The fatigue strength of weld joints manufactured using gas metal arc welding and cold wire GMAW (CW-GMAW) was evaluated under stress-controlled cyclic loading. The material used in this study was class ASTM 131 grade A steel, joined using ER70S wire filler metal. The addition of cold wire led to a decrease in the amount of intergranular ferrite and an increase in hardness in the heat-affected zone. The assessment of fatigue life was performed by using the Weibull distribution and the results revealed that with a 99% reliability the joints produced using the CW-GMAW process have a longer fatigue life, especially as the stress amplitude increases.
CabralT. S., BragaE. M., MendonçaE. A. M. and ScottA.: ‘Influence of procedures and transfer modes in MAG welding in the reduction of deformations on marine structure panels’, Weld. Int., 2015, 29, (12), 928–936. doi: 10.1080/09507116.2014.932993
2.
RibeiroR. A., SantosE. B. F., AssunçãoP. D. C., MacielR. R. and BragaE. M.: ‘Predicting weld bead geometry in the novel CW-GMAW process’, Weld. J., 2015, 94, (September), 301s–311s.
3.
NakamuraT. and HiraokaK.: ‘Ultranarrow GMAW process with newly developed wire melting control system’, Sci. Technol. Weld. Joi., 2001, 6, (6), 355–362. doi: 10.1179/stw.2001.6.6.355
4.
ChenM. A., WuC. S., LiS. K. and ZhangY. M.: ‘Analysis of active control of metal transfer in modified pulsed GMAW’, Sci. Technol. Weld. Joi., 2007, 12, (1), 10–14. doi: 10.1179/174329306X131848
5.
GuoN., LinS. B., ZhangL. and YangC. L.: ‘Metal transfer characteristics of rotating arc narrow gap horizontal GMAW’, Sci. Technol. Weld. Joi., 2009, 14, (8), 760–764. doi: 10.1179/136217109X12505932584655
6.
FanY. Y., FanC. L., YangC. L., LiuW. G. and LinS. B.: ‘Research on short circuiting transfer mode of ultrasonic assisted GMAW method’, Sci. Technol. Weld. Joi., 2012, 17, (3), 186–191. doi: 10.1179/1362171811Y.0000000058
7.
WeiH. L., LiH., YangL. J. and GaoY.: ‘Consumable double electrode with a single arc GMAW’, Int. J. Adv. Manuf. Technol., 2013, 68, (5–8), 1539–1550. doi: 10.1007/s00170-013-4941-x
8.
MoinuddinS. Q., KapilA., KohamaK., SharmaA., ItoK. and TanakaM.: ‘On process-structure-property interconnection in anti-phase synchronised twin-wire GMAW of low-carbon steel’, Sci. Technol. Weld. Joi., 2016, 1718, (November), 1–8. doi: 10.1080/13621718.2015.1124960
9.
ASTM A131 / A131M-14 - Standard Specification for Structural Steel for Ships, ASTM International, West Conshohocken, PA, 2014. doi: 10.1520/A0131_A0131M-14, available at http://www.astm.org
10.
AWS A5.18/A5.18M: Specification for Carbon Steel Electrodes and Rods for Gas Shielded Arc Welding, American Welding Society (AWS), Miami, FL, 2005.
11.
ASTM E3-11 - Standard Guide for Preparation of Metallographic Specimens, ASTM International, West Conshohocken, PA, 2011. doi: 10.1520/E0003-11, available at http://www.astm.org
12.
ASTM E384-16, Standard Test Method for Microindentation Hardness of Materials, ASTM International, West Conshohocken, PA, 2016. doi: 10.1520/E0384-16, available at http://www.astm.org
13.
ASTM E466-15, Standard Practice for Conducting Force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Materials, ASTM International, West Conshohocken, PA, 2015, doi:10.1520/E0466-15, available at http://www.astm.org
14.
