The aim of this study was to perform micro-Raman spectroscopy as an alternative and nondestructive method to identify the phase transformation of zirconia after mechanical stress. The groups evaluated were experimental zirconia, zirconcad, IPS e.max ZirCad, and In Ceram YZ. Ten specimens were constructed for each group (n 30) and subjected to a three-point bending test with a crosshead speed of 0.5 mm/min. The fractured surfaces were analyzed by micro-Raman spectroscopy. The laser power was kept at 10 mW, and scanning was performed in three regions of the fractured surface: (i) near the source of the failure (region of tensile stress), (ii) central to the fractured surface, and (iii) far from the source of failure. All materials showed the characteristic bands of tetragonal and monoclinic phases of zirconia. All zirconia studied showed a monoclinic phase in the tensile stress region. Micro-Raman spectroscopy was effective in detecting the presence of crystalline phases in polycrystals ceramics.
PiconiC.MaccauroG.. “Zirconia as a Ceramic Biomaterial”. Biomaterials.1999. 20(1): 1–25.
2.
Vult Von SteyernP.JonssonO.NilnerK.. “Five-Year Evaluation of Posterior All-Ceramic Three-Unit (In-Ceram) FPDs”. Int. J. Prosthodont.2001. 14(4): 379–384.
3.
RaigrodskiA.J.ChicheG.J.PotiketN.HochstedlerJ.L.MohamedS.E.BilliotS.MercanteD.E.. “The Efficacy of Posterior Three-Unit Zirconium-Oxide-Based Ceramic Fixed Partial Dental Prostheses: A Prospective Clinical Pilot Study”. J. Prosthet. Dent.2006. 96(4): 237–244.
4.
SuttorD.. “Lava Zirconia Crowns and Bridges”. Int. J. Comput. Dent.2004. 7(1): 67–76.
5.
SailerI.FeherA.FilserF.GaucklerL.J.LuthyH.HammerleC.H.. “Five-Year Clinical Results of Zirconia Frameworks for Posterior Fixed Partial Dentures”. Int. J. Prosthodont.2007. 20(4): 383–388.
6.
DenryI.KellyJ.R.. “State of the Art of Zirconia for Dental Applications”. Dent. Mater.2008. 24(3): 299–307.
7.
GarvieR.C.NicholsonP.S.. “Phase Analysis in Zirconia Systems”. J. Am. Ceram. Soc.1972. 55(6): 303–305.
8.
ChevalierJ.GremillardL.VirkarA.V.ClarkeD.R.. “The Tetragonal-Monoclinic Transformation in Zirconia: Lessons Learned and Future Trends”. J. Am. Ceram. Soc.2009. 92(9): 1901–1920.
9.
HanninkR.H.J.KellyP.M.MuddleB.C.. “Transformation Toughening in Zirconia-Containing Ceramics”. J. Am. Ceram. Soc.2000. 83(3): 461–487.
10.
HeuerA.H.ClaussenN.KrivenW.M.RuhleM.. “Stability of Tetragonal ZrO2 Particles in Ceramic Matrices”. J. Am. Ceram. Soc.1982. 65(12): 642–650.
11.
ManiconeP.F.Rossi IommettiP.RaffaelliL.. “An Overview of Zirconia Ceramics: Basic Properties and Clinical Applications”. J. Dent.2007. 35(11): 819–826.
12.
WulfmanC.SadounM.Lamy de la ChapelleM.. “Interest of Raman Spectroscopy for the Study of Dental Material: The Zirconia Material Example”. IRBM.2010. 31(5-6): 257–262.
13.
DevilleS.GremillardL.ChevalierJ.FantozziG.. “A Critical Comparison of Methods for the Determination of the Aging Sensitivity in Biomedical Grade Yttria-Stabilized Zirconia”. J. Biomed. Mater. Res., Part B.2005. 72(2): 239–245.
14.
ZhuW.SuganoN.PezzottiG.. “Nondestructive Inspection of Phase Transformation in Zirconia-Containing Hip Joints by Confocal Raman Spectroscopy”. J. Biomed. Opt.2013. 18(12): 127002. doi:10.1117/1.JBO.18.12.127002.
15.
PetryR.SchmittM.PoppJ.. “Raman Spectroscopy – A Prospective Tool in the Life Sciences”. ChemPhysChem.2003. 4(1): 14–30.
