Reasonable zirconia surface pretreatment results in excellent bond strength. This study compared the effects of different surface treatments on the shear bond strength of zirconia. A total of 48 zirconia discs were divided into six separate groups (n = 8) including a Control (CL), Alumina particle blasting (AP), Silica coating (SC), Alumina particle blasting and silica coating (AS), Femtosecond laser (FL) and Femtosecond laser and silica coating (FS) group. Resin block was bound with zirconia using resin cement after performing different surface processing. Shear bond strength (SBS) was measured using a universal testing machine with a crosshead speed of 1 mm min–1 and analysed through one-way analysis of variance (ANOVA)/Tukey tests. SEM revealed many regular microgrooves structured on the surface by laser irradiation. Some nano-columns and nano-holes were found on the side walls of the groove. SBS test results showed that pretreatment of the femtosecond laser and the conjunctive use of a femtosecond laser and silica coating significantly improved SBS (13.769 ± 1.570 MPa and 13.516 ± 1.759 MPa) between zirconia and resin. Owing to limitations of this study, regular microgrooves were structured on zirconia surfaces using femtosecond laser treatment. SBS values of zirconia were significantly improved after femtosecond laser processing and the use of femtosecond laser and silica coating. The influence of surface roughness on the adhesion between zirconia and resin cement was seem more effectively observed in this study.
MiyazakiT, NakamuraT, MatsumuraH, Current status of zirconia restoration. J Prosthodont Res. 2013;57(4):236–261. doi: 10.1016/j.jpor.2013.09.001
2.
ThomaDS, SailerI, IoannidisA, A systematic review of the survival and complication rates of resin-bonded fixed dental prostheses after a mean observation period of at least 5years. Clin Oral Implan Res. 2017;28(11):1421–1432. doi: 10.1111/clr.13007
ChenJY, CaiH, RenXC, A systematic review of the survival and complication rates of all-ceramic resin-bonded fixed dental prostheses. J Prosthodont. 2017;26(7):535–543.
ŞanlıS, ÇömlekoğluMD, ÇömlekoğluE, Influence of surface treatment on the resin-bonding of zirconia. Dent Mater. 2015;31(6):657–668. doi: 10.1016/j.dental.2015.03.004
7.
Ramos-TonelloCM, TrevizoBF, RodriguesRF, Pre-sintered Y-TZP sandblasting: effect on surface roughness, phase transformation, and Y-TZP/veneer bond strength. J Appl Oral Sci. 2017;25(6):666–673. doi: 10.1590/1678-7757-2017-0131
8.
MartinsSB, Abi-RachedFO, AdaboGL, Influence of particle and air-abrasion moment on Y-TZP surface characterization and bond strength. J Prosthodont. 2019;28(1):271–278. doi: 10.1111/jopr.12718
9.
KosmacT, OblakC, JevnikarP, The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater. 1999;15(6):426–433. doi: 10.1016/S0109-5641(99)00070-6
10.
LorenteMC, ScherrerSS, RichardJ, Surface roughness and EDS characterization of a Y-TZP dental ceramic treated with the CoJet™ Sand. Dent Mater. 2010;26(11):1035–1042. doi: 10.1016/j.dental.2010.06.005
11.
El GamalA, MedioniE, RoccaJP, Shear bond, wettability and AFM evaluations on CO2 laser-irradiated CAD/CAM ceramic surfaces. Lasers Med Sci. 2017;32(4):779–785. doi: 10.1007/s10103-017-2171-4
12.
VicenteM, Gomes AnaL, MonteroJ, Influence of cyclic loading on the adhesive effectiveness of resin-zirconia interface after femtosecond laser irradiation and conventional surface treatments. Lasers Surg Med. 2016;48(1):36–44. doi: 10.1002/lsm.22442
13.
AkpinarYZ, KepceogluA, YavuzT, Effect of femtosecond laser beam angle on bond strength of zirconia-resin cement. Lasers Med Sci. 2015;30(8):2123–2128. doi: 10.1007/s10103-015-1762-1
14.
RoiteroE, LasserreF, AngladaM, A parametric study of laser interference surface patterning of dental zirconia: effects of laser parameters on topography and surface quality. Dent Mater. 2017;33(1):e28–e38. doi: 10.1016/j.dental.2016.09.040
15.
KasraeiS, Rezaei-SoufiL, HeidariB, Bond strength of resin cement to CO2 and Er:YAG laser-treated zirconia ceramic. Restor Dent Endod. 2014;39(4):296–302. doi: 10.5395/rde.2014.39.4.296
16.
TanişMÇ, AkçaboyC.Effects of different surface treatment methods and MDP monomer on resin cementation of zirconia ceramics an in vitro study. J Lasers Med Sci. 2015;6(4):174–181. doi: 10.15171/jlms.2015.15
17.
YasumaruN, MiyazakiK, KiuchiJ.Femtosecond-laser-induced nanostructure formed on hard thin films of TiN and DLC. Appl Phys A Mater. 2003;76(6):983–985. doi: 10.1007/s00339-002-1979-2
18.
BorowiecA, HaugenHK.Subwavelength ripple formation on the surfaces of compound semiconductors irradiated with femtosecond laser pulses. Appl Phys Lett. 2003;82(25):4462–4464. doi: 10.1063/1.1586457
19.
Delgado-RuizRA, GomezMG, Aguilar-SalvatierraA, Human fetal osteoblast behavior on zirconia dental implants and zirconia disks with microstructured surfaces. An experimental in vitro study. Clin Oral Implants Res. 2016;27(11):144–153. doi: 10.1111/clr.12585
20.
