The moisture protection of wood coating systems is influenced by the total solid content applied as well as by the hydrophobic properties of the coating film. Water permeability, water vapour permeability and contact angle of water on wood surfaces treated with 21 different coating systems were measured. Water permeability tests were also carried out with artificial mechanical defects of the surfaces. The results showed that the influence of the total solid content applied was predominant, whereas the surface hydrophobicity was less efficient. Systems with a higher total solid content and in particular with continuous coating films showed a higher sensitivity to mechanical defects.
AholaP.1991. Moisture transport in wood coated with joinery paints.Holz Roh Werkst.49: 428–432.
2.
AholaP., DerbyshireH., HoraG., and de MeijerM.1999. Water protection of wooden window joinery painted with low organic solvent content paints with known composition.Holz Roh Werkst.57: 45–50.
3.
De VetterL., and Van AckerJ.2005. Standard testing of organosilicon compounds as wood modification agents. Proc. 2nd European Conf. on Wood Modification. Göttingen, Germany, October 2005. University of Göttingen,232–241.
4.
DerbyshireH., and MillerE. R.1996. Moisture conditions in coated exterior wood. Part1: An investigation of the moisture transmission characteristics of exterior wood coatings and the effect of weathering on coating permeability.J. Inst. Wood Sci. 14(1): 40–47.
5.
EkstedtJ.2002. Studies on the barrier properties of wood coatings. PhD thesis. Royal Institute of Technology, Stockholm, Sweden.
6.
GrüllG.2007. Bringt die Nanotechnologie das Wundermittel für Holzoberflächen? Proc. Holzschutztagung der DGfH. Biberach, Germany, September 2007. DGfH. Vol. 25, 87–92.
7.
HoraG.1994. The dynamic contact angle – a characteristic to predict the lifetime of a wood topcoat.J. Coat. Technol. 66(832): 55–59.
8.
KünnigerT., and FischerA.2011. ‘Nanobeschichtungen’ auf Holz - Erfahrungen im Außenbereich. In Venzmer 2011, Vol. 21, 111–120.
9.
MaiC., DonathS., and MilitzH.2003. Einsatz von Siliziumverbindungen zur Holzvergütung. Proc. Holzschutztagung der DGfH. Augsburg, Germany, March 2003. DGfH. Vol. 23.
10.
MaiC., DonathS., WeigenandO., and MilitzH.2005. Aspects of wood modificationn with silicon compounds: material properties and process development. Proc. 2nd European Conf. on Wood Modification. Göttingen, Germany, October 2005. University of Göttingen.222–231.
11.
ÖNORM EN 927-1. 1996. Lacke und Anstrichstoffe - Beschichtungsstoffe und Beschichtungssysteme für Holz im Außenbereich; Teil 1: Einteilung und Auswahl.
12.
ÖNORM EN 927-2. 2006. Beschichtungsstoffe - Beschichtungssysteme und Beschichtungssysteme für Holz im Außenbereich; Teil 2: Leistungsanforderungen.
13.
ÖNORM EN 927-5. 2006. Beschichtungsstoffe - Beschichtungsstoffe und Beschichtungssysteme für Holz im Außenbereich - Teil 5: Beurteilung der Wasserdurchlässigkeit.
14.
ÖNORM EN ISO 12572. 2002. Wärme- und feuchtetechnisches Verhalten von Baustoffen und Bauprodukten - Bestimmung der Wasserdampfdurchlässigkeit.
15.
ÖNORM EN ISO 2808. 2007. Paints and varnishes - Determination of film thickness
16.
TurkulinH.2006. Hydrophobic treatment for improvement of wood surface durability, Proc. 5th Woodcoatings Cong. Prague, Czech Republic, October 2006. PRA, Paper 20.