16.
PezzottiG.YamadaK.SakakuraS.PittoR.P.. “Raman Spectroscopic Analysis of Advanced Ceramic Composite for Hip Prosthesis”. J. Am. Ceram. Soc.2008. 91(4): 1199–1206.
17.
LiJ.TangZ.ZhangZ.LuoS.. “Study of Factors Influencing the Microstructure and Phase Content of Ultrafine Y-TZP”. Mater. Sci. Eng.: B.2003. 99(1-3): 321–324.
18.
SekulicA.FuricK.TonejcA.TonejcA.M.StubicarM.. “Determination of the Monoclinic, Tetragonal and Cubic Phases in Mechanically Alloyed ZrO2-Y2O3 and ZrO2-CoO Powder Mixtures by Raman Spectroscopy”. J. Mater. Sci. Lett.1997. 16(4): 260–262.
19.
WitkeK.ÖsterleW.SkoppA.WoydtM.. “Raman Microprobe Spectroscopy and Transmission Electron Microscopy of Thermal Sprayed ZrO2 Coatings Before and After Rub Testing of Outer Air Seals”. J. Raman Spectrosc.2001. 32(12): 1008–1014.
20.
International Standard ISO. Dental Ceramics. International Organization for Standardization: Geneve, Switzerland: 1995. 6872.
21.
SteinbrechR.W.. “Toughening Mechanisms for Ceramic Materials”. J. Eur. Ceram. Soc.1992. 10(3): 131–142.
22.
EvansA.G.CannonR.M.. “Toughening of Brittle Solids by Martensitic Transformations”. Acta Metall.1986. 34(5): 761–800.
23.
EvansA.G.. “Perspective on the Development of High-Toughness Ceramics”. J. Am. Ceram. Soc.1990. 73(2): 187–206.
24.
HeuerA.H.LangeF.F.SwainM.V.EvansA.G.. “Transformation Toughening: An Overview”. J. Am. Ceram. Soc.1986. 69(3): 1–4.
25.
HannninkR.H.J.SwainM.V.. “Metastability of the Martensitic Transformation in a 12 mol% Ceria-Zirconia Alloy: I, Deformation and Fracture Observations”. J. Am. Ceram. Soc.1989. 72(1): 90–98.
26.
SwainM.V.. “Inelastic Deformation of Mg-PSZ and Its Significance for Strength Toughness Relationship of Zirconia-Toughened Ceramics”. Acta Metall.1985. 33(11): 2083–2091.
27.
DjuradoE.BouvierP.LucazeauG.. “Crystallite Size Effect on the Tetragonal-Monoclinic Transition of Undoped Nanocrystalline Zirconia Studied by XRD and Raman Spectrometry”. J. Solid State Chem.2000. 149(2): 399–407.
28.
MatsuiK.HorikoshiH.OhmichiN.OhgaiM.YoshidaH.IkuharaY.. “Cubic-Formation and Grain-Growth Mechanisms in Tetragonal Zirconia Polycrystal”. J. Am. Ceram. Soc.2003. 86(8): 1401–1408.
29.
ChevalierJ.DevilleS.MμnchE.JullianR.LairF.. “Critical Effect of Cubic Phase on Aging in 3mol% Yttria-stabilized Zirconia Ceramics for Hip Replacement Prosthesis”. Biomaterials.2004. 25(24): 5539–5545.
30.
LazarD.R.BottinoM.C.OzcanM.ValandroL.F.AmaralR.UssuiV.BressianiA.H.A.. “Y-TZP Ceramic Processing from Coprecipitated Powders: A Comparative Study with Three Commercial Dental Ceramics”. Dent. Mater.2008. 24(12): 1676–1685.
31.
PezzottiG.PorporatiA.A.. “Raman Spectroscopic Analysis of Phase Transformation and Stress Patterns in Zirconia Hip Joints”. J. Biomed. Opt.2004. 9(2): 372–384.
32.
DietrichB.DombrowskiK.F.. “Experimental Challenges of Stress Measurements with Resonant Micro-Raman Spectroscopy”. J. Raman Spectrosc.1999. 30(10): 893–897.
33.
AtkinsonA.JainS.C.. “'Spatially Resolved Stress Analysis Using Raman Spectroscopy”. J. Raman Spectrosc.1999. 30(10): 885–891.