Attenuated Total Internal Reflection Infrared Microscopy of Multilayer Plastic Packaging Foils

Abstract

Multilayer plastic foils are important packaging materials that are used to extend the shelf life of food products and drinks. Fourier transform infrared (FT-IR) spectroscopic imaging using attenuated total internal reflection (ATR) can be used for the identification and localization of different layers in multilayer foils. A new type of ATR crystal was used in combination with a linear array detector through which large sample areas (400 × 400 μm²) could be imaged with a pixel size of 1.6 μm. The method was tested on laminated plastic packing materials containing 5 to 12 layers. The results of the identification of the different materials using ATR-FT-IR were compared with differential scanning calorimetry (DSC) and the layer thickness of the individual layers measured by ATR-FT-IR was compared with polarized light microscopy (LM) and scanning electron microscopy (SEM). It has been demonstrated that individual layers with a thickness of about 3 μm could be identified in multilayer foils with a total thickness ranging from 100 to 150 μm. The results show a spatial resolution of about 4 μm (measured at wavenumbers ranging from 1000 to 1730 cm⁻¹), which is about a factor of two better than can be obtained using transmission FT-IR imaging. An additional advantage of ATR is the ease of sample preparation. A good correspondence was found between visible and FT-IR images. The results of ATR-FT-IR imaging were in agreement with those obtained by LM, SEM, and DSC. ATR-FT-IR is superior to the combination of these techniques because it delivers both spatial and chemical information.