Abstract
This paper presents the influence of solution and aging temperatures on the microstructure and mechanical properties of 319 secondary cast aluminium alloy. Experimental alloy was subjected to different heat treatment cycles. Heat treatments were designed with two solutionising temperatures (504 and 545°C) at two solutionising times (4 and 8 h), followed by quenching in water at 60°C and artificial aging. The artificial aging was carried out at two temperatures (200 and 154°C) for 6 h. The improvement in mechanical properties was obtained with low solution temperature (504°C) for 8 h followed by quenching in water to 60°C and aging at low temperature (154°C). The increase in the solutionising temperature from 504 to 545°C was recommendable only for short solutionising time (4 h). Increase in the aging temperature from 154 to 200°C has led to the increase in hardness with the corresponding decrease in ductility. Aging under unfavourable conditions (prolonged aging at high temperature) caused coarsening of spheroidised eutectic silicon crystals and precipitated particles resulted in deleterious effect on the tensile strength.
Get full access to this article
View all access options for this article.