Tribological properties and structure of ultra-high molecular weight polyethylene after gamma irradiation

Abstract

The aim of the present study was to investigate the effects of irradiation and post treatment on the molecular structure, mechanical, and tribological properties of ultra-high molecular weight polyethylene (UHMWPE). UHMWPE was irradiated by gamma ray at doses of 120, 250, and 500 kGy in air and encapsulation by plastic film, and then posttreated in vacuum. The tribological properties were investigated by sliding UHMWPE against Si₃N₄ ceramic ball on a ball-on-disc tribometer in the presence of distilled water lubricant. The result showed that, after gamma irradiation, the crystallinity and cross-linking degree of UHMWPE increased with dose increasing, whereas its toughness and the elongation decreased sharply. All irradiated samples exhibited lower wear rates with dose in the range from 120 to 250 kGy, but, higher friction coefficients, compared with those un-irradiated. However, over 250 kGy, the wear factor began to increase, which may be associated with the ductile-brittle transition in its mechanical properties. Posttreatment in vacuum promoted residual radicals to cross-link and improved wear resistance of UHMWPE further. The 250 kGy irradiated and posttreated sample showed the best wear resistance. The wear mechanism of un-irradiated UHMWPE and those posttreated ones was mainly plowing, plastic deformation, and adhesion, whereas the irradiated samples were characterized mainly by abrasive wear.

Keywords

ultra-high molecular weight polyethylene gamma irradiation cross-linking and oxidation postirradiation treatment tribological properties

Get full access to this article

View all access options for this article.

References

Saikko

Wear and friction properties of joint materials evaluated on a reciprocation pin-on-flat apparatus

Wear, 1993, 166, 169–178.

McGee

M. A.

Howie

D.W.

Neale

S. D.

Haynes

D. R.

Pearcy

M. J.

The role of polyethylene wears in joint replacement failure

Proc. Instn Mech. Engrs, Part H: J. Engineering in Medicine, 1997, 211, 65–72.

Fan

W. M.

Wang

Tao

S. N.

Investigation of aseptic loosening of prosthesis (in Chinese)

Chin. J. Orthop., 1998, 18 (9), 518–521.

Xiong

D. S.

S. R.

Research status of bio-tribological behaviors of UHMWPE (in Chinese)

J. CUMT (Tribological Monograph), 1999, 28, 49–52.

Andrzej

Jacek

Ion beam modification of surface properties of polyethylene

Vacuum, 2003, 70, 201–206.

Xiong

D. S.

Jin

Z. M.

Tribological properties of ion implanted UHMWPE against Si₃N₄ under different lubrication conditions

Surf. Coat. Technol., 2004, 182, 149–155.

Chang

Bellare

Cohen

R. E.

Spector

Wear behavior of bulk oriented and fiber reinforced UHMWPE

Wear, 2000, 241, 109–117.

Lewis

Properties of cross linked ultra-high-molecular-weight polyethylene

Biomaterials, 2001, 22, 371–401.

Kang

P. H.

Nho

Y. C.

The effect of γ-irradiation on ultra-high molecular weight polyethylene recrystallized under different cooling conditions

Radiat. Phys. Chem., 2001, 60, 79–87.

10.

Kurtz

S. M.

Manley

Wang

Taylor

Dumbleton

Comparison of the properties of annealed crosslinked (crossfire) and conventional polyethylene as hip bearing materials

Bull. Hosp. Jt. Dis., 2002-2003, 61 (1-2), 17–26.

11.

Kurtz

S. M.

Villarraga

M. L.

Herr

M. P.

Bergstrom

J. S.

Rimnac

C. M.

Edidin

A. A.

Thermomechanical behavior of virgin and highly crosslinked ultrahigh molecular weight polyethylene used in total joint replacements

Biomaterials, 2002, 23, 3681–3697.

12.

Gencur

S. J.

Rimnaca

C. M.

Kurtzb

S. M.

Failure micromechanisms during uniaxial tensile fracture of conventional and highly crosslinked ultra-high molecular weight polyethylenes used in total joint replacements

Biomaterials, 2003, 24, 3947–3954.

13.

Muratoglu

O. K.

Greenbaum

E. S.

Bradgon

C. R.

Jasty

Freiberg

A. A.

Harris

W. H.

Surface analysis of early retrieved acetabular polyethylene liners

J. Arthroplasty, 2004, 19 (1), 68–77.

14.