ASTM E739-10, Standard Practice for Statistical Analysis of Linear or Linearized Stress-Life (S-N) and Strain-Life (ε-N) Fatigue Data, ASTM International, West Conshohocken, PA, 2015. doi:10.1520/E0739-10R15, available at http://www.astm.org
15.
WeibullW.: ‘A statistical distribution function of wide applicability’, J. Appl. Mech., 1951, 18, (3), 293–297.
16.
ColemanB. D.: ‘On the strength of classical fibres and fibre bundles’, J. Mech. Phys. Solids, 1958, 7, (1), 60–70. doi: 10.1016/0022-5096(58)90039-5
17.
WuH. F.: ‘Statistical analysis of tensile strength of ARALL(R) laminates’, J. Compos. Mater., 1989, 23, (10), 1065–1080. doi: 10.1177/002199838902301008
18.
SakinR. and AyI.: ‘Statistical analysis of bending fatigue life data using Weibull distribution in glass-fiber reinforced polyester composites’, Mater. Des., 2008, 29, (6), 1170–1181. doi: 10.1016/j.matdes.2007.05.005
19.
BasquinO. H.: ‘The exponential law of endurance tests’, ‘Proceedings of American society for testing and materials, ASTEA’, Vol. 10, 625–630; 1910.
20.
KunF., CarmonaH. A., AndradeJ. S. and HerrmannH. J.: ‘Universality behind Basquin's law of fatigue’, Phys. Rev. Lett., 2008, 100, (9), 094301. doi: 10.1103/PhysRevLett.100.094301
21.
AnkemS. and MargolinH.: ‘Finite element method (FEM) calculations of stress-strain behavior of alpha-beta Ti-Mn alloys: part I. Stress-strain relations’, Metall. Trans. A, 1982, 13, (4), 595–601. doi: 10.1007/BF02644424
22.
AnkemS. and MargolinH.: ‘Finite element method (FEM) calculations of stress-strain behavior of alpha-beta Ti-Mn alloys: part II. Stress and strain distributions’, Metall. Trans. A, 1982, 13, (4), 603–609. doi: 10.1007/BF02644425
23.
LindemannJ. and WagnerL.: ‘Mean stress sensitivity in fatigue of α, (α+β) and β titanium alloys’, Mater. Sci. Eng. A, 1997, 236, 1118–1121. doi: 10.1016/S0921-5093(97)00347-X
24.
ChanK. S. and LeeY.-D.: ‘Effects of deformation-induced constraint on high-cycle fatigue in Ti alloys with a duplex microstructure’, Metall. Mater. Trans. A, 2008, 39, (7), 1665–1675. doi: 10.1007/s11661-008-9540-3
25.
ChanK. S.: ‘Changes in fatigue life mechanism due to soft grains and hard particles’, Int. J. Fatigue, 2010, 32, (3), 526–534. doi: 10.1016/j.ijfatigue.2009.04.015
26.
ChanK. S.: ‘Roles of microstructure in fatigue crack initiation’, Int. J. Fatigue, Sep. 2010, 32, (9), 1428–1447. doi: 10.1016/j.ijfatigue.2009.10.005
27.
RideraR. J., HarveyaS. J. and ChandlerH. D.: ‘Fatigue and ratcheting interactions’, Int. J. Fatigue, Oct. 1995, 17, (7), 507–511. doi: 10.1016/0142-1123(95)00046-V
28.
XiaZ., KujawskiD. and EllyinF.: ‘Effect of mean stress and ratcheting strain on fatigue life of steel’, Int. J. Fatigue, 1996, 18, (5), 335–341. doi: 10.1016/0142-1123(96)00088-6
29.
DuttaK. and RayK. K.: ‘Ratcheting strain in interstitial free steel’, Mater. Sci. Eng. A, 2013, 575, 127–135. doi: 10.1016/j.msea.2013.02.052
30.
CurtisR. V. and CurtisR. V.: ‘Analysis of strength data using two- and three-parameter Weibull models’, J. Mater. Sci., Mar. 1998, 33, (5), 1151–1157. doi: 10.1023/A:1004361222711