In the present paper, the possible relationships among the variables of the potentiodynamic anodic polarisation (PAP) test and the electrochemical potentiokinetic reactivation (EPR) test, both performed on resistance spot welding joints of AISI 304 stainless steel, are investigated. Results show that PAP variables are statistically independent from those of EPR, which implies independence between the pitting corrosion behaviour and the degree of sensitisation of the material. Parameters from PAP test are dependent among them, but this association is found noisy since the current density along the passive zone is not exactly constant. The parameters from the EPR test are confirmed as very related, presenting a linear relationship and a high coefficient of determination.
HamidinejadSMKolahanFKokabiAH.The modeling and process analysis of resistance spot welding on galvanized steel sheets used in car body manufacturing. Mater Des. 2012; 34: 759–767.
2.
ÖzyürekD.An effect of weld current and weld atmosphere on the resistance spot weldability of 304L austenitic stainless steel. Mater Des. 2008; 29 (3): 597–603.
3.
KianersiDMostafaeiAMohammadiJ.Effect of welding current and time on the microstructure, mechanical characterizations, and fracture studies of resistance spot welding joints of AISI 316L austenitic stainless steel. Metall Mater Trans A Phys Metall Mater Sci. 2014; 45 (10): 4423–4442.
4.
MarashiPPouranvariMSanaeeSMH. Relationship between failure behaviour and weld fusion zone attributes of austenitic stainless steel resistance spot welds. Mater Sci Technol. 2008; 24 (12): 1506–1512.
5.
SalvadorCFAntunesRA.FCAW repair welding cycles, HAZ microstructure and corrosion resistance of 2304 duplex stainless steel. Corros Eng Sci Technol. 2016; 51 (8): 573–580.
6.
RodriguesCADPagottoJFMotheoAJ. The effect of titanium on pitting corrosion resistance of welded supermartensitic stainless steel. Corros Eng Sci Technol. 2017; 52 (2): 141–148.
7.
ChengFTLoKHManHC.NiTi cladding on stainless steel by TIG surfacing process. Part II. Corrosion behavior. Surf Coatings Technol. 2003; 172 (2-3): 316–321.
8.
LinYCJiangYQZhangXC. Effect of creep-aging processing on corrosion resistance of an Al–Zn–Mg–Cu alloy. Mater Des. 2014; 61: 228–238.
9.
BaiGLuSLiD. Intergranular corrosion behavior associated with delta-ferrite transformation of Ti-modified Super304H austenitic stainless steel. Corros Sci. 2015; 90: 347–358.
10.
PadilhaAFRiosPR.Decomposition of austenite in austenitic stainless steels. ISIJ Int. 2002; 42 (4): 325–327.
11.
SrinivasanNKainVBirbilisN. Near boundary gradient zone and sensitization control in austenitic stainless steel. Corros Sci. 2015; 100: 544–555.
12.
WasnikDNDeyGKKainV. Precipitation stages in a 316L austenitic stainless steel. Scr Mater. 2003; 49 (2): 135–141.
13.
BühlerHEGerlachLGrevenO. The electrochemical reactivation test (ERT) to detect the susceptibility to intergranular corrosion. Corros Sci. 2003; 45 (10): 2325–2336.
14.
De TiedraPMartínÓLópezM. Use of EPR test to study the degree of sensitization in resistance spot welding joints of AISI 304 austenitic stainless steel. Corros Sci. 2011; 53 (4): 1563–1570.
15.
MatulaMHyspeckaLSvobodaM. Intergranular corrosion of AISI 316L steel. Mater Charact. 2001; 46 (2-3): 203–210.
16.
BoseADePK.An EPR study on the influence of prior cold work on the degree of sensitization of AISI 304 stainless steel. Corrosion. 1987; 43 (10): 624–631.
17.
MudaliUKDayalRKGnanamoorthyJB. High nitrogen steels relationship between pitting and intergranular corrosion of Nitrogen-bearing Austenitic stainless steels. ISIJ Int. 1996; 36 (7): 799–806.
