Compressive strength reduction due to fibre waviness is a key concern in composite structures. Specimens with fibre misalignments representative of those that can occur at ply drops and resin rich areas in components were manufactured by incorporating either two or 10 discontinuous plies oriented either in 0° (‘longitudinal’) or 90° (‘transverse’). Longitudinal specimens did not fail in compression but failed by delamination initiating at the ply drops. Transverse specimens did not fail directly due to the waviness: specimens with 8° waviness failed at similar stresses and strains as fully aligned specimens, while 30° waviness specimens failed in the aligned plies at a slightly reduced overall stress due to redistribution of load from the less stiff wavy plies. None of the specimens failed directly in compression due to misalignment in the wavy plies, indicating that this is not necessarily the critical failure mechanism, and highlighting the importance of delamination and load redistribution at ply drops.
ArgonAS: ‘Fracture of composites’, in‘Treatise on materials science and technology’, (ed. , HermanH, ed), Vol. 1, 78–114; 1972, New York, Academic Press.
SchaperyRA: ‘Prediction of compressive strength and kink bands in composites using work potential’, Int. J. Solids Struct., 1995, 32(6/7), 739–765.
5.
PimentaS, GutkinR, PinhoST, RobinsonP: ‘A micromechanical model for kink-band formation: part I—experimental study and numerical modelling’, Compos. Sci. Technol., 2009, 69, 948–955.
6.
MoranPM, LiuXH, ShihCF: ‘Kink band formation and band broadening in fiber composites under compressive loading’, Acta Metall. Mater., 1995, 43(8), 2943–2958.
7.
DanielIM, HsiaoHM, WoohS: ‘Failure mechanisms in thick composites under compressive loading’, Composites B, 1996, 27B, 543–552.
8.
KuoC.-M, TakahashiK, ChouT.-W: ‘Effect of fiber waviness on the nonlinear elastic behavior of flexible composites’, J. Comp. Mater., 1988, 22, 11, 1004–1025.
9.
AdamsOD, HyerMW: ‘Effects of layer waviness on the compression strength of thermoplastic composite laminates’, J. Reinf. Plast. Compos., 1993, 12, (4), 414–429.
10.
HsiaoHM, DanielIM: ‘Effect of fiber waviness on stiffness and strength reduction of unidirectional composites under compressive loading’, Compos. Sci. Technol., 1996, 56, 5, 581–593.
11.
ChunHJ, ShinJY, DanielIM: ‘Effects of material and geometric nonlinearities on the tensile and compressive behavior of composite materials with fiber waviness’, Compos. Sci. Technol., 2001, 61, 125–134.
12.
CaiazzoA, OrletM, McShaneH, StraitL, RachauC: ‘The effects of Marcel defects on composite structural properties’, in‘Composite structures: theory and practice’, (ed. , GrantP, RousseauQ), ASTM STP1383, 158–187; 2000, West Conshohocken, PA, American Society for Testing and Materials.
13.
MrseAM, PiggottMR: ‘Compressive properties of unidirectional carbon fibre laminates. II: the effects of unintentional and intentional fibre misalignments’, Compos. Sci. Technol., 1993, 46, (3), 219–227.
14.
WisnomMR, AtkinsonJW: ‘Compressive failure due to shear instability: experimental investigation of waviness and correlation with analysis’, J. Reinf. Plast. Compos., 1996, 15, 420–439.
15.
BudianskyB, FleckNA: ‘Compressive failure of fibre composites’, J. Mech. Phys. Solids, 1993, 41, 183–211.
16.
SteevesCA, FleckNA: ‘Compressive strength of composite laminates with terminated internal plies’, Composites A, 2005, 36A, (6), 798–805.
17.
SoutisC, SmithFC, MatthewsFL: ‘Predicting the compressive engineering performance of carbon fibre-reinforced plastics’, Composites A, 2000, 31A, (6), 531–536.
18.
LeeJ, SoutisC: ‘A study on the compressive strength of thick carbon fibre/epoxy laminates’, Compos. Sci. Technol., 2007, 67, (10), 2015–2026.
19.
DanielIM, HsiaoH.-M, WoohS.-C: ‘Failure mechanisms in thick composites under compressive loading’, Composites B, 1996, 27B, (6), 543–552.
20.
LeongM, OvergaardLCT, ThomsenOT, LundE: ‘Investigation of failure mechanisms in GFRP sandwich structures with face sheet wrinkle defects used for wind turbine blades’, Compos. Struct., 2012, 94(2), 768–778.
21.
WangJ, PotterKD, HazraK, WisnonMR: ‘Experimental fabrication and characterisation techniques of out-of-plane fibre waviness in continuous fibre-reinforced composites’, J. Compos. Mater., 2012, 46, (17), 2041–2053.
22.
PotterK: ‘Understanding the origins of defects and variability in composites manufacturing’, Proc. 17th Int. Conf. on ‘Composite materials’, Edinburgh, UK, July 2009, P1.5 Potter, IOM Communications.
23.
HaberleJG, MatthewsFL: ‘An improved technique for compression testing of unidirectional fibre-reinforced plastics; development and results’, Composites, 1994, 25, 5, 358–371.