Diode laser brazing of aluminium alloy to steels with aluminium filler metal

Abstract

Diode laser brazing of aluminium alloy (A5052) to interstitial free steel (IF steel) or type 304 stainless steel (SUS304) was conducted using aluminium filler metal (BA4047) with Nocolock flux. The processing parameters of laser power, wire feed rate and travel speed were varied. The strength of lap joints of A5052 on steels was evaluated by tensile shear test. The joint strength of A5052/steels was increased with increasing laser power and reached the maximum strength, more than approximately 80% of the A5052 base metal strength, at a laser power of 1300 W. Voids and incomplete penetration of filler metal were observed at the A5052/braze layer interface when the laser power was below 1100 W. The Fe–Al intermetallic compounds were formed at the steel/braze layer interfaces and grew drastically when the laser power exceeded 1300 W. Superior brazability of A5052/steels was found at brazing conditions corresponding to a temperature of filler metal droplet of 1050–1250 K.