Investigation of corrosion behaviours of high level waste container materials in simulated groundwater in China

Abstract

Appropriate high level radioactive waste container materials in China are still under investigation. The corrosion behaviours of four types of materials (carbon steel Q235, aluminium alloy 2024, copper and stainless steel SUS 304) in simulated groundwater at room temperature were investigated. The corrosion rate was measured through the weight loss method. The chemical composition of corrosion product films formed on the surface of materials was investigated by means of X-ray diffraction and energy dispersive X-ray spectroscopy. The results showed that there was no crevice and pitting corrosion for carbon steel after one year of immersion; the corrosion was dominated by general corrosion, the composition of the corrosion product film being mainly γ-FeOOH, as well as Fe₃O₄. Copper underwent slight crevice corrosion, but aluminium alloy 2024 suffered serious localised corrosion. No corrosion was observed on stainless steel SUS 304. The presence of oxygen promoted crevice corrosion of copper and aluminium alloy 2024.

Keywords

High level radioactive waste Groundwater Crevice corrosion

Get full access to this article

View all access options for this article.

References

http://en.wikipedia.org/wiki/Nuclear_power_in_China

Férona

Crusset

and Gras

J.-M

: ‘Corrosion issues in nuclear waste disposal’ J. Nucl. Mater. 2008 379 16–23.

Wang

Liu

Shen

and He

: ‘Research progress of container materials for high level radioactive waste’ Corros. Protect. 2011 32 40–44.

Bennett

and Gens

: ‘Overview of European concepts for high-level waste and spent fuel disposal with special reference waste container corrosion’ J. Nucl. Mater. 2008 379 1–8.

Hornus

and Rodríguez

: ‘Effect of temperature on the crevice corrosion resistance of Ni-Cr-Mo alloys as engineered barriers of nuclear repositories’ Proc. Mater. Sci. 2012 1 251–258.

Liepina

and Kadek

: ‘Conditions for disruption of the primary film during corrosion of aluminum in neutral solutions’ Corros. Sci. 1966 6 177–181.

Cheng

and Man

: ‘An electrochemical study of the crevice corrosion resistance of NiTi in Hanks’ solution’, J. Alloys Compd 2007 437 322–328.

Christy

Lowe

Otieno-Alego

Stoll

and Webster

: ‘Voltammetric and Raman microspectroscopic studies on artificial copper pits grown in simulated potable water’ J. Appl. Electrochem. 2004 34 (2) 225–233.

Hung

Taxen

Williams

and Scully

: ‘Effects of selected water chemistry variables on copper pitting propagation in potable water’ Electrochim. Acta 2011 56 6165–6183.