Liquid metal embrittlement (LME) cracking can occur during resistance spot welding (RSW) in zinc-coated advanced high-strength steels (AHSS) for automotive production. In this study, a methodological variation of hold time is performed to investigate the process-related crack influence factors. A combination of numerical and experimental investigations confirms, that the extent of heat dissipation and re-heating of the sheet surface can be influenced and thus the degree of crack formation can be controlled in a targeted manner by the parameterisation of the hold time. The temperature and stress history of crack-free and crack-afflicted spot welds are analysed and a conclusion on the borders defining the LME active region is derived.
MeschutG, MatzkeM, HoerholdR, Hybrid technologies for joining ultra-high-strength boron steels with aluminum alloys for lightweight car body structures. Procedia CIRP. 2014; 23:19–23. doi: 10.1016/j.procir.2014.10.089
2.
SchmittJ-H, IungT.New developments of advanced high-strength steels for automotive applications. C R Phys. 2018; 19:641–656. doi: 10.1016/j.crhy.2018.11.004
3.
ManladanSM, AbdullahiI, HamzaMF.A review on the application of resistance spot welding of automotive sheets. J Eng Techn. 2015; 10:20–37.
4.
LingZ, WangM, KongL.Liquid metal embrittlement of galvanized steels during Industrial processing: a review. In: ChenS, ZhangY, FengZ, editors. Transactions on Intelligent Welding Manufacturing. Singapore: Springer; 2018. p. 25–42. doi:10.1007/978-981-10-8330-3_2.
5.
BhattacharyaD.Liquid metal embrittlement during resistance spot welding of Zn-coated high-strength steels. Mater Sci Technol. 2018; 34:1809–1829. doi: 10.1080/02670836.2018.1461595
6.
ChoiD-Y, UhmS, EnloeC, Liquid metal embrittlement of resistance spot welded 1180TRIP steel – effects of crack geometry on weld mechanical performance. In: Contributed papers from MS&T17. Proceedings; 2017 Oct 08–10. p. 454–462.
7.
DiGiovanniC, HanX, PowellA, Experimental and numerical analysis of liquid metal embrittlement crack location. J Materi Eng and Perform. 2019; 28:2045–2052. doi: 10.1007/s11665-019-04005-2
8.
DiGiovanniC, BiroE, ZhouNY.Impact of liquid metal embrittlement cracks on resistance spot weld static strength. Sci Technol Weld Joining. 2019; 24:218–224. doi: 10.1080/13621718.2018.1518363
9.
AshiriR, ShamanianM, SalimijaziHR, Liquid metal embrittlement-free welds of Zn-coated twinning induced plasticity steels. Scr Mater. 2016; 114:41–47. doi: 10.1016/j.scriptamat.2015.11.027
10.
SiglerDR, SchrothJG, YangW, Observations of liquid metal-assisted cracking in resistance spot welds of zinc-coated advanced high-strength steels. In: Sheet metal welding conference XIII. Proceedings; 2008 May 14–16; Livonia, MI, USA.
11.
ChoiD-Y, SharmaA, JungJP.Parametric study for liquid metal embrittlement in resistance spot welds of galvanized trip steel. In: Sheet metal welding conference XVIII. Proceedings; 2018 Oct 17–18; Livonia, MI, USA.
12.
KimYG, KimIJ, KimJS, Evaluation of surface crack in resistance spot welds of Zn-coated steel. Mater Trans. 2014; 55:171–175. doi: 10.2320/matertrans.M2013244
13.
SierlingerR, GruberM.A cracking good story about liquid metal embrittlement during spot welding of advanced high strength steels. In: Steels in cars and trucks 2017. Proceedings; 2017 Jun 18–22; Noordwijkerhout/Amsterdam.
14.
FreiJ, RethmeierM.Susceptibility of electrolytically galvanized dual-phase steel sheets to liquid metal embrittlement during resistance spot welding. Weld World. 2018; 62:1031–1037. doi: 10.1007/s40194-018-0619-1
15.
DiGiovanniC, BagS, MehlingC, Reduction in liquid metal embrittlement cracking using weld current ramping. Weld World. 2019; 63:1583–1591. doi: 10.1007/s40194-019-00790-5
16.
BenlatrecheY, DupuyT, MescoliniD, Design rules to minimize LME (liquid metal embrittlement). Presented at: Joining in car body engineering; 2019 Apr 9–11; Bad Nauheim.
17.
FritzscheC.Prüfmethoden zur Charakterisierung des Auftretens von LME beim Widerstandspunktschweißen von Stählen [Test methods to characterize the occurrence of LME during resistance spot welding of steels]. In: 24. DVS-Sondertagung Widerstandsschweißen. Proceedings; 2019 May 22–23; Duisburg. p. 171–183.
18.
WintjesE, DiGiovanniC, HeL, Effect of multiple pulse resistance spot welding schedules on liquid metal embrittlement severity. J Manuf Sci Eng. 2019; 141. doi:
10.1115/1.4044099 doi: 10.1115/1.4044099
19.
ChoiD-Y, SharmaA, UhmS-H, Liquid metal embrittlement of resistance spot welded 1180 TRIP steel: effect of electrode force on cracking behavior. Met Mater Int. 2019; 25:219–228. doi: 10.1007/s12540-018-0180-x
20.
FreiJ, BieglerM, RethmeierM, Investigation of liquid metal embrittlement of dual phase steel joints by electro-thermomechanical spot-welding simulation. Sci Technol Weld Joining. 2019; 24:624–633. doi: 10.1080/13621718.2019.1582203
21.
BöhneC, MeschutG, BieglerM, Prevention of liquid metal embrittlement cracks in resistance spot welds by adaption of electrode geometry. Sci Technol Weld Joining. 2019; 39:1–8.
22.
VDA 239-100:2016 sheet steel for cold forming (German version). Verband der Automobilindustrie (VDA), Germany; 2016.
23.
ISO 5821:2009 resistance welding – spot welding electrode caps (German version). Deutsches Institut für Normung (DIN), Germany; 2009.
24.
SEP 1220-2:2011 testing and documentation guideline for the joinability of thin sheet of steel – part 2: resistance spot welding. Düsseldorf: Verlag Stahleisen GmbH; 2011.
25.
ISO/TS 18166:2016 numerical welding simulation – execution and documentation (German version). Deutsches Institut für Normung (DIN), Germany; 2016.
26.
DiGiovanniC, HeL, PistekU, Role of spot weld electrode geometry on liquid metal embrittlement crack development. J Manuf Process. 2020; 49:1–9. doi: 10.1016/j.jmapro.2019.11.015
27.
NicolasMG, OldCF.Liquid metal embrittlement. J Mater Sci. 1979; 14:1–18. doi: 10.1007/BF01028323
28.
ColineB.Mechanical behaviour of a new automotive high manganese TWIP steel in the presence of liquid zinc [Dissertation]. Lyon; 2011.
29.
MarderAR.The metallurgy of zinc-coated steel. Prog Mater Sci. 2000; 45(3):191–271. doi: 10.1016/S0079-6425(98)00006-1