Processing of unidirectional (UD) carbon fibre reinforced thermoplastic composites using a laboratory scale modular composite line was investigated. Thin continuous tapes were manufactured from a 12k carbon fibre tow via wet impregnation impregnated using a slurry based polymer suspension. Hardware design as well as processing parameters influencing the tape quality and the fibre volume content of the resulting tapes, is discussed. Two different grades of polyetheretherketone were used for in‐house manufacturing of UD carbon fibre reinforced composite tapes. Laminates were prepared from the manufactured tapes via compression moulding and tested. Results from short beam strength, flexural and compression tests show that the properties of the manufactured composites match the properties of commercially available aromatic polymer composites (APC2). The flexibility of the process is demonstrated, showing that it is also possible to manufacture unidirectional carbon fibre reinforced polyvinylidene fluoride composites.
LacroixF, LuHQ, SchulteK: ‘Wet powder impregnation for polyethylene composites: preparation and mechanical properties’, Compos. Part A: Appl. Sci. Manuf., 1999, 30A, (3), 369–373.
4.
HoganPA: ‘The production and uses of film stacked composites for the aerospace industry’, Proc. SAMPE Conf., Society for the Advancement of Material and Process Engineering, New York, USA, 1980, 114.
LagattuF, Lafarie‐FrenotMC: ‘Variation of PEEK matrix crystallinity in APC‐2 composite subjected to large shearing deformations’, Compos. Sci. Technol., 2000, 60, (4), 605–612.
17.
NakagawaK, IshidaY: ‘Dielectric relaxations and molecular motions in poly(vinylidene‐fluoride) with crystal form II’, J. Polym. Sci. Part B: Polym. Phys., 1973, 11B, (8), 1503–1533.
‘Standard test method for short‐beam strength of polymer matrix composites and their laminates, ASTM D2344, West Conshohocken, PA, USA, 2000.
20.
‘Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials, ASTM D790, West Conshohocken, PA, USA, 2003.
21.
HaeberleJG: ‘Compressive strength and failure mechanism of unidirectional CFRP’, PhD thesis, Imperial College London, London, UK, 1991.
JelfPM, FleckNA: ‘Compression failure mechnisms in undirectional composites’, J. Compos. Mater., 1992, 26, (18), 2706–2726.
27.
BechJI, GoutianosS, AndersenTL, TorekovRK, BrøndstedP: ‘A new static and fatigue compression test method for composites’, Strain, 2008, DOI: 10·1111/j.1475–1305·2008·00521.