Corrosion behaviour of nanochromium coatings deposited by direct current magnetron sputtering

Abstract

Chromium films are frequently used as corrosion resistant coatings. Chromium coatings with a columnar structure deposited by magnetron sputtering demonstrate poor corrosion resistance. In this paper, a nanochromium coating with a non-columnar structure was deposited on 316L stainless steel by a direct current magnetron sputtering technique. The grain size of chromium coatings with a pyramidal structure was 95 nm. The corrosion performance of the bare and chromium coated steel in 0·5M H₂SO₄ was examined using electrochemical impedance spectroscopy, polarisation and open circuit potential measurements. The results showed that the corrosion rate of nanochromium coatings was lower than that of uncoated steel by more than one order of magnitude. Electrochemical impedance spectra of the nanochromium coatings exhibited distinct characteristics in corrosive solution. No obvious degradation was observed for the coatings after 768 h exposure to the corrosive solution.

Keywords

Nanochromium coating Corrosion behaviour Direct current magnetron sputtering Electrochemical impedance spectra

Get full access to this article

View all access options for this article.

References

Lozano-Morales

, Renz

R. P.

, Fortman

J. J.

and Taylor

E. J.

: ‘Electrically mediated process for functinal and decorative trivalent chromium electroplating: an alternative to hexavalent chromium’, ECS Trans., 2007, 6, 51–61. doi: 10.1149/1.2790401

Zeng

Z. X.

and Zhang

J. Y.

: ‘Electrodeposition and tribological behavior of amorphous chromium-alumina composite coatings’, Surf. Coat. Technol., 2008, 202, 2725–2730. doi: 10.1016/j.surfcoat.2007.10.008

Rosestolato

, Battaglin

and Ferro

: ‘Electrochemical properties of stoichiometric RuN film prepared by rf-magnetron sputtering: s preliminary study’, Electrochem. Commun., 2014, 49, 9–13. doi: 10.1016/j.elecom.2014.09.019

Nygren

, Samuelsson

, Flink

, Ljungcrantz

and Rudolphi

A. K.

: ‘Growth and characterization of chromium carbide films deposited by high rate reactive magnetron sputtering for electrical contact applications’, Surf. Coat. Technol., 2014, 260, 326–334. doi: 10.1016/j.surfcoat.2014.06.069

Ruden

, Restrepo-Parra

, Paladines

A. U.

and Sequeda

: ‘Corrosion resistance of CrN thin films produced by dc magnetron sputtering’, Appl. Surf. Sci., 2013, 270, 150–156. doi: 10.1016/j.apsusc.2012.12.148

Xie

T. T.

, Mao

S. D.

, Yu

, Wang

and Song

Z. L

: ‘Structure, corrosion, and hardness properties of Ti/Al multilayers coated on NdFeB by magnetron sputtering’, Vacuum, 2012, 86, 1583–1588. doi: 10.1016/j.vacuum.2012.03.019

Tsan Kenneth Chiang

and Wei

R. H.

: ‘Growth morphology and corrosion resistance of magnetron sputtered Cr films’, Surf. Coat. Technol., 2011, 206, 1660–1665. doi: 10.1016/j.surfcoat.2011.09.020

Shi

, Long

, Yang

and Pan

: ‘Structural and tribological properties of CrTiAlN coatings on Mg alloy by closed-field unbalanced magnetron sputtering ion plating’, Appl. Surf. Sci., 2008, 254, 7342–7350. doi: 10.1016/j.apsusc.2008.05.338

Pan

, Liu

, Li

, Wang

and Wang

F. H.

: ‘Passive film growth mechanism of nanocrystalline 304 stainless steel prepared by magnetron sputtering and deep rolling techniques’, Electrochim. Acta, 2011, 56, 7740–7748. doi: 10.1016/j.electacta.2011.05.106

10.

and Wang

F. H.

: ‘Effects of surface nanocrystallization on the electrochemical corrosion behavior of metals’, Corros. Prot., 2003, 24, 6–12.

11.

Djouadi

M. A.

, Nouveau

, Banakh

, Sanjines

, Levy

and Nouet

: ‘Stress profiles and thermal stability of Cr_xN_y films deposited by magnetron sputtering’, Surf. Coat. Technol., 2002, 151-152, 510–514. doi: 10.1016/S0257-8972(01)01635-8

12.

Lan

, Wang

and Cao

Z. Q.

: ‘Studies on the corrosion elecrochemical behavior of nanocrystalline Cr in acidic media’, J. Liaoning Techn. Univ., 2012, 31, 387–391.

13.

Manea

A. C.

, Buda

and Visan

: ‘Electrochemical impedance spectroscopy investigations of tantalum and its passive films in some acidic solutions’, U.P.B. Sci. Bull. B, 72B, 2010, 65–78.

14.

Radjabov

T. D.

, Kamardin

A. I.

and Sharudo

A. V.

: ‘The investigation of two-layer protective-decorative coatings on oxide substrates’, Vacuum, 2004, 75, 143–147. doi: 10.1016/j.vacuum.2004.01.078

15.

Schneider

, Schroth

, Schilm

and Michaelis

: ‘Micro-EIS of anodic thin oxide films on titanium for capacitor applications’, Electrochim. Acta, 2009, 54, 2663–2671. doi: 10.1016/j.electacta.2008.11.003

16.

T. S.

, Liu

, Zhang

, Li

, Yan

F. K.

, Tao

N. R.

and Wang

F. H.

: ‘Passive behavior of a bulk nanostructured 316L austenitic stainless steel consisting of nanometer-sized grains with embedded nano-twin bundles’, Corros. Sci., 2014, 85, 331–342. doi: 10.1016/j.corsci.2014.04.039