In this work, the corrosion fatigue behaviour of steel armours used in the flexible pipes, in aqueous solutions initially containing different concentrations of Fe²⁺, was investigated by four-point bending testing under saturated 1 bar CO₂ condition. Corrosion fatigue results were supported with ex situ measurements of Fe²⁺ and pH. Characterisation of the corrosion scales and crack formations was performed using microscopic and diffraction techniques. Fatigue results showed two times better fatigue life, at the stress ranges of 250 MPa, for samples tested in solutions containing the concentration of Fe²⁺ marginally above the solubility limit of FeCO₃ compared to the samples tested in highly supersaturated solution of Fe²⁺. Results revealed that the impact of the alternating stresses on the corrosion behaviour of samples reduces with lowering the applied stresses. At the stress range of 100 MPa, fatigue samples experienced the same corrosion rate as samples that were not subjected to dynamic loading.

Keywords

Carbon steel Carbon dioxide Corrosion fatigue Supersaturation Iron carbonate

Get full access to this article

View all access options for this article.

References

Rubin

and Gudme

: ‘Qualification of steel wire for flexible pipes’. NACE International, Houston, TX, March 2006, Paper 06149..

Rubin

and Gudme

: ‘Test method for corrosion fatigue testing of cold rolled steel wire in sour and sweet environment based on deflection controlled four point bending’. NACE International, Houston, TX, March 2009, Paper 09103..

Rubin

Overby

Nielsen

T. S.

Haahr

and Gudme

: ‘Corrosion rates of carbon steel in confined environments’. NACE International, Houston, TX, March 2012, Paper 01495..

Remita

Ropital

and Kittel

: ‘Experimental and theoretical investigation of the uniform corrosion in the annulus of offshore flexible pipelines’. NACE International, Houston, TX, March 2008, Paper 08538..

Berntsen

Seiersten

and Hemmingsen

: ‘Effect of FeCO₃ supersaturation and carbide exposure on the CO₂ corrosion rate of carbon steel’ Corrosion 2013 69 601–613. doi: 10.5006/0553

Henriquez

Pébère

Ochoa

and Viloria

: ‘Electrochemical investigation of the corrosion behavior of API 5L-X65 carbon steel in carbon dioxide medium’ Corrosion 2013 69 1171–1179. doi: 10.5006/0971

Dugstad

: ‘The importance of FeCO₃ supersaturation on the CO₂ corrosion of carbon steels’. NACE International, Houston, TX, March 1992, Paper 14..

Lin

Zheng

Bai

and Zhao

: ‘Effect of temperature and pressure on the morphology of carbon dioxide corrosion scales’ Corrosion 2006 62 501–507. doi: 10.5006/1.3279908

Nordsveen

Nešić

Nyborg

and Stangeland

: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films—part 1: theory and verification’ Corrosion 2003 59 443–456. doi: 10.5006/1.3277576

10.

Ruzic

Veidt

and Nešić

: ‘Protective iron carbonate films—part 3: simultaneous chemo-mechanical removal in single-phase aqueous flow’ Corrosion 2007 63 758–769. doi: 10.5006/1.3278425

11.

Han

Brown

B. N.

and Nešić

: ‘Investigation of the galvanic mechanism for localized carbon dioxide corrosion propagation using the artificial pit technique’. NACE International, Houston, TX, March 2007, Paper 07323..

12.

Dugstad

: ‘Mechanism of protective film formation during CO₂ corrosion of carbon steel’. NACE International, Houston, TX, March 1998, Paper 31..

13.

Sun

Nešić

and Woollam

R. C.

: ‘The effect of temperature and ionic strength on iron carbonate (FeCO₃) solubility limit’ Corros. Sci., 2009 51 1273–1276. doi: 10.1016/j.corsci.2009.03.009

14.

Nešić

: ‘Key issues related to modelling of internal corrosion of oil and gas pipelines—a review’ Corros. Sci., 2007 49 4308–4338. doi: 10.1016/j.corsci.2007.06.006

15.

Nešić

Solvi

G. T.

and Enerhaug

: ‘Comparison of the rotating cylinder and pipe flow tests for flow-sensitive carbon dioxide corrosion’ Corrosion 1995 51 773–787. doi: 10.5006/1.3293555

16.

Ruzic

Veidt

and Nešić

: ‘Protective iron carbonate films—Part 1: simultaneous chemo-mechanical removal in single-phase aqueous flow’ Corrosion 2007 63 758–769. doi: 10.5006/1.3278425

17.

