In this study, graphene nanoplatelets (0.25 and 0.5 wt-%) reinforced aluminium matrix composites were synthesised. Microstructures of composites were investigated by X-ray diffraction, scanning electron microscope and transmission electron microscope. Hardness was measured according to the Vickers test method. Tensile tests were performed at both room (25°C) and elevated temperatures (150°C and 250°C). Results showed that hardness was improved with direct addition of graphene. Microstructure of composites was free of macro defects. Yield and tensile strength behaviours of pure aluminium were increased with the addition of graphene especially at room temperature. Graphene-reinforced samples have higher compressive residual stress. From the outer surface to inner surface, transition from compressive to tensile residual stress was observed for samples.
Pérez-BustamanteRBolaños-MoralesDBonilla-MartínezJMicrostructural and hardness behavior of graphene-nanoplatelets/aluminum composites synthesized by mechanical alloying. J. Alloys Compd. 2014; 615:S578–S582.
2.
RashadMPanFTangAEffect of graphene nanoplatelets addition on mechanical properties of pure aluminum using a semi-powder method. Prog Nat Sci Mater Int. 2014; 24(2):101–108.
3.
ChoiWLahiriISeelaboyinaRSynthesis of graphene and its applications: a review. Crit Rev Solid State Mater Sci. 2010; 35(1):52–71.
4.
MoghadamADOmraniEMenezesPLMechanical and tribological properties of self-lubricating metal matrix nanocomposites reinforced by carbon nanotubes (CNTs) and graphene–a review. Compos Part B Eng. 2015; 77:402–420.
5.
TuranMESunYAkgulY.The effect of GNPs on wear and corrosion behaviors of pure magnesium. J Alloys Compd. 2017; 724:14–23.
6.
YangWChenGQiaoJGraphene nanoflakes reinforced Al-20Si matrix composites prepared by pressure infiltration method. Mater Sci Eng. 2017; 700:351–357.
7.
KumarAGulatiVKumarPParametric effects on formability of AA2024-O aluminum alloy sheets in single point incremental forming. J Mater Res Technol. 2019; 8(1):1461–1469.
8.
ThakurA.Fatigue behavior and fracture mechanism of a hot rolled AA7020 aluminum alloy. Int J Current Eng Technol. 2019; 9(3):401–404.
9.
KumarGVRaoCSPSelvarajN.Mechanical and tribological behavior of particulate reinforced aluminum metal matrix composites–a review. J Miner Mater Charact Eng. 2011; 10(1):59–91.
10.
PolatSSunYÇevikEInvestigation of wear and corrosion behavior of graphene nanoplatelet-coated B4C reinforced Al–Si matrix semi-ceramic hybrid composites. J Compos Mater. 2019; 53(25):3549–3565.
11.
YusupovKUCorthaySBondarevAVSpark plasma sintered al-based composites reinforced with BN nanosheets exfoliated under ball milling in ethylene glycol. Mater Sci Eng A. 2019; 745:74–81.
12.
AwotundeMAAdegbenjoAOObadeleBAInfluence of sintering methods on the mechanical properties of aluminium nanocomposites reinforced with carbonaceous compounds: a review. J Mater Res Technol. 2019; 8(2):2432–2449.
13.
JeyasimmanDNarayanasamyRPonalagusamyRThe effects of various reinforcements on dry sliding wear behaviour of AA 6061 nanocomposites. Mater Des. 2014; 64:783–793.
14.
EsawiAMKMorsiKSayedAThe influence of carbon nanotube (CNT) morphology and diameter on the processing and properties of CNT-reinforced aluminium composites. Compos Part Appl Sci Manuf. 2011; 42(3):234–243.
15.
TuranME.Investigation of mechanical properties of carbonaceous (MWCNT, GNPs and C60) reinforced hot-extruded aluminum matrix composites. J Alloys Compd. 2019; 788:352–360.
16.
TuranMESunYAkgulY.Improved wear properties of magnesium matrix composite with the addition of fullerene using semi powder metallurgy. Fuller Nanotub Carbon Nanostructures. 2018; 26(2):130–136.
17.
DasAHarimkarSP.Effect of graphene nanoplate and silicon carbide nanoparticle reinforcement on mechanical and tribological properties of spark plasma sintered magnesium matrix composites. J Mater Sci Technol. 2014; 30(11):1059–1070.
18.
LiJZhangXGengL.Effect of heat treatment on interfacial bonding and strengthening efficiency of graphene in GNP/Al composites. Compos Part Appl Sci Manuf. 2019; 121:487–498.
19.
Tabandeh-KhorshidMOmraniEMenezesPLTribological performance of self-lubricating aluminum matrix nanocomposites: role of graphene nanoplatelets. Eng Sci Technol Int J. 2016; 19(1):463–469.
