The authors developed a new technique combining ceramic injection moulding and liquid precursor infiltration, presenting a new strategy for fabrication of coloured zirconia ceramics. The authors’ strategy includes ceramic injection moulding 3Y‐TZP powder using a water debinding binder system, debinding moulded parts in water and drying, immersing debound parts in solutions containing different colouring ions and then sintering and creating coloured zirconia ceramics. The fabricated coloured ceramic bars exhibit a core shell structure, and the thickness of the coloured shell can be tailored by adjusting immersion time and temperature. Using solutions containing different colouring ions, ceramic bars with various colours can be prepared.
SongJH, EvansJRG: ‘The injection‐molding of fine and ultra‐fine zirconia powders’, Ceram. Int., 1995, 21, (5), 325–333.
3.
SongJH, EdirisingheMJ, EvansJRG, TwizellEH: ‘Modeling the effect of gas transport on the formation of defects during thermolysis of powder moldings’, J. Mater. Res., 1996, 11, (4), 830–840.
4.
HuzzardRJ, BlackburnS: ‘Influence of solids loading on aqueous injection moulding paste’, Br. Ceram. Trans., 1999, 98, (2), 49–56.
5.
SoykanHS, KarakasY: ‘Injection moulding of thin walled zirconia tubes for oxygen sensors’, Adv. Appl. Ceram., 2005, 104, (6), 285–290.
6.
ShawHM, EdirisingheMJ: ‘Porosity development during removal of organic vehicle from ceramic injection moldings’, J. Eur. Ceram. Soc., 1994, 13, (2), 135–142.
7.
ShawHM, EdirisingheMJ: ‘Shrinkage and particle packing during removal of organic vehicle from ceramic injection moldings’, J. Eur. Ceram. Soc., 1995, 15, (2), 109–116.
8.
BakanHI: ‘Injection moulding of alumina with partially water soluble binder system and solvent debinding kinetics’, Mater. Sci. Technol., 2007, 23, (7), 787–791.
KraussVA, OliveiraAAM, KleinAN, Al‐QureshiHA, FredelMC: ‘A model for PEG removal from alumina injection moulded parts by solvent debinding’, J. Mater. Process. Technol., 2007, 182, (1–3), 268–273.
11.
HuSC, HwangKS: ‘Length change and deformation of powder injection‐molded compacts during solvent debinding’, Metall. Mater. Trans. A, 2000, 31A, (5), 1473–1478
12.
LiuDM, TsengWJ: ‘Influence of debinding rate, solid loading and binder formulation on the green microstructure and sintering behaviour of ceramic injection mouldings’, Ceram. Int., 1998, 24, (6), 471–481
13.
ShivashankarTS, GermanRM: ‘Effective length scale for predicting solvent‐debinding times of components produced by powder injection molding’, J. Am. Ceram. Soc., 1999, 82, (5), 1146–1152
14.
SongJH, EvansJRG, EdirisingheMJ, TwizellEH: ‘Effect of powder bed on critical heating rates for thermolysis of ceramic injection moldings’, AIChE J., 1996, 42, (6), 1715–1722
15.
AboushelibMN, KleverlaanCJ, FeilzerAJ: ‘Effect of zirconia type on its bond strength with different veneer ceramics’, J. Prosthodont., 2008, 17, (5), 401–408
SchabbachLM, BondioliF, FerrariAM, ManfrediniT, PetterCO, FredelMC: ‘Color in ceramic glazes: analysis of pigment and opacifier grain size distribution effect by spectrophotometer’, J. Eur. Ceram. Soc., 2008, 28, (9), 1777–1781
18.
ChiouYH, LinST: ‘Influence of CoO and Al2O3 on the phase partitioning of ZrO2‐3 mol% Y2O3’, Ceram. Int., 1996, 22, (3), 249–256.
19.
FujisakiH: ‘Zirconia‐containing powder for black zirconia sintered body, e.g. for ornamental articles such as watch bands, contains specified amount of cobalt–zinc–iron–aluminum or aluminum oxide containing pigment, aluminum oxide, and yttrium oxide’, European patent no. EP1857428A1, 21 November 2007.
20.
MarpleBR, GreenDJ: ‘Mullite alumina particulate composites by infiltration processing’, J. Am. Ceram. Soc., 1989, 72, (11), 2043–2048
21.
AlbanoMP, ScianAN: ‘Mullite/SiAlON/alumina composites by infiltration processing’, J. Am. Ceram. Soc., 1997, 80, (1), 117–124.
22.
GlassSJ, GreenDJ: ‘Permeability and infiltration of partially sintered ceramics’, J. Am. Ceram. Soc., 1999, 82, (10), 2745–2752.
23.
MarpleBR, GreenDJ: ‘Graded compositions and microstructures by infiltration processing’, J. Mater. Sci., 1993, 28, (17), 4637–4643.
24.
WashburnEW: ‘The dynamics of capillary flow’, 1921,, 374–375College Park, MD, American Physical Society.
25.
EinsetEO: ‘Capillary infiltration rates into porous media with applications to Silcomp processing’, J. Am. Ceram. Soc., 1996, 79, (2), 333–338
26.
‘Colorimetry’; 1986, Vienna, Central Bureau of the Commission Internationale de l'Eclairage.