Advanced high strength steels are usually coated by a zinc layer for an increased resistance against corrosion. During the resistance spot welding of zinc coated steel grades, liquid metal embrittlement (LME) may occur. As a result, cracking inside and around the spot weld indentation is observable. The extent of LME cracks is influenced by a variety of different factors. In this study, the impact of the used electrode geometry is investigated over a stepwise varied weld time. A spot welding finite element simulation is used to analyse and explain the observed effects. Results show significant differences especially for highly increased weld times. Based on identical overall dimensions, electrode geometries with a larger working plane allow for longer weld times, while still preventing LME within the investigated material and maintaining accessibility.
SchmittJ, IungT.New developments of advanced high-strength steels for automotive applications. C R Phys. 2018; 19(8):641–656. doi: 10.1016/j.crhy.2018.11.004
2.
DondersS, BrughmansM, HermansL, The effect of spot weld failure on dynamic vehicle performance. Sound Vib. 2005; 39(4):16–24.
3.
BarthelmieJ, SchramA, WeslingV.Liquid metal embrittlement in resistance spot welding and hot tensile tests of surface-refined TWIP steels. IOP Conference Series: Materials Science and Engineering, Chemnitz, Germany (18th Chemnitz Seminar on Materials Engineering); Vol. 118. 2016.
4.
JosephB, PicatM, BarbierF.Liquid metal embrittlement: a state-of-the-art appraisal. Eur Phys J Appl Phys. 1999; 5(1):19–31. doi: 10.1051/epjap:1999108
5.
BenlatrecheY, DuchetM, DupuyT, No effect of liquid metal embrittlement cracks on the mechanical performances of spot welds. 5th International Conference on Steels in Cars and Trucks, Noordwijkerhout / Amsterdam, The Netherlands; 2017.
6.
BhattacharyaD.Liquid metal embrittlement during resistance spot welding of Zn-coated high-strength steels. Mater Sci Technol. 2018; 34(15):1809–1829. doi: 10.1080/02670836.2018.1461595
7.
ChoiD, SharmaA, UhmS, Liquid metal embrittlement of resistance spot welded 1180 TRIP steel: effect of electrode force on cracking behavior. Met Mater Int. 2019; 25(1):219–228. doi: 10.1007/s12540-018-0180-x
8.
WintjesE, MacwanA, BiroE, Effect of multi-pulse welding on the LME severity in RSW joints. USA Sheet Metal Welding Conference XVIII, Livonia, Michigan; 2018.
9.
TolfE, HedegårdJ, MelanderA.Surface breaking cracks in resistance spot welds of dual phase steels with electrogalvanised and hot dip zinc coating. Sci Technol Weld Joining. 2013; 18(1):25–31. doi: 10.1179/1362171812Y.0000000068
10.
FreiJ, RethmeierM.Susceptibility of electrolytically galvanized dual-phase steel sheets to liquid metal embrittlement during resistance spot welding. Weld World. 2018; 62(5):1031–1037. doi: 10.1007/s40194-018-0619-1
11.
SahaD, ChangI, ParkY.Heat-affected zone liquation crack on resistance spot welded TWIP steels. Mater Charact. 2014; 93:40–51. doi: 10.1016/j.matchar.2014.03.016
12.
KimY, KimI, KimJ, Evaluation of surface crack in resistance spot welds of Zn-coated steel. Mater Trans. 2014; 55(1):171–175. doi: 10.2320/matertrans.M2013244
13.
HeL, DiGiovanniC, HanX, Suppression of liquid metal embrittlement in resistance spot welding of TRIP steel. Sci Technol Weld Joining. 2019; 24(6):579–586. doi: 10.1080/13621718.2019.1573011
14.
AshiriR, MortezaS, SalimijaziH, Liquid metal embrittlement-free welds of Zn-coated twinning induced plasticity steels. Scr Mater. 2015; 114:41–47. doi: 10.1016/j.scriptamat.2015.11.027
15.
ParkY, MuruganS, AshadudzzamanM, Optimized resistance spot welding conditions for complex combinations. USA Sheet Metal Welding Conference XVIII, Livonia, Michigan; 2018.
16.
SierlingerR, GruberM.A cracking good Story about liquid metal embrittlement during spot welding of advanced high strength steels. 5th International Conference on Steels in Cars and Trucks, Noordwijkerhout / Amsterdam, The Netherlands; 2017.
17.
BarthelmieJ.Untersuchung zur Flüssigmetallversprödung beim Widerstandspunktschweißen von hochmanganhaltigen Stählen [Investigation of liquid metal embrittlement during resistance spot welding of high manganese steels] [dissertation]. Clausthal: Technische Universität Clausthal; 2017.
18.
Van der AaE, HanlonD, Van der VeldtT.Resistance spot weldability of 3rd generation advanced high strength steels for automotive applications. 5th International Conference on Steels in Cars and Trucks, Noordwijkerhout / Amsterdam, The Netherlands; 2017.
19.
MuruganS, MahmudK, JiC, Critical design parameters of the electrode for liquid metal embrittlement cracking in resistance spot welding. Weld World. 2019; 63:1613–1632. doi: 10.1007/s40194-019-00797-y
20.
BenlatrecheY, DupuyT, MescoliniD, Design rules to minimize LME (liquid metal embrittlement). In: Joining in Car Body Engineering. Bad Nauheim; 2019.
21.
ISO 5821:2009 Resistance welding – spot welding electrode caps (German version). Deutsches Institut für Normung (DIN).
22.
SEP 1220-2:2011 Testing and documentation guideline for the joinability of thin sheets of steel – part 2: resistance spot welding. Stahlinstitut VDEh.
23.
FreiJ, BieglerM, RethmeierM, Investigation of liquid metal embrittlement of dual phase steel joints by electro-thermomechanical spot-welding simulation. Sci Technol Weld Joining. 2019; 24(7):624–633. doi: 10.1080/13621718.2019.1582203
24.
ISO/TS 18166:2016 Numerical welding simulation – execution and documentation (German version). Deutsches Institut für Normung (DIN).
25.
Merkblatt DVS 2902-3 (02/2016) Widerstandspunktschweißen von Stählen bis 3 mm Einzeldicke – Konstruktion und Berechnung [Technical bulletin DVS 2902-3 (02/2016) Resistance spot welding of steels with individual thicknesses up to 3 mm – construction and calculation].
26.
AshiriR, Haque MdA, JiC, Supercritical area and critical nugget diameter for liquid metal embrittlement of Zn-coated twining induced plasticity steels. Scr Mater. 2015; 109:6–10. doi: 10.1016/j.scriptamat.2015.07.006
27.
ChoiD, SharmaA, JungJ.Parametric study for liquid metal embrittlement in resistance spot welds of galvanized TRIP steel. USA Sheet Metal Welding Conference XVIII, Livonia, Michigan; 2018.
28.
IchinoseH.A simple evaluation of grain boundary diffusion in liquid metal embrittlement. Trans Jpn Inst Met. 1966; 7(1):56–58. doi: 10.2320/matertrans1960.7.56