The electrochemical corrosion behaviour of biomedical Ti–25Nb–3Mo–3Zr-2Sn (TLM) alloy was investigated in various simulated body fluids at 37±0·5°C utilising potentiodynamic polarisation and current–time curves. The Ti–6Al–4V (TC4) alloy was also investigated to make a comparison. The different simulated body fluids comprised of 0·9NaCl saline, Hank's and Ringer's solution were employed. The effect of heat treatment on the electrochemical behaviour of the TLM alloy was also considered. It was discovered that all the test specimens were passivated once immersed into the simulated body fluids. It was also found that the TLM alloy has poorer corrosion resistance in Hank's solution, due to the chemical composition of the Hank's. After different heat treated, the TLM alloy had different phases and microstructure, and the corrosion behaviour of the TLM alloy was different. In this study, after the heat treatment of 760°C/1 h/AC+550°C/6 h/AC, the TLM alloy had better corrosion resistance. Owing to the corrosion resistance of the TLM alloy was influenced by numerous factors, such as microstructure and the chemical composition of electrolyte, the corrosion behaviour of the TLM alloy is complex. By comparing with the corrosion behaviour of the TC4 alloy, the TLM alloy has poorer corrosion resistant than the TC4 alloy under the same conditions. But the current–time curves of the TLM alloy were more stable than these of the TC4 alloy with further experiments, because of the more passivation film on the surface of the TLM alloy.