Nešić

: ‘An electrochemical model for prediction of corrosion of mild steel in aqueous carbon dioxide solutions’ Corrosion 1996 52 280–294. doi: 10.5006/1.3293640

18.

López

D. A.

Schreiner

W. H.

Sanchez

S. R.

and Simison

S. N.

: ‘The influence of carbon steel microstructure on corrosion layers. An XPS and SEM characterization’ Appl. Surf. Sci., 2003 207 69–85. doi: 10.1016/S0169-4332(02)01218-7

19.

López

D. A.

Simison

S. N.

and Sanchez

S. R.

: ‘EIS studies on the inhibition efficiency of benzimidazole’ Electrochim.Acta 2003 48 845–854. doi: 10.1016/S0013-4686(02)00776-4

20.

Ueda

and Ikeda

: ‘Effect of microstructure and Cr content in steel on CO₂ corrosion’. NACE International, Houston, TX, March 1996, Paper 99013..

21.

Videm

and Dugstad

: ‘Corrosion of carbon steel in an aqueous carbon dioxide environment. II. Film formation’ Mater. Perform., 1989 28 46–50.

22.

Videm

and Dugstad

: ‘Corrosion of carbon steel in an aqueous carbon dioxide environment. I. Solution effects’ Mater. Perform., 1989 28 63–67.

23.

Sun

and Nešić

: ‘Kinetics of corrosion layer formation: part 1—iron carbonate layers in carbon dioxide corrosion’ Corrosion 2008 64 334–346. doi: 10.5006/1.3278477

24.

Nyborg

and Dugstad

: ‘Mesa corrosion attack in carbon steel and 0.5 % chromium steel’. NACE International, Houston, TX, March 1998, Paper29..

25.

Kermani

M. B.

and Morshed

: ‘Carbon dioxide corrosion in oil and gas production—a compendium’ Corrosion 2003 59 659–683. doi: 10.5006/1.3277596

26.

Baboian

: ‘Corrosion tests and standards: application and interpretation. Environmental cracking-corrosion fatigue’ ASTM International, Philadelphia, PA; 2005.

27.

Akid

: ‘Corrosion fatigue’, in ‘Shreir's corrosion’928–953; 2010

Sheffield, UK

Elsevier B.V.

28.

Wang

Y. Z.

: ‘Corrosion fatigue’ 3rd edn, ‘ Uhlig's corrosion handbook’, 195–202; 2011

Edinburgh, UK

Cambridge University Press.

29.

Suresh

: ‘Fatigue of materials’ 2nd edn; 1998

Cambridge

Cambridge University Press.

30.

Félix-Henry

: ‘Prevention and monitoring of fatigue-corrosion of flexible risers’ steel reinforcements’. Proc. 26^th Int. Conf. on ‘Offshore Mechanics and Arctic Engineering’, San Diego, CA, June 2007, Paper 29186..

31.

Baxter

: ‘Corrosion fatigue of steel catenary risers in sweet production’. Proc. Int. Conf. on ‘Offshore Mechanics and Arctic Engineering’, Estoril, Portugal, June 2007, Paper 57075..

32.

van der Velden

Ewalds

H. L.

Schultze

W. A.

and Punter

: ‘Anomalous fatigue crack growth retardation in steels for offshore applications’, in ‘Corrosion Fatigue: Mechanics, Metallurgy, Electrochemistry, and Engineering, ASTM STP 801’, (eds. Crooker

T. W.

and Leis

B. N.

), 64–80; 1983 American Society for Testing and Materials 1983 64–80.

33.

Scott

P. M.

: ‘Chemistry effects in corrosion fatigue’, in ‘ Corrosion Fatigue: Mechanics, Metallurgy, Electrochemistry, and Engineering, ASTM STP 801’, (eds. Crooker

T. W.

and Leis

B. N.

), 64–80; 1983 Amercian Society for Testing and Materials.

34.

Mathis

: ‘Initiation and early growth mechanisms of corrosion fatigue cracks in stainless steels’ J. Mater. Sci., 1987 22 907–914. doi: 10.1007/BF01103528

35.

Gangloff

R. P.

: ‘Corrosion fatigue crack propagation in metals’ National Aeronautics and Space Administration, Office of Management, Scientific and Technical Information Division 1990.

36.

Xie

J. H.

: ‘A mechanism for the crack initiation of corrosion fatigue of Type 316L stainless steel in Hank's solution’ Mater. Charact., 2002 48 271–277. doi: 10.1016/S1044-5803(02)00245-0

37.

Andersen

T. R.

: ‘Corrosion fatigue of steel armours in flexible risers’. Proc. International Conference on Offshore Mechanics and Arctic Engineering, Oslo, Norway, June 2002, Paper 28052..

