation and Characterization of α-Chitin Whisker-Reinforced Poly(vinyl alcohol) Nanocomposite Films with or without Heat Treatment, Polymer, 46(15): 5637-5644.

26.

Jiang, L. , Wolcott, M.P. and Zhang, J. (2006). Study of Biodegradable Polylactide/ Poly(butyleneadipate-co-terephthalate) Blends, Biomacromolecules, 7(1): 199-207.

27.

Ljungberf, N. , Cavaille, J.Y. and Heux, L. (2006). Nanocomposites of Isotacic Polypropylene Reinforced with Rod-like Cellulose Whiskers, Polymer, 47: 6285-6292.