20.
TuranMESunYAydınFInfluence of multi-wall carbon nanotube content on dry and corrosive wear performances of pure magnesium. J Compos Mater. 2018; 52(23):3127–3135.
21.
RashadMPanFAsifM.Magnesium matrix composites reinforced with graphene nanoplatelets. Graphene Mater Fundam Emerg Appl. 2015: 151–189. doi:10.1002/9781119131816.ch5.
22.
IzadiHGerlichAP.Distribution and stability of carbon nanotubes during multi-pass friction stir processing of carbon nanotube/aluminum composites. Carbon. 2012; 50(12):4744–4749.
23.
SharmaASagarSMahtoRPSurface modification of Al6061 by graphene impregnation through a powder metallurgy assisted friction surfacing. Surf Coat Technol. 2018; 337:12–23.
24.
ChenLYKonishiHFehrenbacherANovel nanoprocessing route for bulk graphene nanoplatelets reinforced metal matrix nanocomposites. Scr Mater. 2012; 67(1):9–12.
25.
ClyneTWWithersPJ.An introduction to metal matrix composites. Cambridge: Cambridge University Press; 1995.
26.
LusterJWThumannMBaumannR.Mechanical properties of aluminium alloy 6061–Al2O3 composites. Mater Sci Technol. 1993; 9(10):853–862.
27.
RashadMPanFAsifMPowder metallurgy of Mg–1%Al–1%Sn alloy reinforced with low content of graphene nanoplatelets (GNPs). J Ind Eng Chem. 2014; 20(6):4250–4255.
28.
MillerWSHumphreysFJ.Strengthening mechanisms in particulate metal matrix composites. Scr Metall Mater. 1991; 25(1):33–38.
RashadMPanFTangAImproved strength and ductility of magnesium with addition of aluminum and graphene nanoplatelets (Al+ GNPs) using semi powder metallurgy method. J Ind Eng Chem. 2015; 23:243–250.
31.
ZhangZChenDL.Consideration of orowan strengthening effect in particulate-reinforced metal matrix nanocomposites: a model for predicting their yield strength. Scr Mater. 2006; 54(7):1321–1326.
32.
RashadMPanFLinDHigh temperature mechanical behavior of AZ61 magnesium alloy reinforced with graphene nanoplatelets. Mater Des. 2016; 89:1242–1250.
33.
BemporadEBrisottoMDeperoLECritical comparison between XRD and FIB residual stress measurement techniques in thin films. Thin Solid Films. 2014; 572:224–231.
LuoQJonesAH.High-precision determination of residual stress of polycrystalline coatings using optimised XRD-Sin2ψ technique. Surf Coat Technol. 2010; 205(5):1403–1408.
36.
ZenginHTurenYTuranMEEvolution of microstructure, residual stress, and tensile properties of Mg–Zn–Y–La–Zr magnesium alloy processed by extrusion. Acta Metall Sin Engl Lett. 2019; 32:1309–1319.
37.
TuranMEAydinFSunYResidual stress measurement by strain gauge and X-ray diffraction method in different shaped rails. Eng Fail Anal. 2019; 96:525–529.
38.
TsaiSDMahulikarDMarcusHLResidual stress measurements on Al-Graphite composites using X-ray diffraction. Mater Sci Eng. 1981; 47(2):145–149.
39.
McDonaldIGMoehlenkampWMDiAResidual stresses in Cu/Ni multilayer thin films measured using the Sin 2 ψ method. Exp Mech. 2019; 59(1):111–120.
40.
TottenGHowesMInoueT.Handbook of residual stress and deformation of steel. Materials Park (OH): ASM International; 2002. p. 424–436.
41.
TuranMEOzcelikSHusemFThe effect of head hardening process on the residual stress of rails. Proc Inst Mech Eng Part F J Rail Rapid Transit. 2018; 232(2):589–595.
42.
KumarSNKeshavamurthyRHaseebuddinMRMechanical properties of aluminium-graphene composite synthesized by powder metallurgy and hot extrusion. Trans Indian Inst Met. 2017; 70(3):605–613.
43.
LiGXiongB.Effects of graphene content on microstructures and tensile property of graphene-nanosheets/aluminum composites. J Alloys Compd. 2017; 697:31–36.
44.
AhmedSJonesFR.Effect of particulate agglomeration and the residual stress state on the modulus of filled resin. Part II: moduli of untreated sand and glass bead filled composites. Composites. 1990; 21(1):81–84.
45.
RashadMPanFLiuYHigh temperature formability of graphene nanoplatelets-AZ31 composites fabricated by stir-casting method. J Magnes Alloys. 2016; 4(4):270–277.