The corrosion of X70 steel and iron in supercritical CO2/SO2/O2/H2O environment were investigated after a 454 h exposure. Optical microscopy was applied to observe the morphology of etch pits and synthesise the three-dimensional morphology. X-ray diffraction and X-ray photoelectron spectroscopy were employed to detect the composition of product scales. Experimental results verified that the localised corrosion occurred on the X70 steel sample under corrosion product deposits. Ferrous sulphate, sulphur and iron sulphide were detected as the corrosion products.
FarelasFChoiYSNešićS: ‘Corrosion behavior of API 5L X65 carbon steel under supercritical and liquid CO2 phases in the presence of H2O and SO2’Corrosion201369(3)243–250.
2.
RuhlASKranzmannA: ‘Investigation of corrosive effects of sulphur dioxide, oxygen and water vapour on pipeline steels’Int. J. Greenhouse Gas Control201313(0)9–16.
3.
XiangYWangZLiZNiW: ‘Effect of temperature on the corrosion behavior of X70 steel in high pressure CO2/SO2/O2/H2O environments’Corros. Eng. Sci. Technol.201348(2)121–129.
4.
TanYFwuYBhardwajK: ‘Electrochemical evaluation of under-deposit corrosion and its inhibition using the wire beam electrode method’Corros. Sci.201153(4)1254–1261.
5.
OosterkampARamsenJ: ‘State-of-the-art overview of CO2 pipeline transport with relevance to offshore pipelines’POL-O-2007-138-A, POLYTEC2008.
6.
MohitpourMGolshanHMurrayA: ‘Pipeline design & construction, a practical approach’; 2003New York, NYASME Press.
7.
XiangYWangZXuCZhouCLiZNiW: ‘Impact of SO2 concentration on the corrosion rate of X70 steel and iron in water-saturated supercritical CO2 mixed with SO2’J. Supercrit. Fluids201158(2)286–294.
8.
AllamIMArlowJSSaricimenH: ‘Initial stages of atmospheric corrosion of steel in the Arabian Gulf’Corros. Sci.199132(4)417–432.
9.
MoulderJFStickleWFSobolPEBombenKD: ‘Handbook of X-ray photoelectron spectroscopy: a reference book of standard spectra for identification and interpretation of XPS data’; 1992MinnesotaPerkin-Elmer.
10.
MandrinoD: ‘XPS and SEM of unpolished and polished FeS surface’Mater. Technol.201145(4)325–328.
11.
Abdel-SamadHWatsonPR: ‘An XPS study of the adsorption of lead on goethite (alpha-FeOOH)’Appl. Surf. Sci.1998136(1-2)46–54.
12.
Szklarska-SmialowskaZ: ‘Pitting corrosion of iron in sodium-sulfate’Corros. Sci.197818(1)97–101.
13.
TousekJ: ‘Studies on corrosion pitting of nickel and iron produced by sulfate ions’Corros. Sci.197212(1)15–28.
14.
MoayedMHNewmanRC: ‘Deterioration in critical pitting temperature of 904L stainless steel by addition of sulfate ions’Corros. Sci.2006483513–3530.
15.
ZhaoBLiYZhuoYTongHZhangXChenC: ‘Mass transfer and kinetics study on the sulfite forced oxidation with manganese ion catalyst’Korean J. Chem. Eng.200724(3)471–476.
16.
HemmingsenTVangdalHValandT: ‘Formation of ferrous sulfide film from sulfite on steel under anaerobic conditions’Corrosion199248(6)475–481.
17.
RuhlASKranzmannA: ‘Investigation of corrosive effects of sulphur dioxide, oxygen and water vapour on pipeline steels’Int. J. Greenhouse Gas Control2013139–16.
18.
ChoiYSNesicSYoungD: ‘Effect of impurities on the corrosion behavior of CO2 transmission pipeline steel in supercritical CO2–water environments’Environ. Sci. Technol.201044(23)9233–9238.