The aim of this work was to explore the effect of mineralogy and gas reductant on the reduction of nickel laterites. Three different nickel saprolitic ores reduced by carbon monoxide were examined, and the results were compared with hydrogen reduction of the same ores. The reduction experiments were carried out in a thermobalance furnace which allows continuous measurement of mass change. The ores were reduced in CO/CO2 (72%∶28%) at 750 and 900°C for 90 min. Chemical analysis was utilised to determine the degree of metallisation of the reduced pellets. It was found that the reduction rate and degree of removable oxygen at 750 and 900°C in CO/CO2 was lower compared to reduction experiments in H2/N2 (72%∶28%). The reducibility of the samples seems to depend on mineralogy and their modes of decomposition and recrystallisation. The results clearly indicate that using various reducing gases has an impact on the reduction behaviour and generation of metallics of nickel saprolitic ores.
BunjakuA., KekkonenM., HolappaL.2010. Phenomena in thermal treatment of lateritic nickel ores up to 1300°C, Proc. 12th Int. Ferroalloys Cong., (ed. , VartiainenA), 641–652, Helsinki, Outotec Oyj.
2.
BunjakuA., KekkonenM., TaskinenP.2012. The effect of mineralogy on reducibility of calcined nickel saprolite ore by hydrogen, Min. Process. Extract. Metall. (Trans. Inst. Min. Metall. C), 121, (1), 16–22.
3.
BunjakuA., KekkonenM., TaskinenP., HolappaL.2011. Thermal behaviour of hydrous nickel-magnesium silicates when heating up to 750°C, Min. Process. Extract. Metall. (Trans. Inst. Min. Metall. C), 120, (3), 139–146.
4.
BurgerP.A.1996. Origins and characteristics of lateritic nickel deposits, Proc. Nickel ’96 Mineral to Market Cong, (ed. , GrimseyE S, NeussI), 179–183, Kalgoorlie, The Australasian Institute of Mining and Metallurgy.
5.
CroweB.JC, UtigardTA2003. Kinetics of carbon monoxide reduction of oxidized calcines, Can. Metall. Q., 42, (4), 447–454.
6.
DalviA.D, SmeltzerWW1970. Thermodynamics of the iron–nickel–oxygen system at 1000°C, J. Electrochem. Soc., 117, 1431–1436.
7.
DalviA.D., SridharR1976. Thermodynamics of the Fe–Ni–O and Fe–Ni systems at 1056K to 1380K, Can. Metall. Q., 15, (4), 349–357.
8.
DiazC.M., LandoltCA., DalviA.D., BaconW.G., OsborneR.C.2004. The past and the future of nickel laterite, Proc. PDAC Int. Conv., Toronto, Ont., Canada, March, PDAC, 1–27.
9.
EcklemanE.J.2010. Facility-level energy and greenhouse gas life-cycle assessment of global nickel industry, Resour. Conserv. Recycl., 54, (3), 256–266.
10.
HalletC.J.1997. A thermodynamic analysis of solid state reduction of nickel from laterite minerals, Proc. Nickel–Cobolt ’97 Int. Symp., (ed. , LevacC A, BerrymanR A), Vol. II, 299–312, Sudbury, The Metallurgical Society of CIM.
11.
HangP.T., BrindleyG.W.1973. The nature of garnierites-I, II, III, Clays Clay Miner., 21, (1), 27–57.
12.
HarrisC.T., PeaceyJ.G., PicklesC.A.2009Thermal upgrading of nickeliferous laterites: a review, Proc. Pyrometallurgy of Nickel and Cobalt 2009 Int. Symp(, LiuJ, ), 51–75, Montreal, The Metallurgical Society of the Canadian Institute of Mining, Metallurgy and Petroleum.
13.
KawaharaM., ToguriJ.M., BergmanR.A.1988. Reducibility of laterite ores, Metall. Mater. Trans. B: Process Metall. Mater. Process. Sci., 19, B181–B186.
14.
