Pitch-based carbon-fibre-reinforced poly (ether—ether—ketone) OPTIMA® assessed as a bearing material in a mobile bearing unicondylar knee joint

Abstract

Abstract

The introduction of unicondylar knee prostheses has allowed the preservation of the non-diseased compartment of the knee while replacing the diseased or damaged compartment. In an attempt to reduce the likelihood of aseptic loosening, new material combinations have been investigated within the laboratory. Tribological tests (friction, lubrication, and wear) were performed on metal-on-carbon-fibre-reinforced (CFR) poly (ether—ether—ketone) (PEEK) (pitch-based) mobile unicondylar knee prostheses up to 5×10⁶ cycles. Both a loaded soak control and an unloaded soak control (both medial and lateral components) were used to compensate for weight change due to lubricant absorption. For this material combination the loaded soak control gave slightly lower wear for both the medial and the lateral components than did the unloaded soak control. The medial components gave higher steady state wear than the lateral components (1.70 mm³ per 10⁶ cycles compared with 1.02 mm³ per 10⁶ cycles with the loaded soak control). The results show that the CFR PEEK unicondylar knee joints performed well in these wear tests. They gave lower volumetric wear rates than conventional metal-on-ultra-high-molecular-weight polyethylene prostheses have given in the past when tested under similar conditions. The friction tests showed that, at physiological viscosities, these joints operated in the boundary—mixed-lubrication regime. The low wear produced by these joints seems to be a function of the material combination and not of the lubrication regime.