In this study, the influence of the microstructural evolution of galvannealed (GA) coating and the thermomechanical characteristics of liquid metal embrittlement (LME) cracking during resistance spot welding (RSW) of steels were investigated. The analysis of LME cracks, coating microstructure and thermomechanical characteristics at various weld regions revealed a synergistic effect of liquid Zn, α-Fe(Zn), and tensile stress on LME cracking during RSW. A continuous α-Fe(Zn) layer inhibits liquid Zn from contacting the steel substrate; hence, LME was suppressed. However, a long-duration, high-magnitude tensile stress can fragment the α-Fe(Zn) layer and enable LME cracking. Conversely, α-Fe(Zn) particles allow the easy infiltration of liquid into the steel and make the crack on tensile stress development.
MarderAR, MarderARR.The metallurgy of zinc-coated steel. Prog Mater Sci.2000; 45:191–271. doi:10.1016/S0079-6425(98)00006-1.
3.
ChunEJ, LimSS, KimYT, Influence of heat-treated Al–Si coating on the weldability and microstructural inhomogeneity for hot stamped steel resistance nut projection welds. Met Mater Int.2019; 25:179–192. doi:10.1007/s12540-018-0108-5.
4.
JiC, ParkC, KimC, A comparative study of weldable current range on AC and MFDC resistance spot welding for 440 MPa grade steel sheet. J Weld Join.2017; 35:34–42. doi:10.5781/jwj.2017.35.1.34.
5.
MuruganSP, CheepuM, VijayanV, The resistance spot weldability of a stainless steel/aluminium/low carbon steel 3-ply clad sheet. J Weld Join.2018; 36:25–33. doi:10.5781/jwj.2018.36.1.3.
6.
KimJW, MuruganSP, YooJH, Enhancing nugget size and weldable current range of ultra-high-strength steel using multi-pulse resistance spot welding. Sci Technol Weld Join.2020; 25:235–242. doi:10.1080/13621718.2019.1680483.
7.
BhattacharyaD.Liquid metal embrittlement during resistance spot welding of Zn-coated high-strength steels. Mater Sci Technol. (United Kingdom)2018; 34:1809–1829. doi:10.1080/02670836.2018.1461595.
8.
FreiJ, RethmeierM.Susceptibility of electrolytically galvanized dual-phase steel sheets to liquid metal embrittlement during resistance spot welding. Weld World.2018; 62:1031–1037. doi:10.1007/s40194-018-0619-1.
9.
LingZ, WangM, KongL, Towards an explanation of liquid metal embrittlement cracking in resistance spot welding of dissimilar steels. Mater Des.2020; 195:109055. doi:10.1080/10426914.2020.1779935.
10.
DiGiovanniC, HeL, PistekU, Role of spot weld electrode geometry on liquid metal embrittlement crack development. J Manuf Process.2020; 49:1–9. doi:10.1016/j.jmapro.2019.11.015.
11.
MuruganSP, VijayanV, JiC, Four types of LME cracks in RSW of Zn-coated AHSS. Weld J.2020; 99:75–92.
12.
BealC, KleberX, FabregueD, Embrittlement of a zinc coated high manganese TWIP steel. Mater Sci Eng A.2012; 543:76–83. doi:10.1016/j.msea.2012.02.049.
13.
KangH, ChoL, LeeC, Zn penetration in liquid metal embrittled TWIP steel. Metall Mater Trans A.2016; 47:2885–2905. doi:10.1007/s11661-016-3475-x.
14.
RazmpooshMH, MacwanA, GoodwinF, Role of random and coincidence site lattice grain boundaries in liquid metal embrittlement of iron (FCC)-Zn Couple. Metall Mater Trans A Phys Metall Mater Sci.2020; 51:3938–3944. doi:10.1007/s11661-020-05857-3.
15.
DiGiovanniC, BiroE, ZhouNY.Impact of liquid metal embrittlement cracks on resistance spot weld static strength. Sci Technol Weld Join.2019; 24:218–224. doi:10.1080/13621718.2018.1518363.
16.
TumuluruM.Effect of silicon and retained austenite on the liquid metal embrittlement cracking behavior of GEN3 and high-strength automotive steels. Weld J.2019; 98:351S-364S. doi:10.29391/2019.98.029.
17.
MuruganSP, MahmudK, JiC, Critical design parameters of the electrode for liquid metal embrittlement cracking in resistance spot welding. Weld World.2019; 63:1613–1632. doi:10.1007/s40194-019-00797-y.
18.
BöhneC, MeschutG, BieglerM, Prevention of liquid metal embrittlement cracks in resistance spot welds by adaption of electrode geometry. Sci Technol Weld Join.2019; 25(4):303–310. doi:10.1080/13621718.2019.1693731.
19.
LingZ, ChenT, KongL, Liquid metal embrittlement cracking during resistance spot welding of galvanized Q&P980 steel. Metall Mater Trans A Phys Metall Mater Sci.2019; 50:5128–5142. doi:10.1007/s11661-019-05388-6.
20.
ChoiDY, SharmaA, UhmSH, Liquid metal embrittlement of resistance spot welded 1180 TRIP steel: effect of electrode force on cracking behavior. Met Mater Int.2019; 25:219–228. doi:10.1007/s12540-018-0180-x.
21.
LeeH, JoMC, SohnSS, Microstructural evolution of liquid metal embrittlement in resistance-spot-welded galvanized TWinning-induced Plasticity (TWIP) steel sheets. Mater Charact.2019; 147:233–241. doi:10.1016/j.matchar.2018.11.008.
22.
HongSH, KangJH, KimD, Si effect on Zn-assisted liquid metal embrittlement in Zn-coated TWIP steels: importance of Fe-Zn alloying reaction. Surf Coatings Technol.2020; 393(125809). doi:10.1016/j.surfcoat.2020.125809.
23.
MuruganSP, KimJ, KimJ, Role of liquid Zn and α-Fe(Zn) on liquid metal embrittlement of medium Mn steel: an ex-situ microstructural analysis of galvannealed coating during high temperature tensile test. Surf Coat Technol.2020; 398:126069. doi:10.1016/j.surfcoat.2020.126069.
24.
ISO 5821:2009. Resistance welding — spot welding electrode caps; 2009.
25.
KangJH, KimD, KimDH, Fe-Zn reaction and its influence on microcracks during hot tensile deformation of galvanized 22MnB5 steel. Surf Coatings Technol.2019; 357:1069–1075. doi:10.1016/j.surfcoat.2018.08.010.
26.
RazmpooshMH, MacwanA, GoodwinF, Crystallographic study of liquid-metal-embrittlement crack path. Mater Lett.2020; 267:127511. doi:10.1016/j.matlet.2020.127511.