The effect of anodic inhibitors [calcium nitrate Ca(NO3)2, calcium nitrite Ca(NO2)2 and potassium nitrate NaNO2] has been evaluated using cylinders with steel rebars exposed to the following environments: in the marine tidal zone, at roof top and in air of 38°C and 90% relative humidity for 4 years. The experiments showed that the half cell potentials were more negative than the visual inspections proved when anodic inhibitors are used. Inhibitor dosage on 3–4% of cement weight seems sufficient to protect the rebar against corrosion. Capillary absorption experiments showed that the concrete porosity was unaffected by the inhibitors. The concentration profiles of chloride, nitrite and nitrate were investigated with respect to leaching. However, it was difficult to find the background level of nitrite due to possible chemical alteration.
FlugeF: ‘Environmental loads on coastal bridges’, Proc. Int. Conf. on ‘Repair of concrete structures’, Svolvær, Norway, May 1997, Norwegian Road Research Laboratory, 89–98.
JustnesH, NygaardEC: ‘The influence of technical calcium nitrate additions on the chloride binding capacity of cement and the rate of chloride induced corrosion of steel embedded in mortars’, Proc. Int. Confon. ‘Corrosion and corrosion protection of steel in concrete’, Sheffield, UK, July 1994, University of Sheffield, Vol. I, 491–502.
7.
AlonsoC, AndradeC: ‘Estudio de la effiacacia del Nit-Cal como inhibidor de la corrosión de armaduras del hormigón’, Report no. 16·878, Instituto de ciencias de la construccion Eduardo Torroja, Madrid, Spain1999.
8.
D'yachenkoYuK, EnisherlovaSG, KucheryaevaGS, RatinovVB, SemenovaSD: ‘Influence of chloride, nitrate and nitrite on the corrosion of pre-stressed reinforcing in heavy concrete’, Zashchita Metallov, 1987, 23, (4), 655–659.
9.
GoetzCW: ‘Accelerated corrosion forcing testing on reinforced concrete using Pozzolith 555 accelerator admixture’, Report WE no. 85134, Webster's Engineering Assoc. Inc., Wooster, OH, USA, 1987.
HolmJ: ‘Comparison of the corrosion potential of calcium chloride and a calcium nitrate based non-chloride accelerator – a Macro-Cell corrosion approach’, in ‘Corrosion, concrete and chlorides. Steel corrosion in concrete: causes and restraints’, (ed. F. W. Gibson), 35; 1987, Detroit, MI, American Concrete Institute.
12.
VogelsangJ: ‘Investigations on corrosion inhibitors and chelating agents in alkaline solution using cyclovoltametry’, Proc. 8th Eur. Symp. on ‘Corrosion inhibitors’, Ferrara, Italy, September 1995, Ann. Univ. Ferrara, Sez. V, Suppl. no. 10, 589–597.
13.
JustnesH: ‘Corrosion inhibitors for reinforced concrete’, Proc. 7th CANMET/ACI Int. Conf. on ‘Durability of concrete’, Montreal, PQ, Canada, May–June 2006, CANMET/ACI, 53–70.
14.
Al-AmoudiOSB, MaslehuddinM, LashariAN, AlmusallamAA: ‘Effectiveness of corrosion inhibitors in contaminated concrete’, Cem. Concr. Compos., 2003, 25, (4–5), 439–450.
15.
Al-MethelM, Al-DulaijanS, Al-IdiSH, ShameemM, AliMR, MaslehuddinM: ‘Performance of generic and proprietary corrosion inhibitors in chloride-contaminated silica fume cement concrete’, Constr. Build. Mater., 2009, 23, 1768–1774.
16.
AlonsoC, AndradeC: ‘Effect of nitrite as a corrosion inhibitor in contaminated and chloride-free carbonated mortars’, ACI Mater. J., 1990, 87, (2), 130–137.
17.
AndradeC, AlonsoC, GonzálezJA: ‘Some laboratory experiments on the inhibitor effect of sodium nitrite on reinforcement corrosion’, Cem. Concr. Aggreg.CCAGPD,, 1986, 8, (2), 110–116.
18.
El-JazairiB, BerkeN: ‘Use of calcium nitrite as a corrosion inhibiting admixture to steel reinforcement in concrete’, in ‘Corrosion of reinforcement in concrete’. (ed. , PageC L, ed), 571–585; 1990, London, Elsevier Science Publishers.
19.
Sagoe-CrentsilKK, YilmazVT, GlasserFP: ‘Properties of inorganic corrosion inhibition admixtures in steel-containing OPC mortars. Part 1: chemical properties’, Adv. Cem. Res., 1991/1992, 4, (15), 91–96.
20.
YilmazVT, Sagoe-CrentsilKK, GlasserFP: ‘Properties of inorganic corrosion inhibition admixtures in steel-containing OPC mortars. Part 2: electrochemical properties’, Adv. Cem. Res., 1991/1992, 4, (15), 97–102.
21.
Sagoe-CrentsilKK, GlasserFP: ‘“Green rust”, iron solubility and the role of chloride in the corrosion of steel at high pH’, Cem. Concr. Res., 1993, 23, 785–791.
22.
RosenbergAM, GaidisJM: ‘The mechanism of nitrite inhibition of chloride attack of reinforced steel in alkaline aqueous environments’, Mater. Perform., 1979, 18, (11), 45–48.
23.
BrownMC, WeyersRE, SprinkelMM: ‘Solution tests of corrosion-inhibiting admixtures for reinforced concrete’, ACI Mater. J., 2002, 99, (4), 371–378.
24.
JustnesH, NygaardEC, GrøstadT: ‘Calcium nitrate as a retarder of chloride initiated rebar corrosion’, Proc. Int. Conf. on‘Infrastructure regeneration and rehabilitation – improving the quality of life through better construction – a vision for the next millennium’, (ed. , SwamyR N, ed), 189–198; 1999, Sheffield, Sheffield Academic Press.
25.
BertoliniL, ElsnerB, PedeferriP, PolderR: ‘Corrosion of steel in concrete’; 2004, Weinheim, Wiley-VCH Verlag GmbH & Co. KGaA.