Blending polytetrafluorothylene (PTFE) to PA6 at different compositions was produced in a corotating twin screw extruder where PTFE acts as the polymer matrix and PA6 acts as the dispersed phase. The effects of PA6 content on mechanical and tribological properties of the composites were investigated. The worn surface morphologies of neat PTFE and its composites were examined by scanning electron microscopy (SEM) and the wear mechanisms were discussed. The presence of PA6 particles dispersed in the PTFE continuous phase exhibited superior tribological characteristics to unfilled PTFE. The optimum wear reduction was obtained when the content of PA6 is 30 vol.-%.
FrankeR., LehmannD. and KunzeK.: ‘Chemically bonded PTFE polyamides — a new generation of bearing materials’, Proc. Conf. WTC 2001, Vienna, Austria, September 2001, Austrian Chemical Society, 3-7.
2.
BelyiV. A., SviridenokA. I., PetrokovetsM. I. and SavkinV. G.: ‘Friction and wear of polymer based materials’, 235; 1982, Oxford, Pergamon Press.
3.
LiF., HuK., LiJ. L. and ZhaoB.: ‘The friction and wear characteristics of nanometer ZnO filled polytetrafluoroethylene’, Wear, 2002, 249, (10), 877.
4.
WeiT., ThuB. L., LiuJ. J. and ZhaoA. C.: ‘An investigation of the anti-wear behavior and wear mechanisms of TLCP in situ reinforced polytetrafluoroethylene composite’, Tribology, 2000, 20, (1), 10.
5.
CartledgeH. C. Y., BaillieC. and MaiY.-W.: ‘Friction and wear mechanisms of a thermoplastic composite GF/PA6 subjected to different thermal histories’, Wear, 1996, 194, (1-2), 178–184.
6.
SuF.-H., ZhangZ.-Z. and LiuW.-M.: ‘Tribological behavior of hybrid glass/PTFE fabric composites with phenolic resin binder and nano-TiO2 filler’, Wear, 2008, 264, (7-8), 562–570.
7.
ShiY. J., FengX., WangH. Y., LiuC. and LuX. H.: ‘Effects of filler crystal structure and shape on the tribological properties of PTFE composites’, Tribot Int., 2007, 40, (7), 1195–1203.
8.
BijweJ., RattanR. and FahimM.: ‘Abrasive wear performance of carbon fabric reinforced polyetherimide composites: influence of content and orientation of fabric’, Tribol. Int., 2007, 40, (5), 844–854.
9.
BijweJ. and RattanR.: ‘Carbon fabric reinforced polyetherimide composites: optimization of fabric content for best combination of strength and adhesive wear performance’, Wear, 2007, 262, (5-6), 749–758.
10.
SuF.-H., ZhangZ.-Z., GuoF., MenX.-H. and LiuW.-M.: ‘Friction and wear properties of fabric/phenolic composites with plasma treated-hybrid glass/PTFE fabric’, Compos. Set Technot, 2007, 67, (6), 981–988.
11.
WangY. X. and YanF. Y.: ‘A study on tribological behaviour of transfer films of PTFE/bronze composites’, Wear, 2007, 262, (7-8), 876–882.
12.
LinJ.-C.: ‘Compression and wear behavior of composites filled with various nanoparticles’, Composites B, 2007, 38B, (1), 79–85.