Dry sliding wear behaviour of nickel-, iron- and cobalt-based superalloys has been investigated using pin-on-disc wear test rig. Superni 600 has shown the highest coefficient of friction, whereas that of Superco 605 is found to be least. Superfer 800H has shown the lowest value of specific wear rate whereas Superni 600 has given highest specific wear rate, followed by Superni 75. The worn samples were analysed with SEM, and the wear debris was analysed using XRD and SEM. Nickel based superalloys have shown comparatively higher wear rates than the cobalt and iron based superalloys due to the formation of NiO.
EzugwuEO: Int. J. Machine Tools Manuf., 2005, 45, 1353–1367.
3.
LiMH, SunXF, LiJG, ZhangZY, JinT, GuanHR, HuZQ: ‘Oxidation behaviour of a single-crystal Ni-base superalloy in air-I: at 800 and 900°C’, Oxid. Met., 2003, 59, 591–605.
4.
GoebelJA, PettitFS, GowardGW: ‘Mechanisms for the hot corrosion of nickel-base alloys’, Metall. Trans., 1973, 4, 261–275.
5.
TabakoffW: ‘High-temperature erosion resistance of coatings for use in turbomachinery’, Wear, 1995, 186–187, 224–229.
6.
TabakoffW: ‘Protection of coated superalloys from erosion in turbomachinery and other systems exposed to particulate flows’, Wear, 1999, 233–235, 200–208.
7.
KamarajM: ‘Rafting in single crystal nickel-base superalloys – an overview’, Sadhana - Academy Proceedings in Engineering Sciences, 2003, 28, 115–128.
8.
F. H. Stott, The Role of Oxidation in the Wear of Alloys,Trib. Int.1998, 31, 61–71.
9.
StottFH, JordanMP: ‘The effects of load and substrate hardness on the development and maintenance of wear-protective layers during sliding at elevated temperatures’, Wear, 2001, 250–251, 391–400.
DuHL, DattaPK, InmanI, GeurtsR, KubelC: ‘Microscopy of wear affected surface produced during sliding of Nimonic 80A against Stellite 6 at 20°C’, Mater. Sci. Eng. A, 2003, 357, 412–422.
12.
ZhangK, BattistonL: ‘Friction and wear characterization of some cobalt- and iron-based superalloys in zinc alloy baths’, Wear, 2002, 252, 332–344.
13.
LinDS, StottFH, WoodGC, WrightKW, AllenJH: ‘The friction and wear behaviour of nickel-base alloys in air at room temperature’, Wear, 1973, 24, 261–278.
14.
ChatterjeeUK, BoseSK, RoySK: ‘Environmental degradation of metals’, (ed. , DekkerMarcel, ed), 270; 2001, New York, Madison Avenue.
15.
RameshCS, SeshadriSK., IyerJL: ‘A model for wear rates of composite coatings’, Wear, 1992, 156, 205–209.
16.
JiangJ, StottFH, StackMM: ‘A generic model for dry sliding wear of metals at elevated temperatures’, Wear, 2004, 256, 973–985.
17.
PanagopoulosCN, PapachristosVD, ChristoffersenLW: ‘Lubricated sliding wear behaviour of Ni-P-W multilayered alloy coatings produced by pulse plating’, Thin Solid Films, 2000, 366, 155–163.
18.
JiangJ, StottFH, StackMM: ‘A mathematical model for sliding wear of metals at elevated temperatures’, Wear, 1995, 181–183, 20–31.
19.
KashaniH, AmadehA, GhasemiHM: ‘Room and high temperature wear behaviors of nickel and cobalt base weld overlay coatings on hot forging dies’, Wear, 2007, 262, 800–806.
20.
JiangJ, StottFH, StackMM: ‘Some frictional features associated with the sliding wear of the nickel-base alloy N80A at temperatures to 250°C’, Wear, 1994, 176, 185–194.
21.
JiangJ, StottFH, StackMM: ‘The role of triboparticulates in dry sliding wear’, Tribol. Int., 1998, 31, 245–256.