The rotating cylinder method was applied to measure the viscosities of an industrial iron silicate slag and mixtures of this slag with 5, 10 and 15 wt-% alumina addition, in temperature range 1100–1300°C. The measured viscosities were compared with the predicted values using two of the commercially available software products for viscosity calculations, namely Thermoslag®1·5 and FactSage™6·2. As the models can only predict viscosities for a solid free melt, obtained values by FactSage™6·2 were modified using the Einstein–Roscoe equation. Results show that aluminium behaves as a network former cation in this type of slag, and by increasing the alumina concentration, the melt becomes progressively polymerised. Consequently, the viscosity of the slag increases at a given temperature, which is supported by thermodynamic predictions. According to the modified FactSage™6·2 calculations, the viscosity of the solid containing slag increases from 2·1 to 5·5 poise at the industrial operating temperature (∼1250°C).
GhoshD, KrishnamurthyVA, SankaranarayananSR. 2010. Application of optical basicity to viscosity of high alumina blast furnace slag, J. Min. Metall. B, 46B, (1), 41–49.
IidaT, SakaiH, KitaY, MurakamiK. 2000. Equation for estimating viscosities of industrial mold fluxes, High Temper. Mater. Process., 19, (3–4), 153–164.
6.
KondratievA, HayesPC, JakE. 2006a. Development of a Quasi-chemical viscosity model for fully liquid slags in the Al2O3–CaO– ‘FeO’–MgO–SiO2 system. Part 1.Description of the model and its application to the MgO, MgO–SiO2, Al2O3–MgO and CaO–MgO sub-systems, ISIJ International, 46, (3), 359–367.
7.
KondratievA, HayesPC, JakE. 2006b. Development of a Quasi-chemical viscosity model for fully liquid slags in the Al2O3–CaO–‘FeO’–MgO–SiO2 system. Part 2.A review of the experimental data and the model predictions for the Al2O3–CaO–MgO, CaO–MgO–SiO2 and Al2O3–MgO–SiO2 systems, ISIJ International, 46, (3), 368–374.
8.
KondratievA, HayesPC, JakE. 2006 c. Development of a Quasi-chemical viscosity model for fully liquid slags in the Al2O3–CaO– ‘FeO’–MgO–SiO2 system. Part 3. Summary of the model predictions for the Al2O3–CaO–MgO–SiO2 system and its sub-systems, ISIJ Int., 46, (3), 375–384.
9.
KondratievA, HayesPC, JakE. 2008. Development of a Quasi-chemical viscosity model for fully liquid slags in the Al2O3–CaO–‘FeO’-MgO–SiO2 system. The experimental data for the ‘FeO’–MgO–SiO2, CaO–‘FeO’–MgO–SiO2 and Al2O3–CaO–‘FeO’–MgO–SiO2 systems at iron saturation, ISIJ International, 48, (1)7–16.
10.
KondratievA, JakE. 2001. Predicting coal ash slag flow characteristics (viscosity model for the Al2O3–CaO–‘FeO’–SiO2 system), Fuel, 80, 1989–2000.
11.
KowalczykJ, MrozW, WarczokA, UtigardTA. 1995. Viscosity of copper slags from chalcocite concentrate smelting, Metall. Mater. Trans. B, 26B, 1217–1223.
12.
KucharskiM, StubinaNM, ToguriJM. 1989. Viscosity measurement of molten Fe–O–SiO2, Fe–O–CaO–SiO2, and Fe–O–MgO–SiO2 slags, Can. Metall. Q., 28, (1), 7–11.
13.
MillsKC. 1993. The influence of structure on the physico-chemical properties of slags, ISIJ Int., 33, (1), 148–155.
14.
MillsKC, FoxAB, ThackrayRP, LiZ. 2004. ‘The performance and properties of mould fluxes’, Proc. VII Int. Conf. on ‘Molten slags fluxes and salts’, Cape Town, South Africa, January 2004, South Africa Institute of Mining & Metallurgy.
15.
NakamotoM, LeeJ, TanakaT. 2005. A model for estimation of viscosity of molten silicate slag, ISIJ Int., 45, (5), 651–656.
