Abstract
A wide range of cold thickness reduction (10–80%) and subsequent annealing were carried out on AISI 301LN stainless steel. X-rays and Feritscope MP30 were used to identify the strain induced α′-martensite phase and its volume fraction respectively. The microstructure was observed by optical micrograph and scanning electron microscope. The results show that shear bands were present and strain induced α′-martensite nucleated at their intersections. The volume fraction of α′-martensite increased with the increased cold reduction by the continuous growth of embryos, which resulted in the increasing yield and tensile strength. The reversion of α′-martensite to austenite occurred after subsequent annealing. The grain size variation of austenite was related to the annealing regime. A good combination of strength and ductility can be obtained after annealing at 650°C for 30 min. The effect of grain size on yield strength conformed with the Hall–Petch relationship in the entire range of our analysis.
Get full access to this article
View all access options for this article.