Over recent years, owing to the need to increase productivity, it has been necessary among other things to increase the hot metal temperature in the blast furnace hearth. As a result, refractory lining wear becomes more intense. While publications present a host of comparative tests for hearth refractories and their performance, hardly any information is available in such publications regarding reaction mechanisms and further deterioration of these materials. Based upon comparative laboratory test results using two carbon materials of different concepts, the various reaction mechanisms and enhanced refractory lining deterioration for the blast furnace hearth have been identified. From an understanding of these wear mechanisms acting upon the hearth lining, it has been decided to introduce some practical operating measures, with a view to extending the blast furnace campaign.

Get full access to this article

View all access options for this article.

References

Spreij

: Proc. Conf. UNITECR’95, Osaka, Japan, 1995, Technical Association of Refractories, 167–175.

Ishikawa

et al.: Taikabutsu Overseas, 1993, 14, (3), 49–55.

Yamaguchi

A. E.

Zhang

: 2nd Int. Symp. on ‘Advances in refractories for the metallurgical industry’, Montreal, Canada, 1996, CIM.

Bauer

J. M.

et al.: ISS Ironmaking Conf. Proc., 1988, 47, 27–33.

Michio

Yamamoto

: Taikabutsu Overseas, 1990, 2, (1), 42–50.

Onoye

et al.: Trans. Iron Steel Inst. Jpn, 1983, 23, (8), B276.

Tamura

et al.: Am. Ceram. Soc. Bull., 1986, 65, 1065–1072.

Tijhuis

G. J.

Bleijendaal

N. G. J.

: Steel Times Int., 1995, 19, (3), 26–27.

Hiragushi

et al.: Iron Steel Eng., 1978, 55, (5), 47–53.

10.

Campbell

J. P.

Standish

: Iron Steelmaker, 1984, 11, (9), 39–45.

11.

Bold

D. A.

Evans

N. T.

: Rev. Latina-am. Siderurgia, 1975, 185, 77–87.

12.

Chow

C. K.

W. K.

: Trans. AIME, 1979, 38, 201–205.

13.

Morti

Starzacher

: Proc. Colloquium on ‘Blast furnace refractories’, Aachen, Germany, 1982 Verlag Stahleisen.

14.

Aratani

et al.: Int. Ceram. Rev ., 1983, Special Issue, 86–92.

15.

M. W. R.

Brown

J. J.

: J. Am. Ceram. Soc., 1989, 72, (1), 110–115.

16.

Podgurski

H. H.

et al.: J. Am. Ceram. Soc., 1950, 72, 5382–5388.

17.

Uenaka

et al.: ISS Ironmaking Conf. Proc., 1986, 45, 185–191.

18.

Biswas

A. K.

: ‘Principles of blast furnace iron making’, 1–13; 1982, Brisbane, Australia, University of Queensland.

19.

Miwa

Yamamoto

: Taikabutsu Overseas, 1982, 2, (1), 42–50.

Wear mechanism for blast furnace hearth refractory lining

Abstract

Get full access to this article

References