Abstract

A series of TiO₂ sols with different pH values prepared by the sol-gel method under acid conditions were coated onto the surfaces of ceramic tiles to obtain the corresponding TiO₂ films respectively. The surface gloss and roughness of the as-prepared TiO₂ films were measured by a glossmeter and an atomic force microscope (AFM) respectively. It has been found that the surface gloss of the as-prepared TiO₂ films is decreased but its roughness is increased with the increase of the pH value of TiO₂ sol. Moreover, the measurement result of the as-prepared TiO₂ sols by Zetasizer shows that the ζ potential of TiO₂ sol is increased with the increase of pH value of TiO₂ sol. It is proposed that the increase of ζ potential will cause a stronger repulsion of particles in TiO₂ sol, resulting in a rougher surface and then lower surface gloss of the corresponding TiO₂ film.

Keywords

TIO2 FILM TIO2 SOL CERAMIC TILES PH SURFACE GLOSS ζ POTENTIAL

Get full access to this article

View all access options for this article.

References

Negishi

, Iyoda

, Hashimoto

and Fujishima

: Chem. Lett., 1995, 24, 841–842.

Ohko

and Fujishima

: J. Phys. Chem. B., 1998, 102B, 1724–1729.

Ohko

, Tryk

D. A.

, Hashimoto

and Fujishima

: J. Phys. Chem. B, 1998, 102B, 2699–2704.

Hoffmann

M. R.

, Martin

S. T.

and Choi

: Chem. Rev., 1995, 95, 69–96.

Bount

M. C.

, Kim

D. H.

and Falconer

J. L.

: Environ. Set Technol., 2001, 35, 2988–2994.

J. G.

, Yu

J. C.

, Ho

W. K.

and Jiang

Z. T.

: New J. Chem., 2002, 26, 607–613.

Sakai

, Fujishima

, Watanabe

and Hashimoto

: J. Phys. Chem., 2001, 105, 3023–3026.

Hur

J. S.

and Koh

: Biotechnot Lett., 2002, 24, 23–25.

J. C.

, Ho

, Lin

, Yip

and Wong

P. K.

: Environ. Set Technol., 2003, 37, 2296–2301.

10.

H. Y.

and Anderson

M. A.

: J. Environ. Eng., 1996, 122, 217–221.

11.

Zhu

, Zhang

, Wang

, Fu

and Cao

L. L.

: J. Mater. Chem., 2001, 11, 1864–1868.

12.

Oqawa

, Yoshioka

, Tsubouchi

, Saito

, Hasegawa

, Fujishima

and Hashimoto

: Architectural Material Using Metal Oxide Exhibiting Photocatalytic Activity, US Patent, 1997, 5595813.

13.

Oqawa

, Yoshioka

, Tsubouchi

, Saito

, Hasegawa

, Fujishima

and Hashimoto

: Architectural Material Using Metal Oxide Exhibiting Photocatalytic Activity, US Patent, 1997, 5643436.

14.

G. F.

, Vary

P. S.

and Lin

C. T.

: J. Phys. Chem. B, 2005, 109B, 8889–8898.

15.

Diebold

: Surf Set Rep., 2003, 48, 53–229.

16.

Chrysicopoulou

, Davazoglou

, Trapalis

and Kordas

: Thin Solid Films, 1998, 323, 188–193.

17.

Wang

, Helmersson

and Kali

P. O.

: Thin Solid Films, 2002, 405, 50–54.

18.

, Liu

and Lin

: A Self—cleaning Multi-functional Ceramic, China Patent, 1999, 99204468.

19.

X. Z.

, Liu

, Chen

M. G.

and Wang

X. X.

: A Kind of Outerwall Ceramic Tiles with a Coating of Photocatalytic Nano-films, China Patent, 2002, 02239603.

20.

Sugimoto

, Zhou

and Muramatsu

: J. Colloid Interface Set, 2003, 259, 53–61.

21.

, Tsai

H. L.

and Huang

C. L.

: Mater. Sci. Eng. A, 2003, A344, 209–214.

22.

Koelsch

, Cassaignon

and Jolivet

J. P.

: Mater. Res. Soc. Symp Proc., 2004, 822, 79.

23.

, White

T. J.

and Lim

S. H.

: J. Solid State Chem., 2004, 177, 1372–1381.

24.

Yanagisawa

and Ovenstone

: J. Phys. Chem. B, 1999, 103B, 7781–7787.

25.

Zhang

Q. H.

, Gao

and Guo

J. K

: J. Eur. Ceram. Soc., 2000, 20, 2153–2158.

26.

Isley

S. L.

and Penn

R. L.

: J. Phys. Chem. B, 2006, 110B, 15134–15139.

27.

Gunther and Peukert

: Colloid Surface A: Physicochem. Eng. Aspects, 2003, 225, 49–61.

28.

Snoswell

D.R.E.

, Duan

, Fornasiero

and Ralston

: J. Colloid Interf Set, 2005, 286, 526–535.

29.

Kosmulski

: J. Colloid Interf Set, 2006, 298, 730–741.

30.

Attard

: Curr. Opin. Colloid Interf Set, 2001, 6, 366–371.

31.

Sugimoto

, Zhou

and Muramatsu

: J. Colloid Interf Set, 2002, 252, 339–346.

32.

Sugimoto

, Zhou

and Muramatsu

: J. Colloid Interf Set, 2003, 259, 43–52.

33.

Wiese

G. R.

and Healy

T. W.

: J. Colloid Interf Set, 1975, 51,427–433.

34.

X. P.

: ‘Electrophoresis deposition of TiO film and the photocatalytic properly of the resulted TiO film’, M. D. Dissertation, Fuzhou University, China, 2004.

Influence of pH value of TiO 2 sol on surface gloss of corresponding TiO 2 film coated on ceramic tiles

Abstract

Keywords

Get full access to this article

References