Optimisation of eco-friendly binary binder system for powder injection moulding

Abstract

In recent years, many efforts have been made to obtain more environmentally acceptable powder injection moulding processes. In this sense, the purpose of this study is to optimise an eco-binder based on polyethylene glycol (PEG) as a water soluble component and cellulose acetate butyrate (CAB) as a natural backbone polymer derived from cellulose for powder injection moulding of zirconium silicate powders until a solvent debinding stage. Four different feedstocks have been investigated. As well as, a volume fraction of PEG and CAB 70/30 (vol.-%) and a solid loading of 57·5 (vol.-%) were maintained, molecular weights of polymers were combined in order to minimize distortion during binder solvent extraction. Water solvent debinding was carried out at three temperatures stepwise during 5 h. As a result, efficient removal of the PEG as well as free defects samples were obtained after solvent debinding for binder systems based on low molecular weight of PEG.

Keywords

Water solvent debinding Polyethylene glycol (PEG)Cellulose acetate butyrate (CAB)Zircon (zirconium silicate)Rheology Powder injection moulding Molecular weight

Get full access to this article

View all access options for this article.

References

Shi

, Huang

and Yan

: ‘Fabrication of hot-pressed zircon ceramics: Mechanical properties and microstructure’, Ceram. Int. 1997, 23, (5), 457–462.

German

and Bose

: ‘Injection molding of metals and ceramics’; 1997, Metal Powder Industries Federation. Princeton, NJ, USA.

Zaky

: ‘Effect of solvent debinding variables on the shape maintenance of green molded bodies’, J. Mater. Sci., 2004, 39, (10), 3397–3402.

Omar

, Ibrahim

, Sidik

, Mustapha

and Mohamad

: ‘Rapid debinding of 316L stainless steel injection moulded component’, J. Mater. Process. Technol. 2003, 140, (1–3), 397–400.

Krauss

, Oliveira

AAM

, Klein

, Al-Qureshi

and Fredel

: ‘A model for PEG removal from alumina injection moulded parts by solvent debinding’, J. Mater. Process. Technol., 2007, 182, (1–3), 268–273.

Checot-Moinard

, Rigollet

and Lourdin

: ‘Powder injection moulding PIM of feedstock based on hydrosoluble binder and submicronic powder to manufacture parts having micro-details’, Powder Technol., 2011, 208, (2), 472–479.

Liu

, Yang

, Xie

, Jia

and Wang

: ‘Novel fabrication of injection-moulded ceramic parts with large section via partially water-debinding method’, J. Eur. Ceram. Soc., 2012, 32, (10), 2187–2191.

Bernardo

, Hidalgo

, Jiménez-Morales

and Torralba

: ‘Feedstock development for powder injection moulding of zirconium silicate’, Powder Inject. Mould. Int., 2012, 6, (1), 75–78.

Hidalgo

, Jiménez-Morales

, Barriere

, Gelin

and Torralba

: ‘Water soluble Invar 36 feedstock development for μPIM’, J. Mater. Process. Technol., 2014, 214, (2), 436–444.

10.

Hidalgo

, Jiménez-Morales

and Torralba

: ‘Torque rheology of zircon feedstocks for powder injection moulding’, J. Eur. Ceram. Soc., 2012, 32, (16), 4063–4072.

11.

Yang

W.-W

, Yang

K.-Y

and Hon

M.-H

: ‘Effects of PEG molecular weights on rheological behavior of alumina injection molding feedstocks’, Mater. Chem. Phys., 2003, 78, (2), 416–424.

12.

Huang

M.-S

and Hsu

H.-C

: ‘Effect of backbone polymer on properties of 316L stainless steel MIM compact’, J. Mater. Process. Technol., 2009, 209, (15–16), 5527–5535.

13.

Yang

W.-W

, Yang

K.-Y

, Wang

M.-C

and Hon

M.-H

: ‘Solvent debinding mechanism for alumina injection molded compacts with water-soluble binders’, Ceram. Int., 2003, 29, (7), 745–756.