Preparation of Microporous Films from Immiscible Blends via Melt Processing

Abstract

Microporous films from immiscible blends were produced via melt processing and post-step treatments. Polystyrene (PS)/polypropylene (PP) and poly(ethylene terephthalate) (PET)/polypropylene blend systems with different viscosity ratios were studied. The blends were first compounded in a co-rotating twin-screw extruder and subsequently extruded through a sheet die to obtain the precursor films. These were uniaxially or biaxially drawn (100–400%) with respect to the original dimension to induce microporous structure and post treated at elevated temperature to maintain the porous structure which consisted of uniform microcracks in the order of a few hundred nanometers. The fabrication process here is shown to be a promising technique for producing microporous films that can be used for liquid and gas separations.

Keywords

microporous film immiscible blends melt processing methanol permeability PP PS PET membranes

Get full access to this article

View all access options for this article.

References

1. M.L. Druin, J.T. Loft, and S.G. Plovan, “Novel open-celled microporous film,” US Patent 3801404 (1974).

2. H.S. Bierenbaum , R.B. Isaacson , M.D. Druin , and S.G. Plovan , “Microporous polymeric films”, I&ECProd. Res. Develop, 13, 2-2 (1974).

3. H.S. Bierenbaum, L.R. Daley, D. Zimmerman, and I.L. Hay, “Process for preparing a thermoplastic microporous film involving a cold stretching step and multiple hot stretching steps”, US Patent 3843761 (1974).

4. Brazinsky, W.M. Cooper and A.S. Gould, “Process for preparing a microporous polymer film”, US Patent 4138459 (1979).