Comparison of the Thermal Decomposition Behavior of a Non-Fire Retarded and a Fire Retarded Flexible Polyurethane Foam with Phosphorus and Brominated Additives

Abstract

Thermogravimetric analysis was carried out to investigate the thermal decomposition behavior of a commercial fire retarded (FR) and a non-fire retarded (NFR) flexible polyurethane foam. The effects of the heating rate and the reaction atmosphere on the thermal decomposition process were studied at three different heating rates ranging from 5°C/min to 20°C/min in both nitrogen and air environment. Results from the time-of-flight secondary ion mass spectrometry (ToF SIMS) study revealed that the additives in the FR foam were phosphorus and brominated compounds. The measurements by means of colorimetric method further certified that the concentrations of phosphorus and bromine in the FR foam sample were 0.08 wt% and 1.4 wt% respectively. From the thermogravimetric (TG) and the derivative thermogravimetric (DTG) curves, it was seen that the thermal decomposition processes of both the FR and the NFR foams followed a two-step reaction in nitrogen. However, the thermal decomposition processes followed a three-step reaction in air. The thermal analysis results showed that the flame retardant additives of phosphorus and brominated compounds acted not only in the gas phase but also in the solid phase. Furthermore, the flame retardant additives decreased the thermal stability and increased the char formation in the temperature ranging from 300°C to 400°C, which, commonly, is the temperature range for smoldering combustion in this kind of foam material. From the kinetic parameters estimated from the TG and the DTG curves, it was seen that the activation energies of the flexible polyurethane foams were very sensitive to the temperature and were also influenced significantly by the flame retardant additives.

Keywords

thermogravimetric analysis kinetic parameter flexible polyurethane foam flame retardant additive

Get full access to this article

View all access options for this article.

References

Buszard, D. L. 1987. “Polymer Flammability—Mechanisms of Achieving Flame Retardance,” in Fundamental Aspects of Polymer Flammability, G. Cox and G. Stevens , ed., England: the Institute of Physics Techno House, pp. 1-16.

Ohlemiller, T. J. 1986. “Modeling of Smoldering Combustion Propagation,” Progress in Energy and Combustion Science, 11:277-310.

Palmer, K. N. 1957. “Smoldering Combustion in Dusts and Fibrous Materials,” Combustion and Flame, 1:129-154.

Damant, G. H. 1975. “Cigarette Induced Smoldering of Uncovered Flexible Polyurethane Foams,” J. Consumer Product Flammability, 2:140-153.

Eicher, W. J. and Szabat, J. F. 1980. “Response of Polyurethane Foams to Cigarette Ignition Tests,” J. Consumer Product Flammability, 7(3):172-188.

Pearce, E. P. , Khanna, Y. P. and Raucher, D. 1997. “Chap 8. Thermal Analysis in Polymer Flammability,” in Thermal Characterization of Polymeric Materials, E. A. Turi , ed., San Diego: Academic Press Inc., pp. 793-844.

Voorhees, K. J. , Hileman, F. D. , Einhorn, I. N. and Futrell, J. H. 1978. “An Investigation of the Thermolysis Mechanism of Model Urethanes,” J. of Polymer Science: Polymer Chemistry Edition, 16:213-228.

Rogers, F. E. and Ohlemiller, T. J. 1981. “Pyrolysis Kinetics of a Polyurethane Foam by Thermogravimetry: A General Kinetic Method,” J. Macromol. Sci.-Chem., A15(1):169-185.

Larsen, E. R. and Ecker, E. L. 1988. “Thermal Stability of Fire Retardants: V. Decomposition of Haloalkyl Phosphates under Polyurethane Processing Conditions,” J. of Fire Sciences, 6:363-379.

10.

Bilbao, R. , Mastral, J. F. , Ceamanos, J. and Aldea, M. E. 1996. “Kinetics of the Thermal Decomposition of Polyurethane Foams in Nitrogen and Air Atmospheres,” J. of Analytical and Applied Pyrolysis, 37:69-82.

11.

Reed, C. S. , Taylor, J. P. , Guigley, K. S. , Coleman, M. M. and Allcock, H. R. 2000. “Polyurethane/Poly[bis(carboxylatophenoxy)phosphazene] Blends and Their Potential as Flame-Retardant Materials,” Polymer Engineering and Science, 40(2):465-472.

12.

Department of Consumer Affairs Bureau of Home Furnishing and Thermal Insulation, State of California, USA, “California Technical Bulletin 117.”

13.

Sekiguchi, Y. and Shafizadeh, F. 1984. “The Effect of Inorganic Additives on the Formation, Composition, and Combustion of Cellulosic Char,” J. of Applied Polymer Science, 29:1267-1286.

14.

Daniels, T. 1973. “Techniques Based on the Measurement of Sample Weight,” in Thermal Analysis, London: Kogan Page Limited, pp. 53-62.

15.

Brauman, S. K. 1977. “Phosphorus Fire Retardance in Polymers. I. General Mode of Action,” J. of Fire Retardant Chemistry, 4:18-37.

16.

Brauman, S. K. and Fishman N. 1977. “Phosphorus Fire Retardance in Polymers. III. Some Aspects of Combustion Performance,” J. of Fire Retardant Chemistry, 4:93-111.

17.

Ravey, M. , Keidar, I. , Weil, E. D. and Pearce, E. M. 1998. “Flexible Polyurethane Foam. II. Fire Retardation by Tris(1,3-dichloro-2-propyl) Phosphate. Part A. Examination of the Vapor Phase (the Flame),” J. of Applied Polymer Science, 68:217-229.

18.

Ravey, M. , Weil, E. D. , Keidar, I. and Pearce, E. M. 1998. “Flexible Polyurethane Foam. II. Fire Retardation by Tris(1,3-dichloro-2-propyl) Phosphate. Part B. Examination of the Condensed Phase (the Pyrolysis Zone),” J. of Applied Polymer Science, 68:231-254.

19.

Friedman, H. L.

“Kinetics of Thermal Degradation of Char-Forming Plastics from Thermogravimetry. Application to a Phenolic Plastic,”

J. of Polymer Science: Part C, 6:183-195.

20.

Freeman, E. S. and Carroll, B. 1958. “The Application of Thermoanalytical Techniques to Reaction Kinetics. The Thermogravimetric Evaluation of the Kinetics of the Decomposition of Calcium Oxalate Monohydrate,” The J. of Physical Chemistry, 62:394-397.

21.

Chang, W. L. 1994. “Decomposition Behavior of Polyurethanes via Mathematical Simulation,” J. of Applied Polymer Science, 53:1759-1769.

22.

Ozawa T. 1965. “A New Method of Analyzing Thermogravimetric Data,” Bull. of the Chemical Society of Japan, 38:1881-1886.

23.

Kissinger, H. E. 1957. “Reaction Kinetics in Differential Thermal Analysis,” Analytical Chemistry, 29(11):1702-1706.