In this study, molybdenum plates (99·5% purity) were subjected to electrochemical boriding in a molten borax electrolyte in order to synthesise molybdenum boride phases on exposed surfaces. Electrochemical boriding was carried out at temperatures of 900, 950 and 1000°C for a duration of 30–180 min at a current density of 0·5 A cm−2. Cross-sectional microscopic examination of the plates indicated formation of 20 to 50 μm thick boride layers, depending on process temperature and duration. These layers consisted of two distinct boride phases: Mo2B4·027 and Mo2B5. The boride layer cross-sectional hardness was in the range of 1900–3250 HV with 50 g load. The adhesion of the boride coating to the molybdenum substrate was determined by a Rockwell C indentation adhesion test machine. The boride layers produced due to the electrochemical boriding technique were thick, hard, dense, and homogeneous.
KudakaK, IizumiK, SasakiT and OkadaS: ‘Mechanochemical synthesis of MoB2 and Mo2B5’, J. Alloys Compd, 2001, 315, 104–107.
2.
LiY, FanY and ChenY: ‘A novel route to nanosized molybdenum boride and carbide and/or metallic molybdenum by thermo-synthesis method from MoO3, KBH4, and CCl4’, J. Solid State Chem., 2003, 170,135–141.
3.
YangG, Z-kunH, XiaoleiX and GangX: ‘Formation of molybdenum boride cermet coating by the detonation spray process’, J. Thermal Spray Technol., 2001, 10, (3), 456–460.
4.
XuX, FuK, YuM, LuZ, ZhangX, LiuG and TangC: ‘The thermodynamic, electronic and elastic properties of the early-transition-metal diborides with AlB2-type structure: a density functional theory study’, J. Alloys Compd, 2014, 607, 198–206.
5.
QiC, JiangY, LiuY and ZhouR: ‘Elastic and electronic properties of XB2 (X = V, Nb, Ta, Cr, Mo, and W) with AlB2 structure from first principle calculations’, Ceram Int., 2014, 40, 5843–5851.
6.
YuLG, KhorKA and SundararajanG: ‘Boride layer growth kinetics during boriding of molybdenum by the Spark Plasma Sintering (SPS) technology’, Surf. Coat. Technol., 2006, 201, 2849–2853.
7.
SteinitzR, BinderI and MoskowitzD: ‘System molybdenum-boron and some properties of the molybdenum-borides’, Trans. Am. Inst. Min. Metall. Pet. Eng., 1952, 194, 983–987.
8.
YasudaT, BannoA, ItoT, KiyoshiK, IshibayashiK, Chubu Sukegawa Enterprise Co., Ltdand Kabushiki KaishaSD: ‘Durability against corrosion by a molten light alloy’, US Patent 6238807 B1, published 29 May 2001.
9.
KudoT and ObayashiH, Hitachi, Ltd.: ‘Electrode catalyst’, US Patent 4242421, published 30 December 1980.
10.
SheinIR and IvanovskiiAL: ‘The influence of lattice vacancies on the structural, electronic and cohesive properties of niobium and molybdenum borides by first-principles’, Phys. Rev. B, 2006, 73, 14, 144108/1-9.
11.
KugaiLN: ‘Chemical stability of molybdenum and tungsten borides’, Poroshk. Metall., 1971, 12, 108, 54–57.
12.
KuznetsovSA, RebrovEV, MiesMJM, de CroonMHJM and SchoutenJC: ‘Synthesis of protective Mo–Si–B coatings in molten salts and their oxidation behavior in an air–water mixture’, Surf. Coat. Technol., 2006, 201, 3, 971–978.
13.
KuznetsovSA, KuznetsovaSV, RebrovEV, MiesMJM, de CroonMHJM and SchoutenJC: ‘Synthesis of molybdenum borides and molybdenum silicides in molten salts and their oxidation behavior in an air-water mixture’, Surf. Coat. Technol., 2005, 195, 182–188.
14.
AlfintsevaRA, BodrovaLG and VerkhoturovAD: ‘The application of refractory metal borides as electrodes in electrospark machining’, J. Less-Common Met., 1979, 67, 443–448.
15.
ZhangGJ, YueXM and WatanabeT: ‘Al2O3/TiC/(MoSi2 + Mo2B5) multilayer composites prepared by tape casting’, J. Eur. Ceram. Soc., 1999, 19, 2111–2116.
16.
SilvaAC and KaufmannMJ: ‘Synthesis of MoSi2-boride composites through in-situ displacement reactions’, Intermetallics, 1997, 5, 1–15.
17.
VinesL, CainJ, LeeC.-O, KoenigsederS and FujishiroF, Vlsi Technology, Inc.: ‘Molybdenum boride barrier layers between aluminum and silicon at contact points in semiconductor devices’, US Patent 5329161, published 12 July 1994.
18.
TianX, GuoX, SunZ, YinZ and WangL: ‘Formation of B-modified MoSi2 coating on pure Mo prepared through HAPC process’, Int. J. Refract. Met. H., 2014, 45, 8–14.
