Lubricated friction and wear behaviour of Al–25Zn–3Cu–3Si alloy was investigated on a block-on-disc test machine in comparison with 60/40 brass and SAE 65 bronze. T6 heat treatment increased the hardness, strength and wear resistance of the Al–25Zn–3Cu–3Si alloy. This alloy exhibited much higher wear resistance than the 60/40 brass and SAE 65 bronze in both as-cast and heat-treated conditions. The results obtained from the experimental alloys are discussed in terms of their microstructure, mechanical properties and wear behaviour.
SavaşkanTMurphyS. Mechanical properties and lubricated wear of Zn-25Al based alloys. Wear1987; 116: 221–224.
2.
DelneuvilleP. Tribological behaviour of Zn-Al alloys (ZA27) compared with bronze when used as a bearing material with high load and very low speed. Wear1985; 105: 283–292.
3.
MurphySSavaşkanT. Comparative wear behaviour of Zn-Al based alloys in an automotive engine application. Wear1984; 98: 151–161.
4.
AlemdağYSavaşkanT. Mechanical and tribological properties of Al-40Zn-Cu alloys. Tribol Int2009; 42: 176–182.
5.
SavaşkanTAlemdağY. Effects of pressure and sliding speed on the friction and wear properties of Al-40Zn-3Cu-2Si alloy: a comparative study with SAE 65 bronze. Mater Sci Eng A Struct2008; 496: 517–523.
6.
AlemdağYSavaşkanT. Effects of silicon content on the mechanical properties and lubricated wear behaviour of Al-40Zn-3Cu-(0-5)Si alloys. Tribol Lett2008; 29: 221–227.
7.
SavaşkanTBicanOAlemdağY. Developing aluminium-zinc-based a new alloy for tribological applications. J Mater Sci2009; 44: 1969–1976.
8.
SavaşkanTBicanO. Dry friction and wear properties of Al-25Zn-3Cu-(0-5)Si alloys in the as-cast and heat-treated conditions. Tribol Lett2010; 40: 327–336.
9.
HeywoodJB. Internal combustion engine fundamentals, New York: McGraw Hill Book Company, 1988.
10.
DieterGE. Mechanical metallurgy, New York: McGraw Hill Book Company, 1976.
11.
HallingJ. Principles of tribology, London: Macmillan Education Ltd, 1989.
12.
PrasadBK. Influence of heat treatment on the physical, mechanical and tribological properties of a zinc-based alloy. Z Metallkd1996; 87: 226–232.
13.
PrasadBKPatwardhanAKYagneswaranAH. Influence of aluminum content on the physical, mechanical and sliding wear properties of zinc-based alloys. Z Metallkd1997; 88: 333–338.
14.
ModiOPYadavRPPrasadBK. Effects of swaging and aluminum content on the microstructure and mechanical and sliding wear properties of zinc-based alloys. Mater Trans JIM1998; 39: 582–586.
15.
SavaşkanTBicanO. Effects of silicon content on the microstructural features and mechanical and sliding wear properties of Zn-40Al-2Cu-(0-5)Si alloys. Mater Sci Eng A Struct2005; 404: 259–269.
16.
PrasadBK. Effects of silicon addition and test parameters on sliding wear characteristics of zinc-based alloy containing 37.5% aluminium. Mater Trans JIM1997; 38: 701–706.
17.
LinJFYungYCTsaoCY. Tribological performance of 6061 aluminum alloy/graphite materials under oil-lubricated and dry sliding conditions. Tribol Trans1998; 41: 251–261.
18.
SharmaSCSatishBMGirishBM. Dry sliding wear of short glass fibre reinforced zinc-aluminium composites. Tribol Int1998; 31: 183–188.
19.
WangQChengHSCaracostasCA. Wear of aluminum-alloy matrix composites in lubricated conformal contact with case hardened steel. Tribol Trans1994; 37: 735–742.
20.
GeeAWJVaessenGHGBegelingerA. The influence of composition and structure on the sliding wear of copper-tin-lead alloys. Tribol Trans1969; 12: 44–54.