In this work, the corrosion behaviour of steel wires in solutions containing different concentrations of Fe2+ was investigated by the linear polarisation resistance method, while the evolution of pH was monitored in situ and changes of the Fe2+ concentration were monitored ex situ. Characterisation of the corrosion scales was performed using microscopic and diffraction techniques. Scale analysis revealed that the passivation of samples, exposed to initially highly Fe2+ supersaturated solution, occurred when a formation of a double layer took place, resulting in 30 times lower corrosion rate compared to samples tested in solutions without initial Fe2+.
RubinA. and GudmeJ.: ‘Qualification of steel wire for flexible pipes’NACE International, Houston, TX, March 2006, Paper 06149.
2.
RubinA. and GudmeJ.: ‘Test method for corrosion fatigue testing of cold rolled steel wire in sour and sweet environment based on deflection controlled four point bending’NACE International, Houston, TX, March 2009, Paper 09103.
3.
RubinA.OverbyS.NielsenT. S.HaahrM. and GudmeJ.: ‘Corrosion rates of carbon steel in confined environments’NACE International, Houston, TX, 2012, Paper 01495.
4.
NešićS.: ‘Key issues related to modelling of internal corrosion of oil and gas pipelines—a review’Corros. Sci., 2007494308–4338. doi: 10.1016/j.corsci.2007.06.006
5.
NordsveenM.NešićS.NyborgR. and StangelandA.: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films—part 1: theory and verification’Corrosion200359443–456. doi: 10.5006/1.3277576
6.
NešićS.NyborgR.StangelandA. and NordsveenM.: ‘Mechanistic model for CO2 corrosion with protective iron carbonate films’NACE International, Houston, TX, March 2001, Paper 01040.
7.
NešićS.: ‘An electrochemical model for prediction of corrosion of mild steel in aqueous carbon dioxide solutions’Corrosion199652280–294. doi: 10.5006/1.3293640
8.
NešićS. and LeeK. -L. J.: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films—part 3: film growth model’Corrosion200359616–628. doi: 10.5006/1.3277592
9.
NešićS.NordsveenM. and NyborgR.: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films—part 2: a numerical experiment’Corrosion200359489–497. doi: 10.5006/1.3277579
10.
SunW.NešićS. and WoollamR. C.: ‘The effect of temperature and ionic strength on iron carbonate (FeCO3) solubility limit’Corros. Sci., 2009511273–1276. doi: 10.1016/j.corsci.2009.03.009
SunW. and NešićS.: ‘Kinetics of corrosion layer formation: part 1—iron carbonate layers in carbon dioxide corrosion’Corrosion200864334–346. doi: 10.5006/1.3278477
13.
VidemK. and DugstadA.: ‘Corrosion of carbon steel in an aqueous carbon dioxide environment. II: film formation’Mater. Perform., 19892846–50.
14.
VidemK. and DugstadA.: ‘Corrosion of carbon steel in an aqueous carbon dioxide environment. I: solution effects’Mater. Perform., 19892863–67.
15.
DugstadA.: ‘The importance of FeCO3 supersaturation on the CO2 corrosion of carbon steels’NACE International, Houston, TX, March 1992, Paper 14.
16.
NyborgR. and DugstadA.: ‘Mesa corrosion attack in carbon steel and 0.5% chromium steel’NACE International, Houston, TX, March 1998, Paper 29.
17.
KinsellaB.TanY. J. and BaileyS.: ‘Electrochemical impedance spectroscopy and surface characterization techniques to study carbon dioxide corrosion product scales’Corrosion199854835–842. doi: 10.5006/1.3284803
18.
NešićS.SolviG. T. and EnerhaugJ.: ‘Comparison of the rotating cylinder and pipe flow tests for flow-sensitive carbon dioxide corrosion’Corrosion199551773–787. doi: 10.5006/1.3293555
19.
RuzicV.VeidtM. and NešićS.: ‘Protective iron carbonate films—part 3: simultaneous chemo-mechanical removal in single-phase aqueous flow’Corrosion200763758–769. doi: 10.5006/1.3278425
20.
DugstadA.: ‘Fundamental aspects of CO2 metal loss corrosion—part 1: mechanism’NACE International, Houston, TX’; 2006.
21.
ChokshiK.SunW. and NešićS.: ‘Iron carbonate scale growth and the effect of inhibition in CO2 corrosion of mild steel’NACE International, Houston, TX, 2005, Paper 05285.
22.
HanJ.BrownB. N. and NešićS.: ‘Investigation of the galvanic mechanism for localized carbon dioxide corrosion propagation using the artificial pit technique’NACE International, Houston, TX, 2007, Paper 07323.
23.
NešićS.LeeJ. and RuzicV.: ‘A mechanistic model of iron carbonate film growth and the effect on CO2 corrosion of mild steel’. NACE International, Houston, TX; 2002.
24.
CroletJ. L.ThevenotN. and NešićS.: ‘Role of conductive corrosion products in the protectiveness of corrosion layers’Corrosion199854194–203. doi: 10.5006/1.3284844
25.