16.
ParkH-S, ParkSS, SohnI. 2011. The viscosity behaviour of FeOt–Al2O3–SiO2 copper smelting slags, Metall. Mater. Trans. B, 42B, 692–699.
17.
PerssonM, GörnerupM, SeetharamanS. 2007. Viscosity measurements of some mould flux slags, ISIJ Int., 47, (10), 1533–1540.
18.
RoscoeR. 1952. The viscosity of suspensions of rigid spheres, Br. J. Appl. Phys., 3, 267–269.
19.
SaitoN, HoriN, NakashimaK, MoriK. 2003. Viscosity of blast furnace type slags, Metall. Mater. Trans. B, 34B, 509–516.
SeetharamanS, SichenD. 1994. Estimation of viscosities of binary metallic melts using Gibbs energies of mixing, Metall. Mater. Trans. B, 25B, 589–595.
22.
SeetharamanS, SichenD. 1997. Viscosities of high temperature systems-A modelling approach, ISIJ Int., 37, (2)109–118.
23.
ShahbazianF, SichenD, MillsKC, SeetharamanS. 1999. Experimental studies of viscosities of some CaO–CaF2–SiO2 slags, Ironmaking Steelmaking, 26, (3)193–199.
24.
ShuQ, ZhangJ. 2006. A semi-empirical model for viscosity estimation of molten slags in CaO–FeO–MgO–MnO–SiO2 systems, ISIJ Int., 46, (11)1548–1553.
25.
ShuQF, HuXJ, YanBJ, ZhangJY, ChouK-C. 2010. New method for viscosity estimation of slags in the CaO–FeO–MgO–MnO–SiO2 system using optical basicity, Ironmaking Steelmaking, 37, (5), 387–391.
26.
SichenD, BygdenJ, SeetharamanS. 1994. A model for estimation of viscosities of complex metallic and ionic melts, Metall. Mater. Trans. B, 25B, 519–525.
27.
SongM, ShuQ, SichenD. 2011. Viscosities of the quarternary Al2O3–CaO–MgO–SiO2 slags, Steel Res. Int., 82, (3), 260–268.
28.
SridharS, MillsKC, AfrangeODC, LörzHP, CarliR. 2000. Break temperatures of mould fluxes and their relevance to continuous casting, Ironmaking Steelmaking, 27, (3), 238–242.
29.
SuhI-K, WasedaY, YazawaA. 1988. Some interesting aspects of non-ferrous metallurgical slags, High Temper. Mater. Process., 8, (1)65–88.
ViswanathanNN, JiF-Z, SichenD, SeetharamanS. 2001. Viscosity measurements on some fayalite slags, ISIJ Int., 41, (7), 722–727.
32.
WrightS, ZhangL. 2004, The influence of Fe3+/Fe2+ ratio on the viscosity of iron silicate slags, Proc. VII Int. Conf. on ‘Molten slags, fluxes, and salts’, Cape Town, South Africa, January 2004, South Africa Institute of Mining & Metallurgy.
33.
WrightS, ZhangL, SunS, JahanshahiS. 2000. Viscosity of a CaO–MgO–Al2O3–SiO2 melt containing spinel particles at 1646 K, Metall. Mater. Trans. B, 31B, 97–104.
34.
Xu-longT, Zuo-taiZ, MinG, MeiZ, Xi-dongW. 2011. Viscosities behavior of CaO–SiO2–MgO–Al2O3 slag with low mass ratio of CaO to SiO2 and wide range of Al2O3 content, J. Iron Steel Res. Int., 18, (2), 1–6.
35.
ZhangL, JahanshahiS. 1998a. Review and modeling of viscosity of silicate melts: part II. viscosity of melts containing iron oxide in the CaO–MgO–MnO–FeO–Fe2O3–SiO2 system, Metall. Mater. Trans. B, 29B, 187–195.
36.
ZhangL, JahanshahiS. 1998b. Review and modelling of viscosity of silicate melts: Part I. Viscosity of binary and ternary silicates containing CaO, MgO, and MnO, Metall. Mater. Trans. B, 29B, 177–186.