We examine the performance of clear coatings on wood treated to improve its photostability. The treatments tested were: benzoyl chloride; chromic acid; modified PF resins; vinyl benzoate; and primers containing different photostabilisers. Treated panels were finished with clear coatings containing different types/levels of photostabilisers and exposed outdoors in Australia for 2 years. The coatings performed better on treated than untreated panels, except for coatings on panels treated with a primer containing cerium oxide nanoparticles. Clear coatings performed best on wood treated with chromic acid, vinyl benzoate or PF resin containing a hindered amine light stabiliser. However, the performance of the coatings was also strongly influenced by coating type. We conclude that the performance of clear coatings can be increased if they are applied to photostable wood substrates. However, coating performance is also dependent on coating flexibility, its propensity to form surface defects, and the level/types of photostabiliser in the coatings.
BelfasJ, GrovesKW, EvansPD. 1993. Bonding surface-modified karri and jarrah with resorcinol formaldehyde. 1. The effect of sanding on wettability and shear strength.Holz Roh Werkst. 51(4): 253–259.
2.
BlackJM, MrazEA. 1974. Inorganic surface treatments for weather-resistant natural finishes. U.S. For. Serv. For. Prod. Lab., Madison, WI, USA. Research Paper FPL232.
3.
DerbyshireH, MillerER. 1981. The photodegradation of wood during solar irradiation. Part 1: Effects on the structural integrity of thin wood strips.Holz Roh Werkst. 39(8): 341–350.
4.
DuncanC. 1963. Role of microorganisms in the weathering of wood and degradation of exterior finishes. Off. Digest-Fed.Soc. Paint Tech. 35(465): 1003–1012.
5.
EvansPD. 1988. A note on assessing the deterioration of thin wood veneers during weathering.Wood Fiber Sci.20(4): 487–492.
6.
EvansPD, GibsonSK, CullisI, LiuC, SebeG. 2013. Photostabilization of wood using low molecular weight phenol formaldehyde resin and hindered amine light stabilizer.Polym. Deg. Stab. 98(1): 158–168.
7.
EvansPD, OwenNL, SchmidS, WebsterRD. 2002. Weathering and photostability of benzoylated wood.Polym. Deg. Stab. 76(2): 291–303.
8.
EvansPD, SchmalzlKJ, MichellAJ. 1993. Rapid loss of lignin at wood surfaces during natural weathering. In Kennedy et al. 1993, 335–340.
9.
EvansPD, UrbanK, ChowdhuryMJA. 2008. Surface checking of wood is increased by photodegradation caused by ultraviolet and visible light.Wood Sci Technol.42(3): 251–265.
10.
EvansPD, ThayPD, SchmalzlKJ. 1996. Degradation of surfaces during natural weathering. Effects on lignin and cellulose and on the adhesion of acrylic latex primers.Wood Sci. Technol. 30(6): 411–422.
11.
ForsthuberB, GrüllG. 2010. The effects of HALS in the prevention of photo-degradation of acrylic clear topcoats and wooden surfaces.Polym. Deg. Stab. 95(5): 746–755.
12.
FeistWC, HonDNS. 1984. Chemistry and weathering and protection. In Rowell, 401–451.
13.
FeistWC. 1990. Outdoor weathering and protection. In Rowell and Barbour, 263–298.
14.
HarrisJ, AshtonHE, O'DohertyGA. 1964. Exterior exposure of clear organic coatings on wood. Division of Building Research, National Research Council, Canada. Progress report 295, 1–19.
15.
JebraneM, SèbeG, CullisI, EvansPD. 2009. Photostabilisation of wood using aromatic vinyl esters.Polym. Deg. Stab. 94(2): 151–157.
16.
KalninsMA. 1966. Surface characteristics of wood as they affect the durability of finishes. Part 2: photochemical degradation of wood. U.S. For. Serv. For. Prod. Lab., Madison, WI, USA. Report 57, 23–60.
17.
KennedyJF, PhillipsGO, WilliamsPA. (edited). 1993. Cellulosics: pulp, fibre and environmental aspects. New York: Ellis Horwood.
18.
KiguchiM, EvansPD. 1998. Photostabilisation of wood surfaces using a grafted benzophenone UV absorber.Polym. Deg. Stab. 61(1): 33–45.
19.
KiguchiM, EvansPD, EkstedtJ, WilliamsRS, KataokaY. 2001. Improvement of the durability of clear coatings by grafting of UV-absorbers on to wood.Surf. Coat. Int. Part B: Coat. Trans. 84(4): 263–270.
20.
MeinckenM, EvansPD. 2010. Use of atomic force microscopy to detect wavelength dependent changes in wood veneers and spin-coated lignin and cellulose films exposed to solar radiation.Int. Wood Prod. J. 1(2): 75–80.
21.
OhtaniK. 1987. Chromium trioxide enhances the durability of wooden doors.Chromium Rev.8: 4–7.
22.
PandeyKK, ChandrashekarN. 2006. Photostability of wood surfaces esterified by benzoyl chloride.J. Appl. Polym. Sci. 99(5): 2367–2374.
23.
RowellRM (edited). 1984. The chemistry of solid wood. Washington DC: American Chemical Society.
24.
RowellRM, BarbourRJ. (edited). 1990. Archaeological wood: Properties, chemistry, and preservation. Washington DC: American Chemical Society.
25.
SchallerC, RogezD. 2007. New approaches in wood coating stabilization.J. Coat. Technol. Res. 4(4): 401–409.
26.
SchmalzlKJ, ForsythCM, EvansPD. 1995. The reaction of guaiacol with iron III and chromium VI compounds as a model for wood surface modification.Wood Sci. Technol. 29(4): 307–319.
27.
SchmalzlKJ, ForsythCM, EvansPD. 2003. Evidence for the formation of chromium (III) diphenoquinone complexes during oxidation of guaiacol and 2,6-dimethoxyphenol with chromic acid.Polym. Deg. Stab. 82(3): 399–407.
28.
TarkowH, SoutherlandCF, SeborgRM. 1966. Surface characteristics of wood as they affect durability of finishes. Part I. Surface stabilization. US for. Serv. for. Prod. Lab., Madison, WI, USA. Report 57, 1–22.
29.
WilliamsRS, FeistWC. 1985. Wood modified by inorganic salts: mechanism and properties. I. Weathering rate, water repellency, and dimensional stability of wood modified with chromium (III) nitrate versus chromic acid.Wood Fiber Sci. 17(2): 184–198.