Based upon previous results of direct micromechanical method (DMM) analysis of the representative volume element (RVE) of a plain-weave textile composite, two methods for predicting failure envelopes are presented: a parametric ellipse-fitting scheme, and a 27-term quadratic stress-gradient failure criterion. Both include the consideration of micro level stress gradients and effectively predict failure in agreement with the DMM. The parametric ellipse-fitting method was found to agree with DMM results to within a few percent. The quadratic failure criterion was found to agree within 9.3%, but the method is more robust in its ability to predict failure for complex loading cases.
Tsai, S.W. and Hahn, H.T. (1980). Introduction to Composite Materials, Technomic Publishing Co, Lancaster, PA.
2.
Karkkainen, R.L. and Sankar, B.V. (2006). A Direct Micromechanics Method for Analysis of Failure Initiation of Plain Weave Textile Composites, Journal of CompositesScience and Technology, 66: 137—150.
3.
Whitcomb, J.K. and Srirengan, K. (1996). Effect of Various Approximations on Predicted Progressive Failure in Plain Weave Composites, Composite Structures, 34: 13—20.
4.
Woo, K. and Whitcomb, J.D. (2000). A Post Processor Approach for Stress Analysis of Woven Textile Composites, CompositesScience and Technology , 60: 693—704.
5.
Tang, X. and Whitcomb, J.D. (2003). General Techniques for Exploiting Periodicity and Symmetries in Micromechanics Analysis of Textile Composites, Journal ofComposite Materials, 37: 13.
6.
Whitcomb, J.D. , Chapman, C.D. and Srirengan , K. (1998). Analysis of Plain-Weave Composites Subjected to Flexure, Mechanics of Composite Materials and Structures, 5: 41—53.
7.
Cox, B.N. and Dadkhah, M.S. (1994). A Binary Model of Textile Composites: I-Formulation , Acta Metallurgica et Materiala, 42(10): 3463.
8.
Yang, Q. and Cox, B.N. (2003). Predicting Local Strains in Textile Composites Using the Binary Model Formulation, In: Proceedings of the ICCM2003, San Diego, CA, July.
9.
Bogdanovich, A.E. and Pastore, C.M. (1996). Material-Smart Analysis of Textile-Reinforced Structures, CompositesScience and Technology , 56: 291—309.
10.
Bogdanovich, A.E. (2003). Multiscale Predictive Analysis of 3-D Woven Composites, In: SAMPE 35th International Technical Conference, CD ROM Proceedings, Dayton, OH, September.
11.
Quek, S.C., Waas, A., Shahwan, K.W. and Agaram, V. (2004). Compressive Response and Failure of Braided Textile Composites: Part 2, Computations, International Journal of Nonlinear Mechanics, 39: 649—663.
12.
Quek, S.C., Waas, A., Shahwan, K.W. and Agaram, V. (2004). Compressive Response and Failure of Braided Textile Composites: Part 1, Experiments, International Journal of Nonlinear Mechanics, 39: 635—648.
13.
Gosse J.H. and Christensen, S. (2001). Strain Invariant Failure Criteria for Polymers in Composite Materials, AIAA-2001-1184.
14.
Tay, T.E., Tan, V.B.C. and Tan, S.H.N. (2005). Element-failure: An Alternative to Material Property Degradation Method for Progressive Damage in Composite Structures, Journal ofComposite Materials, 39(18): 1659—1675.
15.
Zhu, H., Sankar, B.V. and Marrey, R.V. (1998). Evaluation of Failure Criteria for Fiber Composites Using Finite Element Micromechanics, Journal ofComposite Materials, 32(8): 766—782.
16.
Marrey, R.V. and Sankar, B.V. (1995). Micromechanical Models for Textile Structural Composites, NASA CR-198229.
17.
Sankar, B.V. and Marrey, R.V. (1997). Analytical Method for Micromechanics of Textile Composites, CompositesScience and Technology, 57(6): 703—713.
18.
Marrey, R.V. and Sankar, B.V. (1997). A Micromechanical Model for Textile Composite Plates, J. of Composite Materials, 31(12): 1187—1213.
19.
Carvelli, V. and Poggi, C. (2001). A Homogenization Procedure for the Numerical Analysis of Woven Fabric Composites, Composites Part A: Applied Science and Manufacturing, 32: 1425—1432.