Stephen TaitW.: ‘An introduction to electrochemical corrosion testing for practicing engineers & scientists’; 1994Racine, WIPairODocs Professionals.
26.
DugstadA.: ‘Mechanism of protective film formation during CO2 corrosion of carbon steel’NACE International, Houston, TX, 1998, Paper 31.
27.
BerntsenT.SeierstenM. and HemmingsenT.: ‘Effect of FeCO3 supersaturation and carbide exposure on the CO2 corrosion rate of carbon steel’Corrosion201369601–613. doi: 10.5006/0553
28.
HanJ.YangY.NesicS. and BrownB. N.: ‘Roles of passivation and galvanic effects in localized CO2 corrosion of mild steel’. NACE International, Houston, TX, 2008, Paper 08332.
29.
PfennigA.WiegandR.WolfM. and BorkC. -P.: ‘Corrosion and corrosion fatigue of AISI 420C (X46Cr13) at 60 °C in CO2-saturated artificial geothermal brine’Corros. Sci., 201368134–143. doi: 10.1016/j.corsci.2012.11.005
30.
Al-HassanS.MishraB.OlsonD. L. and SalamaM. M.: ‘Effect of microstructure on corrosion of steels in aqueous solutions containing carbon dioxide’Corrosion199854480–491. doi: 10.5006/1.3284876
31.
SunJ. B.ZhangG. A.LiuW. and LuM. X.: ‘The formation mechanism of corrosion scale and electrochemical characteristic of low alloy steel in carbon dioxide-saturated solution’Corros. Sci., 201257131–138. doi: 10.1016/j.corsci.2011.12.025
32.
Mora-MendozaJ. L. and TurgooseS.: ‘Fe3C influence on the corrosion rate of mild steel in aqueous CO2 systems under turbulent flow conditions’Corros. Sci., 2002441223–1246. doi: 10.1016/S0010-938X(01)00141-X
33.
UedaM. and IkedaA.: ‘Effect of microstructure and Cr content in steel on CO2 corrosion’NACE International, Houston, TX, March 1996, Paper 13.
34.
LópezD. A.PérezT. and SimisonS. N.: ‘The influence of microstructure and chemical composition of carbon and low alloy steels in CO2 corrosion. A state-of-the-art appraisal’Mater. Des., 200324561–575. doi: 10.1016/S0261-3069(03)00158-4
35.
DugstadA.BørvikL.PalencsarS. and EikremP. A.: ‘Corrosion testing of steel armour wires in flexible pipes—a parametric study’NACE International, Houston, TX, March 2015, Paper 5829.
36.
GaoM.PangX. and GaoK.: ‘The growth mechanism of CO2 corrosion product films’Corros. Sci., 201153557–568. doi: 10.1016/j.corsci.2010.09.060
37.
ZhangY.PangX.QuS.LiX. and GaoK.: ‘Discussion of the CO2 corrosion mechanism between low partial pressure and supercritical condition’Corros. Sci., 201259186–197. doi: 10.1016/j.corsci.2012.03.006
38.
Félix-HenryA.: ‘Prevention and monitoring of fatigue-corrosion of flexible risers’ steel reinforcements’ ‘Proceedings of the 26th International Conference on Offshore Mechanics and Arctic Engineering, San Diego, CA, June 2007, Paper 29186’
WangR. A. Y. and AkidR.: ‘Role of nonmetallic inclusions in fatigue, pitting, and corrosion fatigue’Corrosion19965292–102. doi: 10.5006/1.3292108
42.
CongletonJ.CraigI. H.OliehR. A. and ParkinsR. N.: ‘Some electrochemical and microstructural aspects of corrosion fatigue’367–389; 1983Philadelphia, PAAmerican Society for Testing and Materials.
43.
RopitalF.Condat-TaravelC.SaasJ. N. and DuretC.: ‘Methodology to study the general corrosion of steel armours in simulated conditions of flexible pipe annulus influence of confinement and evaluation of the pH’The European Corrosion Congress, Moscow, Russia; September 2000.
44.
Taravel-CondatC. and DesamaisN.: ‘Qualification of high strength carbon steel wires for use in specific annulus environment of flexible pipes containing CO2 and H2S’. Proc. 25th International Conference on Offshore Mechanics and Arctic Engineering, Hamburg, Germany, June 2006, Paper 92394.
45.
RemitaE.RopitalF. and KittelJ.: ‘Experimental and theoretical investigation of the uniform corrosion in the annulus of offshore flexible pipelines’NACE International, Houston, TX, March 2008, Paper 08538.
46.
RemitaE.TribolletB.SutterE.RopitalF.LongaygueX.KittelJ.Taravel-CondatC. and DesamaisN.: ‘A kinetic model of CO2 corrosion in the confined environment of flexible pipe annulus’, ‘ The European Corrosion Congress, Freiburg, Germany’; September 2007.
47.
ClementsR.: ‘Corrosion assessment prediction for a confined flexible pipe annulus’The European Corrosion Congress, Edinburgh, Scotland; September 2008.