The effect of acetylation on weathering resistance of a hybrid poplar (Pacific Albus®) was studied by colour change evaluation, mechanical tests, FT-IR spectroscopy and moisture absorption measurements. The acetylation process was performed without any pre-treatment and it was verified by means of weight percentage gain and FT-IR spectroscopy: the average weight percentage gain was 14.4 ± 0.6% and the band areas at 1370 and 1740 cm−1 increased about 50% compared to unmodified wood. It was also demonstrated that acetylation process increased mechanical performance and reduced wood moisture absorption. Unmodified and acetylated wood samples were artificially weathered with a Xenon-arc lamp up to 400 h. The mechanical properties of both acetylated and untreated wood showed the same trend, but acetylated samples exhibited higher stiffness, strength and elongation at break. The outcomes demonstrated that acetylated samples were more stable to degradation mechanisms induced by artificial weathering.
BonifaziG, CaliennoL, CapobiancoG, Lo MonacoA, PelosiC, PicchioR, SerrantiS.2015. Modeling color and chemical changes on normal and red heart beech wood by reflectance spectrophotometry, Fourier transform infrared spectroscopy and hyperspectral imaging. Polym Degrad Stab. 113(Suppl C):10–21. doi: 10.1016/j.polymdegradstab.2015.01.001
2.
CaiJB, DingT, YangL.2012. Dimensional stability of poplar wood after densification combined with heat treatment. Appl Mechan Mater. [accessed 2018]. https://www.scientific.net/AMM.152-154.112.
3.
CaniatoM, BettarelloF, FaustiP, FerlugaA, MarsichL, SchmidC.2017. Impact sound of timber floors in sustainable buildings. Build Environ. 120:110–122. doi: 10.1016/j.buildenv.2017.05.015
4.
CaniatoM, BettarelloF, FerlugaA, MarsichL, SchmidC, FaustiP.2017. Acoustic of lightweight timber buildings: A review. Renew Sustain Energy Rev. 80:585–596. doi: 10.1016/j.rser.2017.05.110
5.
ChangS-T, ChangH-T.2001. Comparisons of the photostability of esterified wood. Polym Degrad Stab. 71(2):261–266. doi: 10.1016/S0141-3910(00)00171-3
6.
DöményJ, ČermákP, PařilP, PozsgaynéFF, DejmalA, RademacherP.2015. Application of microwave heating for acetylation of Beech (Fagus sylvatica L.) and Poplar (Populus hybrids) wood. BioResources. 10(4):8181–8193. doi: 10.15376/biores.10.4.8181-8193
7.
EvansPD, UrbanK, ChowdhuryMJA.2008. Surface checking of wood is increased by photodegradation caused by ultraviolet and visible light. Wood Sci Technol. 42(3):251–265. doi: 10.1007/s00226-007-0175-0
8.
FabiyiJS, McDonaldAG.2010. Effect of wood species on property and weathering performance of wood plastic composites. Compos Part Appl Sci Manuf. 41(10):1434–1440. doi: 10.1016/j.compositesa.2010.06.004
9.
FangC-H, MariottiN, CloutierA, KoubaaA, BlanchetP.2012. Densification of wood veneers by compression combined with heat and steam. Eur J Wood Wood Prod. 70(1–3):155–163. doi: 10.1007/s00107-011-0524-4
10.
FojutowskiA, KozirógA, KropaczA, NoskowiakA.2014. The susceptibility of some acetylated hardwood species to mould fungi attack – an attempt to objectify the assessment. Int Biodeterior Biodegrad. 86:60–65. doi: 10.1016/j.ibiod.2013.08.007
11.
GuX, SunL, LiuG, YouCQ, KanC, ChengKH, YaoJF.2015. Chemical modification of poplar wood in gas-and liquid-phase acetylation. Wood Res. 60(2):247–254.
12.
GuoH, XuC, LinL, XuC, WangQ, FuF.2011. The composite wood by poplar wood impregnated with Na2SiO3-polyacrylamide hybrid solution. Sci Eng Compos Mater. 18(3):151–155. doi: 10.1515/secm.2011.025
13.
HillCAS, KhalilHPSA, HaleMD.1998. A study of the potential of acetylation to improve the properties of plant fibres. Ind Crops Prod. 8(1):53–63. doi: 10.1016/S0926-6690(97)10012-7
14.
JebraneM, HarperD, LabbéN, SèbeG.2011. Comparative determination of the grafting distribution and viscoelastic properties of wood blocks acetylated by vinyl acetate or acetic anhydride. Carbohydr Polym. 84(4):1314–1320. doi: 10.1016/j.carbpol.2011.01.026
15.
JebraneM, PichavantF, SèbeG.2011. A comparative study on the acetylation of wood by reaction with vinyl acetate and acetic anhydride. Carbohydr Polym. 83(2):339–345. doi: 10.1016/j.carbpol.2010.07.035
16.
JebraneM, SèbeG, CullisI, EvansPD.2009. Photostabilisation of wood using aromatic vinyl esters. Polym Degrad Stab. 94(2):151–157. doi: 10.1016/j.polymdegradstab.2008.11.013
17.
KalninsMA, FeistWC.1993. Increase in wettability of wood with weathering. For Prod J. 43(2):55.
18.
KlüppelA, CraggSM, MilitzH, MaiC.2015. Resistance of modified wood to marine borers. Int Biodeterior Biodegrad. 104:8–14. doi: 10.1016/j.ibiod.2015.05.013
19.
KnudsonR, BrunetteG.2015. Evaluation of Canadian Prairie-grown hybrid poplar for high value solid wood products. For Chron. 91(2):141–149. doi: 10.5558/tfc2015-025
20.
