Corrosion behaviour of X52 pipeline steel in high H 2 S concentration solutions at temperatures ranging from 25°C to 140°C

Abstract

High temperature and high pressure immersion tests in an autoclave were employed to study the corrosion behaviour of X52 pipeline steel in aqueous solutions containing high concentrations of H₂S. The corrosion products generated were characterised using scanning electron microscope, energy dispersive spectroscopy and X-ray diffraction. It was seen that at a constant H₂S concentration of 22 g/l, the corrosion rate increased with increasing temperature up to 90°C, thereafter decreased at 120°C and slightly increased again at 140°C while the corrosion rate increased with H₂S concentration at a temperature of 90°C. When the temperature and H₂S concentration increased, the corrosion product converted from iron rich to sulphur rich products in the following sequence: mackinawite→troilite→pyrrhotite, where the microstructure and stability of the corrosion products had an important effect on the corrosion rate. The corrosion film was formed through the combination of the outward diffusion of Fe²⁺ ions and the inward diffusion of H₂S and HS⁻ species.