This paper summarises and reviews the industrial manufacturing experience of ceramic components with custom designed complex shapes using low pressure injection moulding technology during a number of years. This technology is successfully used for manufacturing advanced ceramics with different compositions and for different applications. A production level is achieved with hundreds of pieces/day or week or higher. The major principles of this technology are reviewed based on the extensive processing experience. Some processing features, which affect the quality of ceramics and processing yield, are pointed out, particularly for industrial processing. Semi- and automated equipment for low pressure injection moulding technology providing high productivity are described.
EdirisingheMJ, EvansJRG: ‘Review: fabrication of engineering ceramics by injection molding. II. Techniques’, Int. J. High Technol. Ceram., 1986, 2, 249–278.
4.
EdirisingheMJ: ‘Fabrication of engineering ceramics by injection molding’, Am. Ceram. Soc. Bull., 1991, 70, (5), 824–828.
5.
MutsuddyBC, FordRG: ‘Ceramic injection molding’; 1995, London, Chapman and Hall.
KostyukovNS, MedvedovskiEY, KharitonovFY: ‘Electroinsulating corundum-mullite ceramic materials’; 1988, Vladivostok, Far-East Division of Academy of Science USSR.
12.
KnitterR, BauerW, GöhringD, HaußeltJ: ‘Manufacturing of ceramic microcomponents by a rapid prototyping chain’, Adv. Eng. Mater., 2001, 3, (1–2), 49–54.
13.
BauerW, KnitterR: ‘Development of a rapid prototyping process chain for the production of ceramic microcomponents’, J. Mater. Sci., 2002, 37, 3127–3140.
14.
KrindgesI, AndreolaR, PerottoniCA, ZorziJE: ‘Low-pressure injection molding of ceramic springs’, Int. J. Appl. Ceram. Technol., 2008, 5, (3), 243–248.
15.
NovakS, VidovicK, SajkoM, KosmacT: ‘Surface modification of alumina powder for LPIM’, J. Eur. Ceram. Soc., 1997, 17, 217–223.
16.
LinST, GermanRM: ‘Interaction between binder and powder in injection moulding of alumina’, J. Mater. Sci., 1994, 29, 5207–5212.
17.
GermanRM: ‘Homogeneity effects on feedstock viscosity in powder injection moulding’, J. Am. Ceram. Soc., 1994, 77, (1), 283–285.
18.
EdirisingheMJ: ‘The effect of processing additives on the properties of a ceramic-polymer formulation’, Ceram. Int., 1991, 17, 89–96.
19.
ChanT.-Y, LinS.-T: ‘Effects of stearic acid on the injection molding of alumina’, J. Am. Ceram. Soc., 1995, 78, (10), 2746–2752.
20.
LiuD.-M, TsengWJ: ‘Influence of powder agglomerates on the structure and rheological behavior of injection-molded zirconia-wax suspensions’, J. Am. Ceram. Soc., 1999, 82, (10), 2647–2652.
21.
LiuD.-M: ‘Effect of dispersants on the rheological behavior of zirconia-wax suspensions’, J. Am. Ceram. Soc., 1999, 82, (5), 1162–1168.
22.
ZorziJE, PerottoniCA, Da JornadaJAH: ‘Wax-based binder for low-pressure injection molding and the robust production of ceramic parts’, Ind. Ceram., 2003, 23, (1), 47–49.
23.
LenkR, KrivoshchepovAPh: ‘Effect of surface-active substances on the rheological properties of silicon carbide suspensions in paraffin’, J. Am. Ceram. Soc., 2000, 83, (2), 273–276.
24.
LiuZY, LohNH, TorSB, KhorKA, MurakoshiY, MaedalR: ‘Binder system for micropowder injection molding’, Mater. Lett., 2001, 48, 31–38.
25.
WegmannM, ClemensF, HendryA, GrauleT: ‘Dispersion of lanthanoid-coated barium titanate in a paraffin-based extrusion binder system’, Ceram. Int., 2006, 32, (2), 147–156.
26.
EdirisingheMJ, EvansJRG: ‘Systematic development of the ceramic injection moulding process’, Mater. Sci. Eng. A, 1989, A109, 17–26.
DakskoblerA, KosmacT: ‘The effect of interparticle interactions of the rheological properties of paraffin-wax suspensions’, in ‘Advanced processing and manufacturing technologies for structural and multifunctional materials III’, (ed. , OhjiT, SinghM), Vol. 30, 8, 213–220; 2009, Ceramics Engineering and Science Proceedings.
32.
KitanoT, KataokoT, ShirotaT: ‘An empirical equation of the relative viscosity of polymer melts filled with various inorganic fillers’, Rheol. Acta, 1981, 20, 207–209.
33.
MetznerAB: ‘Rheology of suspensions in polymer liquids’, J. Rheol., 1985, 29, 739–775.
34.
IsmaelMR, ClemensF, GrauleT, HoffmannMJ: ‘Effect of different thermoplastic binders on the processability of feedstocks for ceramic co-extrusion process’, Ceram. Int., 2011, 37, (8), 3173–3182.
35.
WrightJK, EvansJRG: ‘Removal of organic vehicle from moulded ceramic bodies by capillary action’, Ceram. Int., 1991, 17, 79–87.
36.
ZorziJE, PerottoniCA, Da JornadaJAH: ‘Hard-skin development during binder removal from Al2O3-based green ceramic bodies’, J. Mater. Sci., 2002, 37, (9), 1801–1807.
37.
LiuD.-M, TsengWJ: ‘Influence of debinding rate, solid loading and binder formulation on the green microstructure and sintering behaviour of ceramic injection mouldings’, Ceram. Int., 1998, 24, 471–481.
38.
TsengWJ, HsuC-K: ‘Cracking defect and porosity evolution during thermal debinding in ceramic injection moldings’, Ceram. Int., 1999, 25, 461–466.
39.
TsengWJ, LiuDM, HsuC-K: ‘Influence of stearic acid on suspension structure and green microstructure of injection-molded zirconia ceramics’, Ceram. Int., 1999, 25, (2), 191–195.
40.
SongJH, EvansJRG: ‘Flocculation after injection molding in ceramic suspensions’, J. Mater. Res., 1994, 9, (9), 22–26.