Natural wood is a ready-to-use template for making porous silicon carbide (SiC) body. Biomorphic β-SiC was synthesised from wood of a mango (Mangifera Indica) tree. Carbon template was made by carbonising this wood at 1000°C in argon gas atmosphere. Thus formed template was repeatedly infiltrated with a mixture of tetraethyl-orthosilicate (TEOS) (in alcohol) and oxalic acid solution (aqueous). Heat treatment at 1600°C for 1 h in vacuum converted the infiltrated template to β-SiC with a complex hierarchical cellular structure- a mimic of the plant structure. To produce phase pure SiC, unreacted carbon (C) and silica (SiO2) (if any) were removed by burning in air followed by treating with hydrofluoric acid. Mono dispersed SiC powder having particle size of ∼225 nm has been obtained by crushing, grinding and milling of thus formed biomorphic SiC body. A grinding limit is reported for the first time in SiC system.
VogliE, MukerjiJ, HoffmanC, Conversion of oak to cellular silicon carbide ceramic by gas-phase reaction with silicon monoxide. J Am Ceram Soc. 2001;84(6):1236–1240.
2.
Arellano-LopezAR, Martinez-FernandezJ, GonzalezP, Biomorphic SiC: a new engineering ceramic material. Int J Appl Ceram Technol. 2004;1(1):56–67.
3.
PappacenaKE, FaberKT.Thermal conductivity of porous silicon carbide derived from wood precursors. J Am Ceram Soc. 2007;90(9):2855–2862.
4.
DingJ, DengCJ, YuanWJ, Preparation of porous TiC/C ceramics using wooden template in molten salt media. Adv Appl Ceram. 2013;112(3):131–135.
5.
JiangF, WangJ, AnZ, Synthesis of biomorphic SiC fabric ceramic from pre-processed ramie fibres. Adv Appl Ceram. 2017;116:242–247.
6.
RiceZA.Porosity of ceramics. New York: Marcel Dekker Inc; 1998.
7.
ZimmermanAF, PalumboG, AustKT, Mechanical properties of nickel silicon carbide nanocomposites. Mater Sci Eng: A. 2002;328:137–146.
StudartAR, GonzenbachUT, TervoortE, Processing routes to macroporous ceramics: a review. J Am Ceram Soc. 2006;89(6):1771–1789.
10.
GreilP.Biomorphous ceramics from lignocellulosics. J Eur Ceram Soc. 2001;21(2):105–118.
11.
SakashitaK. Honeycomb filter and exhaust gas purification device. Patent US 20080236115.A1. 2008.
12.
Jung-HyeE, Young-WookK, SantoshR.Processing and properties of macroporous silicon carbide ceramics: a review. J Asian Ceram Soc. 2013;1:220–242.
13.
MinX, FangM, HuangZ, Preparation of Al2O3–SiC composite powder from kyanite tailings via carbothermal reduction process. Adv Appl Ceram. 2018;117(1):9–15.
14.
ZhaoJ, XueJX, LiuHT, Zrc ceramics incorporated with different-sized SiC particles. Adv Appl Ceram. 2018;117(7):383–388.
15.
LiXK, LiuL, XangYX, Synthesis of nanometre silicon carbide whiskers from binary carbonaceous silica aerogels. Carbon N Y. 2001;39(2):159–165.
16.
QuanJ-M, WangJ-P, QuaoG-J, Preparation of porous SiC ceramic with a woodlike microstructure by sol-gel and carbothermal reduction processing. J Eur Ceram Soc. 2004;24:3251–3259.
17.
MartinH-P, EckeR, MullerE.Synthesis of nano crystalline silicon carbide powder by carbothermal reduction. J Eur Ceram Soc. 1998;18(12):1737–1742.
18.
SaitoM, NagashimaS, KatoA.Crystal growth of SiC whisker from the SiO(g)-CO system. J Mater Sci Lett. 1992;11:373–376.
19.
LiZ, ZhangJ, MengA, Large-area highly-oriented SiC nanowire arrays: synthesis, Raman, and photoluminescence properties. J Phys Chem B. 2006;110:22382–22386.
20.
Joint Committee of Powder Diffraction Standards, Card No: 29-1129.
21.
KuomotoK, TakedaS, PaiCH.High-resolution electron microscopy observations of stacking faults in β-SiC. J Am Ceram Soc. 1989;72(10):1985–1987.
22.
PujarVV, CawleyJD.Effect of stacking faults on the x-ray diffraction profiles of β-SiC powder. J Am Ceram Soc. 1995;78(3):774–782.
23.
FerrariAC, RobertsonJ.Interpretation of Raman spectra of disordered and amorphous carbon. Phys Rev B. 1999;61(20):14095–14107.
24.
OlegoD, CardonaM.Temperature dependence of the optical phonons and transverse effective charge in 3C-SiC. Phys Rev B. 1982;25(6):3889–3896.
25.
NakashimaS, HarimaH.Raman investigation of SiC polytypes. Phys Status Solidi (a). 1997;162(1):39–64.
26.
WardY, YoungRJ, ShatwellRA.Application of Raman microscopy to the analysis of silicon carbide monofilaments. J Mater Sci. 2004;39:6781–6790.
27.
KingmaKJ, HemleyRJ.Raman spectroscopic study of microcrystalline silica. Am Mineral. 1994;79:269–273.
28.
ProchazkaS. Sintered Silicon Carbide and method of making. US patent no 566806. 1997.
29.
ZhaoQ, YamadaS, JimboG.The mechanism and grinding limit of planetary ball milling. KONA. 1989;7:29–36.
30.
ChenY, LianX, ZhengS.Research on superfine grinding process and kinetics of calcined black talc in planetary mill. Procedia Eng. 2015;102:379–387.
31.
HarrisCC.A method for determining the parameters of the Gaudin-Meloy distribution. Trans Soc Mining. Eng. 1967;17:238.
32.
TanakaT. Staub. 1958;18:157–168. Cross Ref. from: Balaz P. Mechanochemistry in Nanoscience and Minerals Engineering. Springer-Verlageds Berlin Heidelberg Chapter- 2 High-Energy Milling.2008;103–132.
33.
PeukertW, SchwarzerHC, StengerF.Control of aggregation in production and handling of nanoparticles. Chem Eng Process. 2005;44:245–252.
FaddaS, CincottiA, ConcasA, Modelling breakage and reagglomeration during fine dry grinding in ball milling devices. Powder Technol. 2009;194:207–216.
36.
PedroLG, AlanAAT, JulianoBS.The onset of particle agglomeration during the dry ultrafine grinding of limestone in a planetary ball mill. Powder Technol. 2015;284:122–129.
37.
GarciaF, Le BolayN, FrancesC.Changes of surface and volume properties of calcite during a batch wet grinding process. Chem Eng J. 2002;85:177–187.
38.
GarciaF, Le BolayN, Jean-LucT, On fragmentation and agglomeration phenomena in an ultrafine wet grinding process: the role of polyelectrolyte additives. Int J Miner Process. 2004;74S:S43–S54.
39.
CatharinaK, CarolaS, StefanR, Nanoparticle production with stirred-mediamills: opportunities and limits. Chem Eng Technol. 2010;33(9):1401–1411.
40.
HasegawaM, KimataM, ShimaneM, The effect of liquid additives on dry ultrafine grinding of quartz. Powder Technol. 2001;114(1–3):145–151.
41.
YujiH, HuseyinY, TakashiS, State of the Dispersant and particle surface during Wet-Jet Milling for preparation of a stable slurry. J Am Ceram Soc. 2008;91(4):1095–1101.