Delgado-RuízRA, Calvo-GuiradoJL, MorenoP, Femtosecond laser microstructuring of zirconia dental implants. J Biomed Mater Res Part B Appl Biomater. 2011;96(1):91–100. doi: 10.1002/jbm.b.31743
21.
KaraO, KaraHB, TobiES, Effect of various lasers on the bond strength of two zirconia ceramics. Photomed Laser Surg. 2015;33(2):69–76. doi: 10.1089/pho.2014.3841
22.
MaríaV, Gomes AnaL, MonteroJ, Influence of cyclic loading on the adhesive effectiveness of resin-zirconia interface after femtosecond laser irradiation and conventional surface treatments. Lasers Surg Med. 2016;48(1):36–44. doi: 10.1002/lsm.22442
23.
LeeJJ, KangCK, OhJW, Evaluation of shear bond strength between dual cure resin cement and zirconia ceramic after thermocycling treatment. J Adv Prosthodont. 2015;7(1):1–7. doi: 10.4047/jap.2015.7.1.1
24.
KhanAA, MohamedBA, MirzaEH, Surface wettability and nano roughness at different grit blasting operational pressures and their effects on resin cement to zirconia adhesion. Dent Mater J. 2019;38(3):388–395. doi: 10.4012/dmj.2018-137
25.
MahmoodAR, De SouzaGM, YoavF.Ultrashort-pulse laser as a surface treatment for bonding between zirconia and resin cement. Dent Mater. 2019;35(11):1545–1556. doi: 10.1016/j.dental.2019.07.009
26.
ChintapalliRK, MestraRA, GarciaMF, Effect of sandblasting and residual stress on strength of zirconia for restorative dentistry applications. J Mech Behav Biomed. 2014;29:126–137. doi: 10.1016/j.jmbbm.2013.09.004
27.
HongboZ, ChenL, ZhenkaiZ, Femtosecond laser-induced periodic surface microstructure on dental zirconia ceramic. Mater Lett. 2018;229:74–77. doi: 10.1016/j.matlet.2018.06.059
28.
GregorčičP, SedlačekM, PodgornikB, Formation of laser-induced periodic surface structures (LIPSS) on tool steel by multiple picosecond laser pulses of different polarizations. Appl Surf Sci. 2016;387:698–706. doi: 10.1016/j.apsusc.2016.06.174
29.
LinX, LiX, ZhangY, Periodic structures on germanium induced by high repetition rate femtosecond laser. Opt Laser Technol. 2018;101:291–297. doi: 10.1016/j.optlastec.2017.11.028
30.
DarMH, KuladeepR, SaikiranV, Femtosecond laser nanostructuring of titanium metal towards fabrication of low-reflective surfaces over broad wavelength range. Appl Surf Sci. 2016;371:479–487. doi: 10.1016/j.apsusc.2016.03.008
31.
BashirS, RafiqueMS, HusinskyW.Liquid assisted ablation of zirconium for the growth of LIPSS at varying pulse durations and pulse energies by femtosecond laser irradiation. Nucl Instrum Meth B. 2015;349:230–238. doi: 10.1016/j.nimb.2015.02.017
32.
Turon-VinasM, AngladaM.Strength and fracture toughness of zirconia dental ceramics. Dent Mater. 2018;34(3):365–375. doi: 10.1016/j.dental.2017.12.007
33.
JeffreyYT, BrianRS, JeffreyRP, Adhesion/cementation to zirconia and other non-silicate ceramics: where are we now?Dent Mater. 2011;27(1):71–82. doi: 10.1016/j.dental.2010.10.022
34.
CattaniLM, ScherrerSS, RichardJ, Surface roughness and EDS characterization of a Y-TZP dental ceramic treated with the CoJet™ Sand. Dent Mater. 2010;26(11):1035–1042. doi: 10.1016/j.dental.2010.06.005
35.
InokoshiM, De MunckJ, MinakuchiS, Meta-analysis of bonding effectiveness to zirconia ceramics. J Dent Res. 2014;93(4):329–334. doi: 10.1177/0022034514524228
36.
TanakaK, KimotoK, SawadaT, Shear bond strength of veneering composite resin to titanium nitride coating alloy deposited by radiofrequency sputtering. J Dent. 2006;34(4):277–282. doi: 10.1016/j.jdent.2005.07.002
37.
QueirozJRC, DuarteDA, SouzaROA, Deposition of SiOx thin films on Y-TZP by reactive magnetron sputtering: influence of plasma parameters on the adhesion properties between Y-TZP and resin cement for application in dental prosthesis. Mater Res. 2011;14(2):212–216. doi: 10.1590/S1516-14392011005000032
38.
QueirozJRC, MassiM, NogueiraJL, Silica-based nano-coating on zirconia surfaces using Reactive magnetron sputtering: effect on chemical adhesion of resin Cements. J Adhes Dent. 2013;15(2):151–159.
39.
WandscherVF, ProchnowC, RippeMP, Retentive strength of Y-TZP crowns: comparison of different silica coating methods on the intaglio surfaces. Oper Dent. 2017;42(5):121–133. doi: 10.2341/16-090-L
40.
PiascikJR, SwiftEJ, ThompsonJY, Surface modification for enhanced silanation of zirconia ceramics. Dent Mater. 2009;25(9):1116–1121. doi: 10.1016/j.dental.2009.03.008
41.
CaegC, LeinfelderKF, LacefieldWR, Effectiveness of a method used in bonding resins to metal. J Prosthet Dent. 1990;64(1):37–41. doi: 10.1016/0022-3913(90)90150-B
42.
AungSSMP, TakagakiT, LyannSK, Effects of alumina-blasting pressure on the bonding to super/ultra-translucent zirconia. Dent Mater. 2019;35(5):730–739. doi: 10.1016/j.dental.2019.02.025