In this study, stress corrosion cracking (SCC) resistance was evaluated for type 316LN stainless steel weld joints fabricated by advanced welding techniques such as Laser, Hybrid Laser – Tungsten inert gas (HLT) and Hybrid Laser – Metal inert gas (HLM) welding. 316 LN stainless steel base metal exhibited significantly better resistance to SCC. The solidification mode, secondary dendritic arm spacing (SDAS) and tensile residual stress distribution in the weld metal was found to strongly influence SCC resistance of 316LN stainless steel weld joints. The weld joint processed by HLM process exhibited the highest time to failure during SCC testing and hence better SCC resistance due to primary ferritic mode of solidification, finer SDAS and lower width of tensile residual stress distribution.
MozhiTAClarkWATWildeBE.The effect of nitrogen and carbon on the stress corrosion cracking performance of sensitized AISI 304 stainless steel in chloride and sulfate solutions at 250°C. Corros Sci. 1987; 27:257–273. [cited 2020 Mar 9] Available from: https://www.sciencedirect.com/science/article/pii/0010938X87900229.
5.
VehovarLVehovarAMetikoš-HukovićMInvestigations into the stress corrosion cracking of stainless steel alloyed with nitrogen. Mater Corros. 2002; 53:316–327. doi:10.1002/1521-4176(200205)53:5%3C316::AID-MACO316%3E3.0.CO.
6.
KainV.Stress corrosion cracking (SCC) in stainless steels [internet]. In: Stress Corros. Crack. Theory Pract. Woodhead Publishing Limited; 2011. doi:10.1533/9780857093769.3.199.
ShaikhHAnitaTDayalRKEffect of metallurgical variables on the stress corrosion crack growth behaviour of AISI type 316LN stainless steel. Corros Sci. 2010; 52:1146–1154. [cited 2019 Aug 21] Available from: https://www.sciencedirect.com/science/article/pii/S0010938X09006465.
12.
GhoshSRanaVPSKainVRole of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel. Mater Des. 2011; 32:3823–3831. doi:10.1016/j.matdes.2011.03.012.
13.
TawancyHMAl-HadhramiLM.Case study: pitting and stress corrosion cracking in heat-affected zone of welded underground 304 stainless steel pipe. J Mater Eng Perform. 2012; 21:1757–1762.
14.
RahimiSMehrezKMarrowTJ.Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel. Corros Eng Sci Technol. 2016; 51:383–391.
WangJSuHChenKEffect of δ-ferrite on the stress corrosion cracking behavior of 321 stainless steel. Corros Sci. 2019; 158:108079.
17.
NanavatiPKKoteckiDJSomanSN.Effect of weld metal ferrite content on mechanical properties and stress corrosion cracking resistance in 22 Cr 5 Ni duplex stainless steel. Weld World. 2019; 63:793–805.
18.
FuZHLiTShanMLHydrogen atoms on the SCC behavior of SUS301L-MT stainless steel laser-arc hybrid welded joints. Corros Sci. 2019; 148:272–280.
19.
PallaviPVermaJTaiwadeRInfluence of advanced laser-arc hybrid welding and conventional MIG process on microstructure, mechanical properties and corrosion resistance of dissimilar joints. Mater Res Express. 2018; 5(6):066558.
TandlerMVehovarLDolečekVPrediction of the remaining lifetime of stainless steels under conditions of stress corrosion cracking. Mater Corros. 2003; 54:595–600.
22.
LeinonenH.Stress corrosion cracking and life prediction of austenitic stainless steels in calcium chloride solution. Corrosion. 1995; 52:337–346.
RagavendranMVasudevanM.Laser and hybrid laser welding of type 316L(N) austenitic stainless steel plates. Mater Manuf Process. 2020: 1–13. [cited 2020 Apr 27] Available from: https://www.tandfonline.com/doi/full/10.1080/10426914.2020.1745231.
AlwinBLakshminarayananAKVasudevanMAssessment of stress corrosion cracking resistance of activated Tungsten Inert Gas-welded duplex stainless steel joints. J Mater Eng Perform. 2017; 26:5825–5836.
27.
RajaKSRaoKP.Effect of applied potentials on room temperature stress corrosion cracking of austenitic stainless steel weldments. Corrosion. 1992; 48:634–640. doi:10.5006/1.3315983.
28.
ShaikhHKhatakHSGnanamoorthyJB.Stress corrosion cracking of weldments of AISI type 316 stainless steel. Mater Corros. 1987; 38:183–187.
29.
KosekiTMatsumiyaTYamadaWNumerical modeling of solidification and subsequent transformation of Fe-Cr-Ni alloys. Metall Mater Trans A. 1994; 25:1309–1321. doi:10.1007/BF02652305.
30.
MukaiYWatanabeMMurataM.Fractographic observation of stress-corrosion cracking of AISI 304 stainless steel in boiling 42 percent magnesium-chloride solution. In: StraussBMCullenWH, editors. Fractography Fail Anal [internet]. West Conshohocken, PA: ASTM International; 1978. p. 164–175. Available from: https://www.astm.org/DIGITAL_LIBRARY/STP/PAGES/STP38091S.htm.
KrishnanKNRaoKP.Effect of ferrite content and weld heat input on the room temperature stress corrosion cracking resistance of austenitic clad metals. Mater Corros. 1990; 41:178–184.