TiC-Ti3AlC2 composites with a novel intragranular structure were fabricated by self-propagating high temperature synthesis technique using Ti, Al and C elemental powders. X-ray diffraction results indicated that the as synthesised composites were composed of TiC and Ti3AlC2, where the amounts of TiC were measured to be 5·4, 9·2 and 16·7 wt-%. Transmission electron microscopy observation showed that the globular TiC was located within the plate-like Ti3AlC2 grain, which confirms the ubiquitous existence of intragranular structure in the composites.
TzenovN. V. and BarsoumM. W.: ‘Synthesis and characterization of Ti3AlC2’, J. Am. Ceram. Soc., 2000, 83, (4), 825–832.
2.
WangX. H. and ZhouY. C.: ‘Microstructure and properties of Ti3AlC2 prepared by the solid—liquid reaction synthesis and simultaneous in-situ hot pressing process’, Acta Mater., 2002, 50, (12), 3141–3149.
3.
BarsoumM. W., TzenovN., ProcopioA., El-RaghyT. and AliM.: ‘Oxidation of Tin+1AlCn, (n=1-3 and X=C, N)-II. Experimental results’, J. Electrochem. Soc., 2001, 148, (8), 551–562.
4.
ZhangJ. and ZhouY. C.: ‘Microstructure, mechanical, and electrical properties of Cu—Ti3AlC2 and in situ Cu—TiCx compo-sites’, J. Mater. Res., 2008, 23, (4), 924–932.
5.
GaoL. Q., ZhouY., ThaiH. X., LiS. B., ZhangZ. L. and LiC. W.: ‘Fabrication and properties of Ti3A1C2/Cu composites’, Rare Metal Mater. Eng., 2007, 36, (51), 682–684.
6.
ChenJ. X. and ZhouY. C.: ‘Strengthening of Ti3AlC2 by incorporation of Al2O3’, Scr. Mater., 2004, 50, (6), 897–901.
7.
WuL., ChenJ. X., LiuM. Y., WangY. W. and ZhouY. C.: ‘Reciprocating friction and wear behavior of Ti3AlC2 and Ti3AlC2/ Al2O3 composites against AIS152100 bearing steel’, Wear, 2009, 266, (1-2), 158–166.
8.
ReimanisI. E.: ‘A review of issues in the fracture of interfacial ceramics and ceramic composites’, Mater. Sci. Eng. A, 1997, A237, (2), 159–167.
9.
SunX. D., LiJ. G., GuoS. W. and XiuZ. M.: Intragranular particle residual stress strengthening of Al2O3—SiC nanocompo-sites,’ J. Am. Ceram. Soc., 2005, 88, (6), 1536–1543.
10.
LiX. C., StampflJ. and PrinzF. B.: ‘Mechanical and thermal expansion behavior of laser deposited metal matrix composites of invar and TiC’, Mater. Sci. Eng. A, 2000, A282, (1–2), 86–90.
11.
ZhuC. C., ZhangX. H. and HeX. D.: ‘Self-propagating high-temperature synthesis of TiC—TiB2/Cu ceramic—matrix composite’, J. Inorg. Mater., 2003, 18, (4), 872–878.
12.
WangC. A., ZhouA. G., QiL. and HuangY.: ‘Quantitative phase analysis in the Ti—Al—C ternary system by X-ray diffraction’, Powder Diffr., 2005, 20, (3), 218–222.
13.
LuW. J., ZhangD., ZhangX. N., BianY. J., WuR. J., SakataT. and MoriH.: ‘Microstructure and tensile properties of in situ synthesized (TiBw+;TiCp)/Ti6242 composites’, J. Mater. Sci., 2001, 36, (15), 3707–3714.