KuoS, BembenekR.2008. Sorption and desorption of chromate by wood shavings impregnated with iron or aluminum oxide. Bioresour Technol. 99(13):5617–5625. doi: 10.1016/j.biortech.2007.10.062
21.
LionettoF, Del SoleR, CannolettaD, VasapolloG, MaffezzoliA.2012. Monitoring wood degradation during weathering by cellulose crystallinity. Materials. 5(10):1910–1922. doi: 10.3390/ma5101910
22.
MatsunagaM, KataokaY, MatsunagaH, MatsuiH.2010. A novel method of acetylation of wood using supercritical carbon dioxide. J Wood Sci. 56(4):293–298. doi: 10.1007/s10086-009-1098-1
23.
MitsuiK.2010. Acetylation of wood causes photobleaching. J Photochem Photobiol B. 101(3):210–214. doi: 10.1016/j.jphotobiol.2010.07.005
24.
MohebbyB.2010. Application of ATR Infrared Spectroscopy in Wood Acetylation. J Agric Sci Technol. 10(0):253–259.
25.
MohebbyB, HajihassaniR.2010. Moisture Repellent Effect of Acetylation on Poplar Fibers. J Agric Sci Technol. 10:157–163.
26.
MohebbyB, MilitzH.2010. Microbial attack of acetylated wood in field soil trials. Int Biodeterior Biodegrad. 64(1):41–50. doi: 10.1016/j.ibiod.2009.10.005
27.
NagarajappaGB, PandeyKK.2016. UV resistance and dimensional stability of wood modified with isopropenyl acetate. J Photochem Photobiol B. 155(Suppl C):20–27. doi: 10.1016/j.jphotobiol.2015.12.012
28.
ObatayaE.2005. Reversible volumetric changes of acetylated wood with after-treatments. Wood Sci Technol. 39(6):472–483. doi: 10.1007/s00226-005-0017-x
29.
ObatayaE, YamauchiH.2005. Compression behaviors of acetylated wood in organic liquids. Part I. Compression in equilibrium conditions. Wood Sci Technol. 39(6):492–501. doi: 10.1007/s00226-005-0018-9
30.
OhkoshiM.2002. FTIR-PAS study of light-induced changes in the surface of acetylated or polyethylene glycol-impregnated wood. J Wood Sci. 48(5):394. doi: 10.1007/BF00770699
31.
OlteanL, TeischingerA, HansmannC.2008. Wood surface discolouration due to simulated indoor sunlight exposure. Holz Als Roh Werkst. 66(1):51. doi: 10.1007/s00107-007-0201-9
32.
OzmenN.2007. Dimensional stabilisation of fast growing forest species by acetylation. J Appl Sci. 7(5):710–714. doi: 10.3923/jas.2007.710.714
33.
PapadopoulosAN, HillCAS.2003. The sorption of water vapour by anhydride modified softwood. Wood Sci Technol. 37(3–4):221–231. doi: 10.1007/s00226-003-0192-6
34.
PapadopoulosAN, PougioulaG.2010. Mechanical behaviour of pine wood chemically modified with a homologous series of linear chain carboxylic acid anhydrides. Bioresour Technol. 101(15):6147–6150. doi: 10.1016/j.biortech.2010.02.079
35.
PapadopoulosAN, TountziarakisP.2012. Toughness of pine wood chemically modified with acetic anhydride. Eur J Wood Wood Prod. 70(1–3):399–400. doi: 10.1007/s00107-011-0544-0
36.
PardoT, AlfaroJ.2014. White-rot fungal decay resistance of teak and Melina wood treated with acetic anhydride. Int Biodeterior Biodegrad. 88:44–47. doi: 10.1016/j.ibiod.2013.12.001
37.
PlackettDV, DunninghamEA, SinghAP.1992. Weathering of chemically modified wood. Holz Als Roh Werkst. 50(4):135. doi: 10.1007/BF02663254
38.
PriesM, WagnerR, KaeslerK-H, MilitzH, MaiC.2013. Acetylation of wood in combination with polysiloxanes to improve water-related and mechanical properties of wood. Wood Sci Technol. 47(4):685–699. doi: 10.1007/s00226-013-0535-x
39.
RowellRM.2014. Acetylation of wood – a review. Int J Lignocellul Prod. 1(1):1–27.
40.
SadeghifarH, DickersonJP, ArgyropoulosDS.2014. Quantitative 31P NMR analysis of solid wood offers an insight into the acetylation of its components. Carbohydr Polym. 113(Suppl C):552–560. doi: 10.1016/j.carbpol.2014.07.046
41.
StefkeB, WindeisenE, SchwanningerM, HinterstoisserB.2008. Determination of the weight percentage gain and of the acetyl group content of acetylated wood by means of different infrared spectroscopic methods. Anal Chem. 80(4):1272–1279. doi: 10.1021/ac7020823
42.
TolvajL, MitsuiK.2005. Light source dependence of the photodegradation of wood. J Wood Sci. 51(5):468–473. doi: 10.1007/s10086-004-0693-4
43.
VestølGI, SivertsenMS.2011. Effects of outdoor weathering and wood properties on liquid water absorption in uncoated Norway spruce cladding. For Prod J. 61(5):352–358.
44.
WeiL, McDonaldAG, FreitagC, MorrellJJ.2013. Effects of wood fiber esterification on properties, weatherability and biodurability of wood plastic composites. Polym Degrad Stab. 98(7):1348–1361. doi: 10.1016/j.polymdegradstab.2013.03.027