19.
TaleghaniPR, BakshiSR, BorhaniGH and ErfanmaneshM: ‘Phase and microstructural characterization of Mo-Si-B multiphase intermetallic alloys produced by pressureless sintering’, J. Alloys Compd, 2014, 582, 734–741.
20.
WangY, WangD and YanJ: ‘Preparation and characterization of MoSi2/MoB composite coating Mo substrate’, J. Alloys Compd, 2014, 589, 384–388.
21.
BrandstötterJ and LengauerW: ‘Multiphase reaction diffusion in transition metal-boron systems’, J. Alloys Compd, 1997, 262–263, 390–396.
22.
YehCL and HsuWS: ‘Preparation of molybdenum borides by combustion synthesis involving solid-phase displacement reactions’, J. Alloys Compd, 2008, 457, 191–197.
23.
KlesnarH, AselageTL, MorosinB, KweiGH and LawsonAC: ‘The diboride compounds of molybdenum: MoB2−x and Mo2B5−y’, J. Alloys Compd, 1996, 241, 1–2, 180–186.
24.
CamurluHE: ‘Preparation of single phase molybdenum boride’, J. Alloys Compd, 2011, 509, 17, 5431–5436.
25.
HigashiI, TakahashiY and OkadaS: ‘Crystal structure of MoB2’, J. Less-Common Met, 1986, 123, 277–283.
26.
MorishitaM, KoyamaK and YagiS: ‘Standard entropy of formation of Mo2B5 at 298K’, J. Alloys Compd, 2004, 376, 111–114.
27.
BonomiA, GiessH and GentazC: ‘Electrochemical boriding of molybdenum in molten salts’, Electrodep. Surf. Treat., 1973, 1, (5), 419–427.
28.
MalyshevVV, GabA, ShakhninD, PopescuAM, ConstantinV and OlteanuM: ‘High temperature electrochemical synthesis of molybdenum, tungsten and chromium borides from halide-oxide melts’, Rev. Roum. Chim., 2010, 55, (4), 233–238.
29.
SistaV, KahveciogluO, EryilmazOL, ErdemirA and TimurS: ‘Electrochemical boriding and characterization of AISI D2 tool steel’, Thin Solid Films, 2011, 520, (5), 1582–1588.
30.
KahveciogluO, SistaV, EryilmazOL, ErdemirA and TimurS: ‘Ultra-fast boriding of nickel aluminide’, Thin Solid Films, 2011, 520, (5), 1575–1581.
31.
SistaV, KahveciogluO, KartalG, ZengQZ, KimJH, EryilmazOL and ErdemirA: ‘Evaluation of Electrochemical Boriding of Inconel 600’, Surf. Coat. Tech., 2013, 215, 452–459.
32.
AtarE, KayaliES and CimenogluH: Characteristics and wear performance of borided Ti6Al4V alloy’, Surf. Coat. Technol., 2008, 202, 4583–4590.
33.
KulkaM, PertekA and MakuchN: ‘The importance of carbon concentration-depth profile beneath iron borides for low-cycle fatigue strength, Mater. Sci. Eng. A, 2011, A528, 8641–8650.
34.
KulkaM, MakuchN, PertekA and PiaseckiA: ‘Microstructure and properties of borocarburized and laser-modified 17CrNi6-6 steel’, Opt. Laser Technol., 2012, 44, 872–881.
35.
KeddamM, KulkaM, MakuchN, PertekA and MaldzinskiL: ‘A kinetic model for estimating the boron activation energies in the FeB and Fe2B layers during the gas-boriding of Armco iron: Effect of boride incubation times’, Appl. Surf. Sci., 2014, 298, 155–163.
36.
GunesI, UlkerS and TaktakS: ‘Plasma paste boronizing of AISI 8620, 52100 and 440C steels, Mater. Des., 2011, 32, 2380–2386.
37.
Campos-SilvaI, Bravo-BarcenasD, CimenogluH, Figueroa-LopezU, Flores-JimenezM and MeydanogluO: ‘The boriding process in CoCrMo alloy: fracture toughness in cobalt boride coatings’, Surf. Coat. Technol., 2014, DOI: 10·1016/j.surfcoat.2014·07·092 (accepted manuscript).
38.
IvanovskiiAL, SheinIR and MedvedevaNI: ‘Non-stoichiometric s-, p-, and d-metal diborides: Synthesis, properties and simulation’, Russ. Chem. Rev., 2008, 77, (5), 467–486.
39.
SheinIR, SheinKI and IvanovskiiAL: ‘First-principles study on the structural, cohesive, and electronic properties of rhombohedral Mo2B5 as compared with hexagonal MoB2’, Phys. B, 2007, 387B, 184–189.
40.
RoglP and SchusterJ C (ed.): ‘Phase diagrams of ternary boron nitride and silicon nitride systems, monograph series on alloy phase diagrams’, 64–67; 1992, Materials Park, OH, ASM International.