Dilatometry and differential scanning calorimetry analyses were used to study the sintering response of Al based powder mixture produced by ECKA Granules, designated as Alumix 431D. Sintering was carried out in atmospheres of pure nitrogen, nitrogen–hydrogen mixture (95∶5 by volume) and argon. The atmosphere influences the amount of shrinkage but not the sintering mechanisms. These are similar for all gases; typical liquid phase sintering mechanisms seem to be mainly responsible for the sintering behaviour. As expected, however, nitrogen is the most effective sintering atmosphere in terms of densification. Metallographic examinations are in accord with the results of thermal analyses.
KimYW, GriffithWM, FroesFH: J. Met., 1985, 37, 27–33.
2.
LumleyRN, SercombeTB, SchafferGB: Metall. Mater. Trans. A, 1999, 30A, 457–463.
3.
LallCh, HeathW: Int. J. Powder Metall., 2000, 36, 45–50.
4.
SchafferGB, HallBJ: Proc. MPIF Conf. on ‘Advances in powder metallurgy and particulate materials’, Orlando, FL, USA, June 2002, MPIF, Vol. 13, 139–149.
5.
SchafferGB, SercombeTB, HuoSH, HallBJ, SparklinJA: Proc. PM2004 World Cong., Vienna, Austria, October 2004, EPMA, Vol. 2, 11–16.
SchubertTh, PieczonkaT, BaunackS, KiebackB: Proc. EURO PM2005 Cong. & Exhibition, Prague, Czech Republic, 2005, EPMA, Vol. 1, 3–8.
25.
PieczonkaT, MitchellSC, WronskiAS, KaziorJ, HebdaM: Proc. PM Conf. on ‘Advances in powder metallurgy & particulate materials’, World Cong. and Exhibition on ‘Powder metallurgy & particulate materials’, June 2008, MPIF, Vol. 5, 25–40.
26.
SchafferGB, HallBJ: Metall. Mater. Trans. A, 2002, 33A, 3279–3284.
27.
PieczonkaT, SchubertTh, BaunackS, KiebackB: Proc. Conf. ‘Sintering’05’, Grenoble, France, 2005, Institut National Polytechnique de Grenoble, 331–334.
28.
Ecka Alumix 431, Brochure: ‘Press-ready mix for aluminum sintered parts’, Ecka Granules, Metal Powder Technologies, Fürth, Germany, 2010.
29.
DanningerH, NeubingHC, GradlJ: Proc. PM World Cong., Granada, Spain, October 1998, EPMA, 272–277.
30.
GradlJ, NeubingHC, MüllerA: Proc. PM World Cong., Vienna, Austria, October 2004, EPMA, Vol. 4, 15–21.
31.
NeubingHC: Proc. Hagen Symp., Hagen, Germany, December 2004, Fachverband Pulvermetallurgie, 3–29.