18.
De TiedraPMartínÓLópezM.Combined effect of resistance spot welding and post-welding sensitization on the degree of sensitization of AISI 304 stainless steel. Corros Sci. 2011; 53 (8): 2670–2675.
19.
ProhaskaMKanduthHMoriG. On the substitution of conventional corrosion tests by an electrochemical potentiokinetic reactivation test. Corros Sci. 2010; 52 (5): 1582–1592.
20.
Čı´halVŠtefecR.On the development of the electrochemical potentiokinetic method. Electrochim Acta. 2001; 46 (24-25): 3867–3877.
21.
WuTFChengTPTsaiWT.Effect of electrolyte composition on the electrochemical potentiokinetic reactivation behavior of Alloy 600. J Nucl Mater. 2001; 295: 233–243. doi:10.1016/S0022-3115(01)00558-X.
22.
WuTFTsaiWT.Effect of KSCN and its concentration on the reactivation behavior of sensitized alloy 600 in sulfuric acid solution. Corros Sci. 2003; 45 (2): 267–280.
23.
MartínÓDe TiedraPLópezM.Artificial neural networks for pitting potential prediction of resistance spot welding joints of AISI 304 austenitic stainless steel. Corros Sci. 2010; 52 (7): 2397–2402.
24.
Jiménez-ComeMJMuñozEGarcíaR. Pitting corrosion behaviour of austenitic stainless steel using artificial intelligence techniques. J Appl Log. 2012; 10 (4): 291–297.
25.
Jiménez–ComeMJTuriasIJTrujilloFJ.An automatic pitting corrosion detection approach for 316L stainless steel. Mater Des. 2014; 56: 642–648.
26.
Fernández-DelgadoMCernadasEBarroS. Do we Need Hundreds of Classifiers to Solve Real World Classification Problems?J Mach Learn Res. 2014; 15: 3133–3181.
27.
HastieTTibshiraniRFriedmanJ.The elements of statistical learning. 2nd ed.New York (NY): Springer; 2009.
28.
de SantosSSTakahashiDYNakataA. A comparative study of statistical methods used to identify dependencies between gene expression signals. Brief Bioinform. 2014; 15 (6): 906–918.
29.
KinneyJBAtwalGS.Equitability, mutual information, and the maximal information coefficient. Proc Natl Acad Sci. 2014; 111 (9): 3354–3359.
30.
ReshefDNReshefYAMitzenmacherM. Cleaning up the record on the maximal information coefficient and equitability. Proc Natl Acad Sci USA. 2014; 111 (33): E3362–E3363.
31.
SimonNTibshiraniR.Comment on “Detecting Novel Associations In Large Data Sets” by Reshef et al, Science Dec 16, 2011. Cornell Univ Libr. 2014; 2009: 1–3. Available from: http://arxiv.org/abs/1401.7645.
ReshefDReshefYMitzenmacherM. Equitability analysis of the maximal information coefficient, with comparisons. Cornell Univ Libr. 2013: 22. doi:1301.6314.
34.
ASTM A 262-91. Standard practices for detecting susceptibility to intergranular attack in austenitic stainless steels; 1993.
35.
AslanlarS.The effect of nucleus size on mechanical properties in electrical resistance spot welding of sheets used in automotive industry. Mater Des. 2006; 27 (2): 125–131.
36.
PouranvariMMarashiSPH.Factors affecting mechanical properties of resistance spot welds. Mater Sci Technol. 2010; 26 (9): 1137–1144. doi:10.1179/174328409X459301.
37.
NarimaniNZareiBPouraliakbarH. Predictions of corrosion current density and potential by using chemical composition and corrosion cell characteristics in microalloyed pipeline steels. Measurement. 2015; 62: 97–107.
38.
SahaDCJiCWParkYD.Coating behaviour and nugget formation during resistance welding of hot forming steels. Sci Technol Weld Join. 2015; 20 (8): 708–720.