KerfootD.G.E.1991. Nickel, in Ullman's encyclopedia of industrial chemistry, 158–219, Weinheim, VCH Verlag.
15.
KobayashiY., TodorokiH., TsujiH.2011. Melting behavior of siliceous nickel ore in a rotary kiln to produce ferronickel alloys, ISIJ Int., 51, (1), 35–40.
16.
LiS., ColeyKS.2000Kinetics and mechanism of reduction of laterite ore high in serpentine, Proc. of J. M. Toguri Symp. on ‘Fundamentals of metallurgical processing(, KaiuraG, ), 179–192, Montreal, Institute of Mining, Metallurgy and Petroleum.
17.
MukhopadhyayS., JacobK.T.1995. Tie lines and activities in the system NiO–MgO–SiO2 at 1373K, J. Phase Equilib., 16, (3), 243–253.
18.
NathN.K., ChakrabortiN., ShekharR.1995. Selective reduction of Indian nickeliferrous ore: single pellet experiments, Scand. J. Metall., 24, (3), 121–138.
19.
PietiläG.K.2011. Reduction of nickel saprolite ore in CO/CO2 atmosphere, Master's dissertation, Aalto University, Espoo, Finland.
20.
RhamdhaniM.A., HayesP.C., JakE.2009. Nickel laterite part 1: microstructure and phase characterizations during reduction roasting and leaching, Min. Process. Extract. Metall. (Trans. Inst. Min. Metall. C), 118, (3), 129–145.
21.
RigopoulosE., KostikaI-P., ZevgolisE.N., HalikiaI.2004. Contribution to the recycling of rotary kiln dust in nickeliferous laterite reduction. Reductive behavior of the dust, Proc. Int. Laterite Nickel Simp., (ed. , ImrieW P, LaneD M), 479–492, Charlotte, NC, TMS.
22.
SolarM.Y.2008. Selection of optimum ferronickel grade for smelting nickel laterites, CIM Mag., 2, (3), 74.
23.
SolarM.Y.2009Mechanical slag losses in laterite smelting nickelProc. Pyrometallurgy of Nickel and Cobalt 2009 Int. Symp.(, LiuJ, ), 277–292, Montreal, The Metallurgical Society of the Canadian Institute of Mining, Metallurgy and Petroleum.
24.
ShiraneY., KuwasakiN., MitsuneY.1980. Activities of NiO in solid solutions of ternary system MgO–NiO–SiO2, Proc. Australia/Japan Extractive Metall. Symp., (ed. , DaveyT R A), 409–418, Sydney, The Australian Institute of Mining and Metallurgy.
25.
SzekelyJ., EvansJW1971. Studies in gas–solid reactions. Part II: an experimental study of nickel oxide reduction with hydrogen.Metall. Mater. Trans. B (Process Metall. Mater. Process. Sci.), 2B, (6), 1699–1710.
26.
UtigardT., BergmanR.A.1992. Gaseous reduction of laterite ores, Metall. Mater. Trans. B (Process Metall. Mater. Process. Sci.), 23B, B271–B275.
27.
ValixM., CheungW.H.2002. Study of phase transformation of laterite ores at high temperature, Miner. Eng., 15, (8), 607–612.
28.
WatanabeT., OnoS, AraiH., MatsumoriT.1987. Direct reduction of garnierite ore for production of ferro-nickel with a rotary kiln at Nippon Yakin Kogyo Co., Oheyama Works, Int. J. Miner. Process., 19, 173–187.
29.
ZevgolisE.N., ZografidisCh., HalikiaI, DevlinE.2009. Roasting reduction study of Greek nickeliferous laterites, Proc. of EPD Cong., (ed. , HowardS M), 493–500, San Francisco, CA, TMS.
30.
ZhuD.Q., CuiY., PanJ., LiH.Q., QiuG.Z.2008Investigation on manufacture of ferronickel from low grade nickel laterite by prereduction-magnetic separation-smeltingProc. of 24 Int. Mineral Processing Cong.(, WangD D, ), 1622–1633, Beijing, Science Press.