A partially recrystallised extrathinned interstitial free steel has been investigated by X-ray diffraction and electron backscattered diffraction (EBSD). The results show that the orientation of recrystallisation nuclei plays an important role in the process of recrystallisation texture formation. The growth of the 〈111〉∥normal direction (ND) is very rapid compared with its nucleation.
ZhaoH., RamaS. C., BarberG. C., WangZ. and WangX.: J. Mater. Process. Technol., 2002, 128, 73–79.
2.
RayR. K., JonasJ. J. and HookR. E.: Int. Mater. Rev., 1994, 39, 129–171.
3.
CaulM. and RandleV.: Mater. Charact., 1997, 38, 155–163.
4.
MurakamiH. and SenumaT.: ISIJ Int., 1998, 38, 653–660.
5.
SamajdarI., VerlindenB. and Van HoutteP.: Acta Mater., 1998, 46, 2751–2763.
6.
SamajdarI., VerlindenB., KestensL. and Van HoutteP.: Acta Mater., 1999, 47, 55–65.
7.
BarnettM. R. and KestensL.: ISIJ Int., 1999, 39, 923–929.
8.
BaczynskiJ. and JonasJ. J.: Proc. 11th Int. Conf. on ‘Textures of materials’: ICOTOM11, Xi'an, China, (ed.LiangZ. et al.), 387-389; 1996, Beijing, International Academic Publishers.
9.
DohertyR. D., HughesD. A., HumphreysF. J., JonasJ. J. and JensenD. J.: Mater. Sci. Eng. A, 1997, A238, 219–274.
10.
HayakawaY. and SzpunarJ. A.: Acta Mater., 1997, 45, 2425–2434.
11.
LeeS. H. and LeeD. N.: Mater. Set Eng. A, 1998, A249, 84–90.
12.
SchulzL. G.: J. Appl. Phys., 1949, 20, 1030–1041.
13.
LiangZ. D., XuJ. Z. and WangF.: ‘3-D orientation distribution function analysis of textured materials’; 1986, Shengyang, China, Northeastern University of Technology Press.
14.
VanderschuerenD., YoshinagaN. and KoyamaK.: ISIJ Int., 1996, 36, 1046–1054.
15.
SamajdarI., VerlindenB., Van HoutteP. and VanderschuerenD.: Scr. Mater., 1997, 37, 869–874.