PeredaMSantosJIMartínÓ. Direct quality prediction in resistance spot welding process: Sensitivity, specificity and predictive accuracy comparative analysis. Sci Technol Weld Join. 2015; 20 (8): 679–685.
41.
GarciaCde TiedraMPBlancoY. Intergranular corrosion of welded joints of austenitic stainless steels studied by using an electrochemical minicell. Corros Sci. 2008; 50 (8): 2390–2397.
42.
VitekJMDavidSAHinmanCR.Improved ferrite number prediction model that accounts for cooling rate effects-part 1: model development. Weld J. 2003: 82 (1): 10s–17s.
43.
VitekJMDavidSAHinmanCR.Improved Ferrite Number Prediction Model that Accounts for Cooling Rate Effects- Part 2 : Model Results. Weld J. 2003; 82 (2): 43s–50s.
44.
PanQYHuangWDSongRG. The improvement of localized corrosion resistance in sensitized stainless steel by laser surface remelting. Surf Coat Technol. 1998; 102 (3): 245–255.
45.
PujarMGDayalRKGillTPS. Role of delta-ferrite in the dissolution of passive films on the austenitic stainless-steel weld metals. J Mater Sci Lett. 1999; 18 (10): 823–826. doi:10.1023/A:1006657604758.
46.
Della RovereCAAquinoJMRibeiroCR. Corrosion behavior of radial friction welded supermartensitic stainless steel pipes. Mater Des. 2015; 65: 318–327.
47.
ZhangPLiuZ.Physical-mechanical and electrochemical corrosion behaviors of additively manufactured Cr-Ni-based stainless steel formed by laser cladding. Mater Des. 2016; 100: 254–262.
48.
ASTM G5-94 (Reapproved 1999). Standard reference test method for making potentiostatic and potentiodynamic anodic polarization measurements; 1999.
49.
De TiedraPMartínÓSan-JuanM.Potentiodynamic study of the influence of gamma prime and eta phases on pitting corrosion of A286 superalloy. J Alloys Compd. 2016; 673: 231–236.
50.
LiHBJiangZHFengH. Microstructure, mechanical and corrosion properties of friction stir welded high nitrogen nickel-free austenitic stainless steel. Mater Des. 2015; 84: 291–299.
51.
AtapourMSarlakHEsmailzadehM.Pitting corrosion susceptibility of friction stir welded lean duplex stainless steel joints. Int J Adv Manuf Technol. 2016; 83: 721–728.
52.
MartínÓDe TiedraPSan-JuanM.Study of influence of gamma prime and eta phases on corrosion behaviour of A286 superalloy by using electrochemical potentiokinetic techniques. Mater Des. 2015; 87: 266–271.
53.
ASTM Standard G108-92. Standard test method for electrochemical reactivation (EPR) for detecting sensitization of AISI type 304 and 304L stainless steels; 1993.
54.
DuK-LSwamyMNS.Neural networks and statistical learning. London: Springer; 2014.
55.
SmolaAJSchölkopfB.A tutorial on support vector regression. Stat Comput. 2004; 14 (3): 199–222.
FriedmanJH.Greedy function approximation: A aradient boosting machine. Ann Stat. 2001; 29 (5): 1189–1232.
58.
SzékelyGJRizzoMLBakirovNK.Measuring and testing dependence by correlation of distances. Ann Stat. 2007; 35 (6): 2769–2794.
59.
HellerRHellerYGorfineM.A consistent multivariate test of association based on ranks of distances. Biometrika2013; 100 (2): 503–510.
60.
ReshefDReshefYFinucaneH. Detecting novel associations in large data sets. Science. 2011; 334 (6062): 1518–1524. doi: 10.1126/science.1205438
61.
ChenYZengYLuoF. A new algorithm to optimize maximal information coefficient. PLoS One. 2016; 11 (6): e0157567. DOI:10.1371/journal.pone.0157567.
62.
GarcíaCMartínFBlancoY. Effect of ageing heat treatments on the microstructure and intergranular corrosion of powder metallurgy duplex stainless steels. Corros Sci. 2010; 52 (11): 3725–3737.