The aim is to study methods to improve the fire properties of carbon fibre reinforced epoxy composites with interlayers without compromising structural performance, i.e. using a carbon fibre veil with expandable graphite, an intrinsically flame retardant thermoplastic film or a carbon fibre reinforced thermoplastic (CFTP) layer. The CFTP layer seems the most promising, with a significant improvement in fire properties as determined with cone calorimetry, while the mechanical performance of the modified composite appears unaffected.
FAR 25·856 App. F, Pt. VII: ‘Part VII—test method to determine the burnthrough resistance of thermal/acoustic insulation materials’, Federal Aviation Administration, Department of Transportation, accessed 30 Sept 2014.
2.
‘Burnthrough resistance of fuselage’, Report EASA.2008.C19, European Aviation Safety Agency, 1st July 2009.
3.
M.G. Stevens and A.B. Morgan, ‘Fire retardancy of polymeric materials’2nd edition, Eds CA Wilkie and AB Morgan, CRC Press, Boca Raton, USA, p. 703–724, 2009.
4.
SchüttM, LuingeJW and GeistbeckM: ‘Fire retardancy of structural cfrp using thermoplastic interlayers’, Proc. ECCM-15, Venice, Italy, June 2012.
5.
LuingeJW, SchüttM and GibsonAG: ‘Fibre-reinforced composite material with improved fire-resistance and structural component made thereof’, Patent WO2013/083268, Published June 2013.
6.
ParlevlietPP, BerseeHEN and BeukersA: ‘Residual stresses in thermoplastic composites—A study of the literature—Part I: Formation of residual stresses’, Comp. A, 2006, 37A, 1847–1857.