The densification of ZrC ceramics doped with different contents of TiC prepared by spark plasma sintering at the temperatures between 1750 and 1850°C has been investigated. The microstructure and mechanical properties of the ceramics have been characterised. It was shown that TiC additions effectively promoted the densification process by forming (Zr,Ti)C solid solution. The relative densities and mechanical properties of ZrC samples increased with the increasing of TiC content or the sintering temperature. Ceramic with the content of TiC up to 10 vol.-% sintering at 1850°C showed an excellent combination of properties including a relative density of 98.7%, hardness of 20.8 GPa and flexural strength of 605 MPa.
ScitiD., GuicciardiS. and NygrenM.: ‘Spark plasma sintering and mechanical behaviour of ZrC-based composites’, Scr. Mater., 2008, 59, 638–641. doi: 10.1016/j.scriptamat.2008.05.026
2.
ZouH., WaliN., YangJ. M. and NarottamP. B.: ‘Microstructural development of a Cf/ZrC composite manufactured by reactive melt infiltration’, J. Eur. Ceram. Soc., 2010, 30, 1527–1535. doi: 10.1016/j.jeurceramsoc.2009.10.016
3.
OgawaT. and IkawaK.: ‘Diffusion of metal fission products in ZrC1.0’, J. Nucl. Mater., 1982, 105, 331–334. doi: 10.1016/0022-3115(82)90391-9
4.
BarnierP., BrodhagC. and ThevenotF.: ‘Hot-pressing kinetics of zirconium carbide’, J. Mater. Sci., 1986, 21, 2547–2552. doi: 10.1007/BF01114305
5.
VasudevamurthyG., KnightT. W., RobertsE. and AdamsT. M.: ‘Laboratory production of zirconium carbide compacts for use in inert matrix fuels’, J. Nucl. Mater., 2008, 374, 241–247. doi: 10.1016/j.jnucmat.2007.08.016
6.
RyuH. J., LeeY. W., ChaS. I. and HongS. H.: ‘Sintering behavior and microstructures of carbides and nitrides for the inert matrix fuel by spark plasma sintering’, J. Nucl. Mater., 2006, 352, 341–348. doi: 10.1016/j.jnucmat.2006.02.089
7.
TaoX. Y., WeiX. Y., ChenQ., LuW. Z., MaM. and ZhaoT.: ‘Synthesis, characterisation and thermal behaviour of new preceramic polymers for zirconium carbide’, Adv. Appl. Ceram., 2013, 112, 301–305. doi: 10.1179/1743676113Y.0000000076
8.
BulychevV. P., AndrievskiiR. A. and NezhevenkoL. B.: ‘The sintering of zirconium carbide’, Powder Metall. Met. Ceram., 1977, 16, 273–276. doi: 10.1007/BF00806128
9.
BarnierP., BrodhagC. and ThevenotF.: ‘Hot-pressing kinetics of zirconium carbide’, J. Mater. Sci., 1986, 21, 2547–2552. doi: 10.1007/BF01114305
10.
SamsonovG. V., Koval'chenkoM. S., PetrykinaR. Y. and NaumenkoV. Y.: ‘Hot pressing of the transition metals and their carbides in their homogeneity regions’, Powder Metall. Met. Ceram., 1970, 9, 713–716. doi: 10.1007/BF00836960
11.
TsuchidaT. and YamamotoS.: ‘MA-SHS and SPS of ZrB2–ZrC composites’, Solid State Ionics, 2004, 172, 215. doi: 10.1016/j.ssi.2004.05.020
12.
KimK. H. and ShimK. B.: ‘The effect of lanthanum on the fabrication of ZrB2–ZrC composites by spark plasma sintering’, Mater. Charact., 2003, 50, 31–37. doi: 10.1016/S1044-5803(03)00055-X
13.
LandwehrS. E., HilmasG. E., FahrenholtzW. G. and TalmyI. G.: ‘Processing of ZrC–Mo cermets for high-temperature applications, part I: chemical interactions in the ZrC–Mo system’, J. Am. Ceram. Soc., 2007, 90, 1998–2002. doi: 10.1111/j.1551-2916.2007.01667.x
14.
TangY., ZhangG. J., XueJ. X., WangX. G., XuC. M. and HuangX.: ‘Densification and mechanical properties of hot-pressed ZrN ceramics doped with Zr or Ti’, J. Eur. Ceram. Soc., 2013, 33, 1363–1371. doi: 10.1016/j.jeurceramsoc.2012.12.013
15.
WangX. G., GuoW. M., KanY. M., ZhangG. J. and WangP. L.: ‘Densification behavior and properties of hot-pressed ZrC ceramics with Zr and graphite additives’, J. Eur. Ceram. Soc., 2011, 31, 1103–1111. doi: 10.1016/j.jeurceramsoc.2011.01.005
16.
GusevA. I.: ‘Calculation of phase diagrams of pseudobinary systems based on high-melting carbides of titanium, zirconium, hafnium, and vanadium’, Inorg. Mater., 1984, 20, 976–981.
17.
ShenZ. J., JohnssonM., ZhaoZ. and NygrenM.: ‘Spark plasma sintering of alumina’, J. Am. Ceram. Soc., 2002, 85, 1921–1927. doi: 10.1111/j.1151-2916.2002.tb00381.x
18.
TokitaM.: ‘Trends in advanced SPS spark plasma sintering systems and technology’, J. Soc. Powder Technol., 1993, 30, 790–804. doi: 10.4164/sptj.30.11_790
19.
GaoL., HongJ. S., MiyamotoH. and TorreS. D. D. L.: ‘Superfast densification of oxide ceramics by spark plasma sintering’, J. Inorg. Mater., 1998, 13, 18–22.
20.
PereraD. S., TokitaM. and MoriccaS.: ‘Comparative study of fabrication of Si3N4/SiC composites by spark plasma sintering and hot isostatic pressing’, J. Eur. Ceram. Soc., 1998, 18, 401–404. doi: 10.1016/S0955-2219(97)00139-8
21.
WangX. G., LiuJ. X., KanY. M. and ZhangG. J.: ‘Effect of solid solution formation on densification of hot-pressed ZrC ceramics with MC (M = V, Nb, and Ta) additions’, J. Eur. Ceram. Soc., 2012, 32, 1795–1802. doi: 10.1016/j.jeurceramsoc.2011.10.045
22.
GendreM., MaîtreA. and TrolliardG.: ‘Synthesis of zirconium oxycarbide (ZrCxOy) powders: Influence of stoichiometry on densification kinetics during spark plasma sintering and on mechanical properties’, J. Eur. Ceram. Soc., 2011, 31, 2377–2385. doi: 10.1016/j.jeurceramsoc.2011.05.037