In this paper, comprehensive utilisation of hydrometallurgy zinc residue, goethite especially, was proposed. The raw material used in this study was mixed residue while the mass ratio of goethite and lead–silver residue was fixed at 4∶1. Based on the characters of mixed residue, the top blowing fuming method was taken by using induction furnace. The effects of parameters such as CaO/SiO2 (0·61–0·91), C/feed mass ratio (18–26%) and reduction time (20–60 min) had been studied. Under the optimum conditions (CaO/SiO2 = 0·71; C/feed mass ratio of 24%; reduction time of 50 min), the average fuming efficiency of zinc, lead and sliver in the mixed residue could reach up to 97·2, 98·1 and 82% respectively.
ChoiCY and LeeYH. 1999. Treatment of zinc residues by ausmelt technology at Onsan zinc refinery, in ‘REWAS ‘99: global symposium on recycling, waste treatment and clean technology’, San Sebastain, Spain.
2.
JakE and HayesP. 2002. Phase equilibria and thermodynamics of zinc fuming slags, Can. Metall. Q., 41, 163–174.
3.
JakE, HayesP and LeeH. 1995. Improved methodologies for the determination of high temperature phase equilibria, Met. Mater. Int., 1, 1–8.
4.
JakE and HayesPC. 2004. Phase equilibria determination in complex slag systems, Proc. Int. Conf. on ‘Molten slags, fluxes and salts’, Cape Town, South Africa, South African Institute of Mining and Metallurgy.
5.
JakE, ZhaoB and HayesP. 2000. Experimental study of phase equilibria in the systems Fe-Zn-O and Fe-Zn-Si-O at metallic iron saturation, Metall. Mater. Trans. B, 31, 1195–1201.
6.
JakE, ZhaoB and HayesP. 2002a. Experimental study of phase equilibria in the ‘FeO’-ZnO-(CaO+SiO2) system with CaO/SiO2 weight ratios of 0·33, 0·93, and 1·2 in equilibrium with metallic iron, Metall. Mater. Trans. B, 33, 877–890.
7.
JakE, ZhaoB and HayesP. 2002b. Experimental study of phase equilibria in the ‘FeO’-ZnO-(CaO+SiO2) system with the CaO/SiO2 weight ratio of 0·71 at metallic iron saturation, Metall. Mater. Trans. B, 33, 865–876.
8.
JhaMK, KumarV and SinghRJ. 2001. Review of hydrometallurgical recovery of zinc from industrial wastes, Res. Cons. Recycl., 33, 1–22.
9.
MatthesJ, WaibelP and KellerHB. 2011. A new infrared camera-based technology for the optimization of the Waelz proecess for zinc recycling, Miner. Eng., 24, 944–949.
10.
RttenJ. 2007. Application of pyro-metallurgical -process on resource recycling of steel mill dust, Proc. 55th GDMB Zinc Experts Committee Meeting, Balen, Belgium.
11.
RaghavanV. 2010. Fe-O-Si-Zn (iron-oxygen-silicon-zinc), J. Phase Equil. Diffus., 31, 385–386.
12.
RichardsG, BrimacombeJ and ToopG. 1985. Kinetics of the zinc slag-Fuming process: Part i. industrial measurements, Metall. Mater. Trans. B, 16, 513–527.
13.
SiegmundAH.-J. 2000. Primary lead production – a survey of existing smelters and refineries, in ‘Lead-zinc 2000’, (ed. J. E. Dutrizac et al.), Pittsburgh, USA.
14.
VerscheureK, Van CampM, BlanpainB, WollantsP, HayesP and JakE. 2005. Modelling of a submerged plasma process for Zn-containing residues treatment and acid mine drainage waters, Proc. European Metallurgical Conf., (ed. U. Waschki), 2005 (ERA 2010 Rank B) Dresden, GDMB.
15.
VerscheureK, Van CampM, BlanpainB, WollantsP, HayesP and JakE. 2007. Continuous fuming of zinc-bearing residues: Part II. the submerged-plasma zinc-fuming process, Metall. Mater. Trans. B, 38, 21–33.
16.
VerscheureK, Van CampM, BlanpainB, WoolantsP, HayesP and JakE. 2006. Freeze linings in zinc fuming process, Proc. Sohn Int. Symp. on ‘Advanced processing of metals and materials’, (ed. F. Kongoli and R. G. Reddy), San Diego, USA, The Minerals, Metals & Materials Society.
17.
XuPL, YuanHK, FeiW and JunLJ. 2010. Treatment of zinc leaching residues at a high percentage by using oxygen low blow furnace, China patent application 201010553116.X.