Shen

F. W.

McKellop

Surface-gradient crosslinked polyethylene acetabular cups: Oxidation resistance and wear against smooth and rough femoral balls

Clin. Orthop. Relat. Res., 2005, 1 (430), 80–88.

15.

Moro

Takatori

Ishihara

Konno

Takigawa

Matsushita

Chung

U. I.

Nakamura

Kawaguchi

Surface grafting of artificial joints with a biocompatible polymer for preventing periprosthetic osteolysis

Nature Mater., 2004, 3 (1), 829–836.

16.

Amal

Joao

C. M. S.

Claudia

M. C. B.

Eloisa

B. M.

Gel fraction measurements in gamma-irradiated ultra high molecular weight polyethylene

Polym. Test., 2003, 22, 647–649.

17.

Oleg

N. T.

Sakae

Surface cross-linking of polyethelene by electron beam irradiation in air

Polymer, 1998, 39 (24), 6115–6120.

18.

Hamilton

J. V.

Schmidt

M. B.

Improved UHMWPE through the control of sterilization dose and atmosphere

Radiat. Phys. Chem., 1998, 52 (16), 283–288.

19.

Suarez

J. C.M.

Ronaldo

S. B.

Effect of gamma irradiation on the ductile-to-brittle transition in ultra-high molecular weight polyethylene

Polym. Degrad. Stabil., 2003, 82, 221–227.

20.

Tomizawa

Fischer

T. E.

Friction and wear of silicon nitride at 150 °C to 180°C, Wear, 1985, 105, 29.

21.

Ingram

J. H.

Stone

M. H.

Fisher

The influence of molecular weight, cross-linking and counterface roughness on TNF-alpha production by macrophages in response to ultra high molecular weight polyethylene particles

Biomaterials, 2004, 25 (17), 3511–3522.

22.

Marrs

Barton

D. C.

Doyle

Jones

R. A.

Lewis

E. L. V.

Ward

I. M.

Fisher

The effect of molecular orientation and acetylene-enhanced cross-linking on the wear of UHMWPE in total artificial joints

J. Mater. Sci. Mater. Med., 2001, 12 (7), 621–628.

23.

Lewis

Carroll

Effect of cross-linking on its tensile and compressive creep performance

Bio-Med. Mater. Eng., 2001, 11 (3), 167–183.

24.

Sun

J. Z.

The effect of chain flexibility and chain mobility on radiation cross-linking of polymers

Radiat. Phys. Chem., 2001, 60, 445–451.

25.

Yang

S. J.

Development of wear-enhanced all polyethylene acetabular component in total hip arthroplasty. PhD Dissertation, University of Iowa, 2003.

26.

Kurtz

S. M.

Radiation and chemical cross-linking promote strain hardening behavior and molecular alignment in ultra high molecular weight polyethylene during multi-axial loading conditions

Biomaterials, 1999, 20, 1449–1462.

27.

Barbour

P. S. M.

Barton

D. C.

Fisher

The influence of stress conditions on the wear of UHMWPE for total joint replacements

J. Mater. Sci. Mater. Med., 1997, 8, 603–611.

28.

Wang

Schmidig

Ceramic femoral heads prevent runaway wear for highly crosslinked polyethylene acetabular cups by third-body bone cement particles

Wear, 2003, 255, 1057–1063.

29.

Cooper

J. R.

Dowson

Fisher

The effect of transfer film and surface roughness on the wear of lubricated ultra-high molecular weight polyethylene

Clin. Mater., 1993, 14, 295–302.

30.

Phipatanakul

Johnson

S. A.

Good

Clarke

I. C.

The fallacy of evaluating biomaterial wear-rates with water as lubricant: A hip simulator study of alumina-PTFE and CoCr-PTFE combinations

J. Biomed. Mater. Res., 1998, 39, 229–233.

31.

Bragdon

C. R.

O'Connor

D. O.

Lowenstein

J. D.

Synivta

W. D.

The importance of multidirectional motion on the wear of polyethylene

J. Eng. Med., 1996, 210, 157–165.

32.

Wang

Stark

Dumbleton

J. H.

Mechanistic and morphological origins of ultra-high molecular weight polyethylene wear debris in total joint replacement prostheses

J. Eng. Med., 1996, 210, 141–155.