38.

Pfennig

Wiegand

Wolf

and Bork

C.-P.

: ‘Corrosion and corrosion fatigue of AISI 420C (X46Cr13) at 60 °C in CO₂-saturated artificial geothermal brine’ Corros. Sci., 2013 68 134–143. doi: 10.1016/j.corsci.2012.11.005

39.

Santos

Pires

Clements

Clevelario

Sheldrake

de Souza

L. F. G.

and Kenedi

P. P.

: ‘Corrosion fatigue behavior of flexible pipe tensile armor wires in CO₂ environment’ Mater. Sci. Forum 2013 758 77–82. doi: 10.4028/www.scientific.net/MSF.758.77

40.

Pelloux

and Genkin

J. M.

: ‘Corrosion fatigue’ ‘Fatigue of materials and structures: fundamentals’377–399; 2010

New York, USA

John Wiley & Sons.

41.

Fujii

C. T.

and Smith

J. A.

: ‘Environmental influences on the aqueous fatigue crack growth rates of HY-130 steel’ Corrosion Fatigue: Mechanics, Metallurgy, Electrochemistry, and Engineering, ASTM STP 801, American Society for Testing and Materials 1983 390–402.

42.

Berge

Bendiksen

Gudme

and Clements

: ‘Corrosion fatigue testing of flexible riser armour: procedures for testing and assessment of design criteria’. Proc. International Conference on Offshore Mechanics and Arctic Engineering, Cancun, June 2003, Paper 18303.

43.

Grealish

Smith

and Zimmerman

: ‘New industry guidelines for fatigue analysis of unbonded flexible risers’. Offshore Technology Conference, May 2006, Paper 18303..

44.

Berge

Langhelle

N. K.

and Eggen

T. G.

: ‘Environmental effects on fatigue strength of armour wire for flexible risers’. Proc. International Conference on Offshore Mechanics and Arctic Engineering, Estoril, Portugal, June 2008, Paper 57132..

45.

Trillo

Kane

R. D.

Ethridge

and Clements

: ‘Corrosion fatigue testing of armor wire materials in subsea environments’ 2007;. NACE International, Houston, TX, March 2007, Paper 07103..

46.

Mehdizadeh

Mcglasso

R. L.

and Landers

J. E.

: ‘Corrosion fatigue performance of a carbon steel in brine containing air, H₂S and CO₂’ Corrosion 1966 22 325–335. doi: 10.5006/0010-9312-22.12.325

47.

Langhelle

N. K.

Berge

and Igland

: ‘Joint industry project: corrosion fatigue of armour wire for flexible pipes—phase I testing in sweet environments’. Norwegian Marine Technology Research Institute 2003, Report 700120..

48.

Brantley

W. A.

and Eliades

: ‘ Orthodontic materials: scientific and clinical aspects ’, 35; 2011

Stuttgart, Germany

Georg Thieme Verlag.

49.

Pantleon

: ‘Phase identification and internal stress analysis of steamside oxides on superheater tubes by means of X-ray diffraction’ Mater. Trans. A 2011 41A.

50.

Schütze

and Holmes

D. R.

: ‘Protective oxide scales and their breakdown’ 1997

Michigan, USA

Wiley.

51.

Rogowska

Gudme

Rubin

Pantleon

and Ambat

: ‘The effect of Fe ion concentration on corrosion of carbon steel in CO₂ environment’ Corros. Eng. Sci. Technol., 2015. DOI: 10.1179/1743278215Y.0000000029.

52.

Dugstad

: ‘Fundamental aspects of CO₂ metal loss corrosion—part 1: mechanism’. NACE International, Houston, TX, March 2006, Paper 06111..

53.

Sun

J. B.

Zhang

G. A.

Liu

and Lu

M. X.

: ‘The formation mechanism of corrosion scale and electrochemical characteristic of low alloy steel in carbon dioxide-saturated solution’ Corros. Sci 2012 57 131–138. doi: 10.1016/j.corsci.2011.12.025

54.

Schmitt

and Horstemeier

: ‘Fundamental aspects of CO₂ metal loss corrosion—part II: influence of different parameters on CO₂ corrosion mechanisms’ NACE International, Houston, TX, March 2006, Paper 06112.

55.

Radon

J. C.

: ‘Crack blunting and arrest in corrosion fatigue of mild steel’ Int. J. Fract., 1976 12 467–469.

Effect of Fe ion concentration on fatigue life of carbon steel in aqueous CO 2 environment

Abstract

Keywords

Get full access to this article

References